A kind of nano-nickel cobaltate and preparation method thereof

A technology of nano-cobalt and acid nickel, which is applied in the direction of active material electrodes, structural parts, electrical components, etc., to achieve good electrochemical performance and reduce costs

Active Publication Date: 2016-08-24
NANJING UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the preparation of two-dimensional coral-like nano-nickel cobalt oxides by template method has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nano-nickel cobaltate and preparation method thereof
  • A kind of nano-nickel cobaltate and preparation method thereof
  • A kind of nano-nickel cobaltate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The first step: ultrasonically disperse 60 mg of graphite oxide in deionized water for 120 minutes to obtain a graphene oxide solution;

[0028] In the second step, 0.291g of nickel nitrate and 0.582g of cobalt nitrate were dissolved in 30mL of water and stirred for 60 minutes;

[0029] In the third step, the systems obtained in the first two steps were mixed and stirred for 60 minutes;

[0030] In the fourth step, the reaction system of the third step is freeze-dried;

[0031] In the fifth step, the powder obtained after freeze-drying in the fourth step is heat-treated at 400° C. for 1 hour under a nitrogen atmosphere to prepare a two-dimensional coral-like nano-nickel cobaltate.

Embodiment 2

[0033] The first step: ultrasonically disperse 20 mg of graphite oxide in deionized water for 30 minutes to obtain a graphene oxide solution;

[0034] In the second step, 0.291g of nickel nitrate and 0.582g of cobalt nitrate were dissolved in 30mL of water and stirred for 20 minutes;

[0035] In the third step, the systems obtained in the first two steps were mixed and stirred for 30 minutes;

[0036] In the fourth step, the reaction system of the third step is freeze-dried;

[0037] In the fifth step, the powder obtained after freeze-drying in the fourth step is heat-treated at 200° C. for 5 hours under a nitrogen atmosphere to prepare a two-dimensional coral-shaped nano-nickel cobaltate.

Embodiment 3

[0039] The first step: ultrasonically disperse 30 mg of graphite oxide in deionized water for 60 minutes to obtain a graphene oxide solution;

[0040] In the second step, 0.291g of nickel nitrate and 0.582g of cobalt nitrate were dissolved in 30mL of water and stirred for 30 minutes;

[0041] In the third step, the systems obtained in the first two steps were mixed and stirred for 60 minutes;

[0042] In the fourth step, the reaction system of the third step is freeze-dried;

[0043] In the fifth step, the powder obtained after freeze-drying in the fourth step is heat-treated at 300° C. for 2 hours under a nitrogen atmosphere to obtain a two-dimensional coral-like nano-nickel cobaltate. The field emission scanning electron microscope shows figure 2 shown. The prepared two-dimensional coral-like nano-nickel cobalt oxide was used as the anode material of lithium-ion battery for electrochemical performance test, the results are as follows image 3 As shown, compared with the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses two-dimensional coral nanometer nickel cobalt oxide and a preparation method thereof. The preparation method comprises the following steps: putting oxidized grapheme in water, carrying out ultrasonic dispersion, adding cobalt nitrate and nickel nitrate into water, stirring, dissolving, mixing the cobalt nitrate and the nickel nitrate uniformly so as to obtain a mixed system, freezing the mixed system, drying to obtain dried powder, and carrying out heat treatment on the dried powder to obtain the two-dimensional coral nanometer nickel cobalt oxide. Oxidized grapheme is used as a template material and a heat treatment method is adopted for preparing the two-dimensional coral nanometer nickel cobalt oxide. The prepared two-dimensional coral nanometer nickel cobalt oxide used as a lithium ion battery negative material has the good application prospect and the good economic benefit.

Description

technical field [0001] The invention relates to a nano-nickel cobaltate and a preparation method thereof, in particular to a two-dimensional coral-like nano-nickel cobaltate and a preparation method thereof, belonging to the field of nanomaterial preparation. Background technique [0002] As a new generation of green high-energy rechargeable batteries, lithium-ion batteries are widely used in electrical equipment such as mobile phones, notebook computers, and small cameras due to their outstanding advantages such as high voltage, high energy density, good cycle performance, small self-discharge, and no memory effect. At the same time, it also shows good application prospects and potential economic benefits in the fields of electric vehicles, satellites, aerospace, and space military. At present, it has become one of the high-tech industries of great significance to the national economy and people's life in this century. The performance of lithium-ion batteries (such as capa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/525H01M4/64H01M4/1391
CPCH01M4/1391H01M4/525H01M4/64H01M2004/027Y02E60/10
Inventor 付永胜彭长青曾晚婷庄家伟王佳瑜汪信朱俊武
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap