Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of acrylic woodware and methacrylate, which is applied in the field of coatings, can solve the problems of heat resistance, poor water resistance, poor brightness and adhesion, easy peeling off and mildew of the paint surface, and achieve good adhesion and gloss. good brightness effect
Inactive Publication Date: 2015-01-14
QINGDAO JIASHANG CREATIVE CULTURE
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there are still some defects in the varnishes currently on the market: poor brightness and adhesion, poor heat resistance and water resistance, and easy peeling and moldy paint surfaces. When this type of traditional varnish is used for interior decoration, the paint surface is dry During the process, toxic air pollution sources such as formaldehyde will be released
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] An acrylic wood varnish, comprising: 25 parts of methacrylate, 55 parts of methacrylic copolymer resin, 35 parts of toughener soluble ester, 13 parts of cellulose acetate butyrate, 3 parts of butanol, 2 parts of xylene, 0.2 part of defoamer, 0.3 part of dispersant, 4 parts of anti-settling agent and 1 part of film-forming aid.
Embodiment 2
[0013] An acrylic wood varnish, comprising: 30 parts of methacrylate, 60 parts of methacrylic copolymer resin, 40 parts of toughening agent soluble ester, 15 parts of cellulose acetate butyrate, 4 parts of butanol, 2.5 parts of xylene, 0.3 parts of defoamer, 0.5 parts of dispersant, 5 parts of anti-settling agent and 5 parts of film-forming aid.
[0014] The acrylic wood varnish formulated according to the components of the above parts by weight is realized through the following steps:
[0015] First add methacrylate, butanol, and xylene to the mixer, and stir for 35 minutes to obtain a mixed liquid; then add methacrylic acid copolymer resin, toughener soluble ester, and cellulose acetate butyrate to the above mixed liquid In the middle, stir for another 35 minutes, and during the stirring process, slowly add the defoamer while stirring (this type of defoamer is selected from polysiloxane-polyether copolymer emulsions, polypropylene glycols, mineral oil-based one or more), di...
Embodiment 3
[0017] An acrylic wood varnish, comprising: 35 parts of methacrylate, 65 parts of methacrylic copolymer resin, 55 parts of toughener soluble ester, 16 parts of cellulose acetate butyrate, 5 parts of butanol, 3 parts of xylene, 0.6 parts of defoaming agent, 0.7 parts of dispersant, 8 parts of anti-settling agent and 6 parts of film-forming aid.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to an acrylic acid woodwork varnish. The varnish is prepared from the following raw materials in parts by weight: 25-35 parts of methacrylate, 55-65 parts of methacrylic acid copolymerized resin, 35-55 parts of flexibilizer dissolved ester, 13-16 parts of cellulose acetate butyrate, 3-5 parts of butanol, 2-3 parts of xylol, 0.2-0.6 part of defoaming agent, 0.3-0.7 part of dispersing agent, 4-8 parts of anti-settling agent, and 1-6 parts of film forming auxiliary. The acrylic acid woodwork varnish can be used for coating wood furniture, wood floors and the like, the varnish surface is good in brightness and adhesion force, and the varnish prepared by adopting methacrylic acid copolymerized resin as a raw material has the functional characteristics such as light resistance, thermal resistance, water resistance, wear resistance and mildew resistance, can meet the decoration effect of wood furniture in interior decoration, thus being a desirable varnish material in interior decoration.
Description
technical field [0001] The invention relates to a varnish, in particular to an acrylic wood varnish, and belongs to the technical field of coatings. Background technique [0002] With the improvement of people's living standards, the quality requirements for home decoration are also getting higher and higher. The requirements for the carpentry work in the decoration, such as the production of bookshelves and wardrobes and the paint surface of the purchased furniture, are also perfect. However, there are still some defects in the varnishes currently on the market: poor brightness and adhesion, poor heat resistance and water resistance, and easy peeling and moldy paint surfaces. When this type of traditional varnish is used for interior decoration, the paint surface is dry During the process, toxic air pollution sources such as formaldehyde will be released. Contents of the invention [0003] The invention provides an acrylic wood varnish aiming at the problems in the prio...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more