Method for repairing coloured glaze component of historic building

A restoration method and technology for ancient buildings, applied in the field of restoration of glazed components of ancient buildings

Inactive Publication Date: 2015-01-21
YANSHI CLASSICAL GARDENS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The glazed tiles used in the palace buildings in the early Ming Dynasty were used in many of the glazed tiles in the mausoleum screen walls, religious temples, pagodas, and utensils. Because the glazed components are precious, they need to be repaired regularly. Damage, it is necessary to manually remove the part to be repaired and then repair or replace it. When repairing, it is necessary to use a heating furnace or a windshield for repair work. The repair requirements are high, and this repair method will cause damage to other parts of the ancient building. At the same time, it is likely to cause damage to the new glaze or new components during installation, requiring secondary repairs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Repair method of glazed components of ancient buildings,

[0033] Step 1, first clean up the original components;

[0034] Step 2, bake with a blowtorch or infrared lamp, stop baking after baking to about 300 degrees, naturally cool down to room temperature, and then carry out a second cleaning, and then carry out a second baking to about 500 degrees, and then reduce to room temperature, carry out the first three cleanings;

[0035] Step 3, repair with one or more of silicone oil, glass water or cooked glazed tile raw materials, and restore the parts by hand molding;

[0036] Step 4, bake with an infrared lamp or a blowtorch, increase the temperature by 100 degrees per hour until 300 degrees, and then cool it down to room temperature with dry water;

[0037] Step 5: Brush the surface of the component with silicone oil with a viscosity of 3 / 1000. After drying, use an infrared lamp or a blowtorch to bake it. The temperature is increased at a rate of 150 degrees per hour...

Embodiment 2

[0043] Repair method of glazed components of ancient buildings,

[0044] Step 1, first clean up the original components;

[0045] Step 2, bake with a blowtorch or infrared lamp, stop baking after baking to about 300 degrees, naturally cool down to room temperature, and then carry out a second cleaning, and then carry out a second baking to about 500 degrees, and then reduce to room temperature, carry out the first three cleanings;

[0046] Step 3, repair with one or more of silicone oil, glass water or cooked glazed tile raw materials, and restore the parts by hand molding;

[0047] Step 4, bake with an infrared lamp or a blowtorch, increase the temperature by 100 degrees per hour until 300 degrees, and then cool it down to room temperature with drying water;

[0048] Step 5: Brush the surface of the component with silicone oil with a viscosity of 3 / 1000. After drying, use an infrared lamp or a blowtorch to bake it. The temperature is increased at a rate of 150 degrees per h...

Embodiment 3

[0054] Repair method of glazed components of ancient buildings,

[0055] Step 1, first clean up the original components;

[0056] Step 2, bake with a blowtorch or infrared lamp, stop baking after baking to about 300 degrees, naturally cool down to room temperature, and then carry out a second cleaning, and then carry out a second baking to about 500 degrees, and then reduce to room temperature, carry out the first three cleanings;

[0057] Step 3, repair with one or more of silicone oil, glass water or cooked glazed tile raw materials, and restore the parts by hand molding;

[0058] Step 4, bake with an infrared lamp or a blowtorch, increase the temperature by 100 degrees per hour until 300 degrees, and then cool it down to room temperature with dry water;

[0059] Step 5: Brush the surface of the component with silicone oil with a viscosity of 3 / 1000. After drying, use an infrared lamp or a blowtorch to bake it. The temperature is increased at a rate of 150 degrees per hour, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for repairing a coloured glaze component of a historic building. The method for repairing the coloured glaze component of the historic building has the advantages that a damaged coloured glaze component can be repaired without being taken down, a hidden trouble that the component is damaged again is eliminated in a repairing process, a repairing effect is good, less tools are used, repairing cost is low, and the component can be quickly repaired.

Description

technical field [0001] The invention relates to a repair method, in particular to a method for repairing glazed components of ancient buildings without dismantling the glazed surfaces of ancient buildings. Background technique [0002] Colored glaze is a kind of ancient Chinese material. It has a history of more than 2,000 years. It has been used exclusively by the royal family since ancient times. There are extremely strict grade requirements for users, so it is rare among the people. Liuli is a kind of low-temperature colored glaze used to decorate ceramics in ancient Shanxi. Liuli appeared in the Warring States Period. It was more popular in the Sui, Tang, and Liao Dynasties, and continued to be fired in the Ming and Qing Dynasties. The glaze of glass ware is made of lead as a flux, iron, copper, cobalt, manganese as a colorant, and quartz. Generally, the second firing is adopted, that is, the plain body is fired first, then the glass glaze is applied, and then the l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 张顺发张丹锋薛站峰
Owner YANSHI CLASSICAL GARDENS
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com