Antirust master batches for various metals as well as preparation method and application of antirust master batches

A multi-metal and masterbatch technology, which is applied in the field of multi-metal rust-proof masterbatch and its preparation, can solve the problems that have not been involved, and achieve the effect of enhancing the anti-rust performance

Active Publication Date: 2015-02-18
青岛鑫盈鑫包装材料有限公司 +1
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But for now, as an ideal green additive, borate is mainly used in the field of water-based cutting fluid (Li Wei, Ma Tao, Wang Sen, Tan Hailin. Application of borate in water-based cutting fluid .Tool Technology, 2010, 44(5): 93-95.), respectively play the role of extreme pressure lubricant, surfactant, antirust agent, anticorrosion and bactericide, and they are also used as additives in gas phase antirust technology There is no reference, especially there is no report on the gas-phase anti-rust masterbatch and its preparation method and application using non-toxic inorganic salts and organic amine borates as compound corrosion inhibitors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antirust master batches for various metals as well as preparation method and application of antirust master batches

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Anti-rust masterbatch a for multi-metal, wherein the mass percentage of each component is: 35% compound anti-rust agent, 45% carrier plastic and 20% auxiliary agent; the compound anti-rust agent consists of sebacic acid Disodium, sodium molybdate, and oleic acid diethanolamide borate are mixed in a mass ratio of 1:1.2:3, and the particle size of the compound antirust agent is 900-1100 mesh; the additive is composed of hard Acetamide, silicon dioxide, sucrose fatty acid ester, and antioxidant 1076 are mixed in a mass ratio of 1:5.5:3:1.

Embodiment 2

[0021] Anti-rust masterbatch b for multi-metal, wherein the mass percentage of each component is 40% compound anti-rust agent, 45% carrier plastic and 15% additive; the compound anti-rust agent consists of sebacic acid di Sodium, sodium molybdate, and oleic acid diethanolamide borate are mixed in a mass ratio of 1:1.2:3, and the particle size of the compound antirust agent is 900-1100 mesh; the additive is composed of stearate Acid amide, silicon dioxide, sucrose fatty acid ester, and antioxidant 1076 are mixed in a mass ratio of 1:5.5:3:1.

Embodiment 3

[0023] Anti-rust masterbatch c for multi-metal, wherein the mass percentage of each component is: 42% compound anti-rust agent, 46% carrier plastic and 12% auxiliary agent; the compound anti-rust agent consists of sebacic acid Disodium, sodium molybdate, and oleic acid diethanolamide borate are mixed in a mass ratio of 1:1.2:3, and the particle size of the compound antirust agent is 900-1100 mesh; the additive is composed of hard Acetamide, silicon dioxide, sucrose fatty acid ester, and antioxidant 1076 are mixed in a mass ratio of 1:5.5:3:1. .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses antirust master batches for various metals as well as a preparation method and application of the antirust master batches. The antirust master batches comprise the following components in percentage by mass: 30-50% of a compounded antirust agent, 40-60% of carrier plastic and 10-20% of an auxiliary agent, wherein the compounded antirust agent is prepared by mixing disodium sebacate, sodium molybdate and diglycolamide oleate borate according to a mass ratio of (1-1.3):(1.1-1.5):(2.2-3.2); and the auxiliary agent is prepared by mixing stearic acid amide, silicon dioxide, sucrose fatty acid ester and an antioxidant 1076 according to a mass ratio of (0.9-1.3):(4.8-6.5):(2.5-3.3):(0.8-1.1). The diglycolamide oleate borate is adopted as an additive and has a dispersion effect and an antirust effect, and the compounded antirust agent has certain polarity, can penetrate through the carrier plastic and volatilize to the surface of a packed metal to form a protective film so as to prevent corrosion of external corrosive substances, and cannot be incompatible with the carrier plastic to generate frost due to too strong polarity. The antirust master batches do not contain harmful ingredients, are environment-friendly and safe to use, and can achieve an antirust effect on various metals.

Description

Technical field: [0001] The invention relates to the field of non-toxic gas-phase anti-rust plastic products suitable for various metal products, and specifically refers to a multi-metal anti-rust masterbatch, its preparation method and specific application. Background technique: [0002] Metal corrosion is a common problem involving various fields of the national economy. It is an electrochemical process in which oxygen and water act on the metal surface to form a mixture of oxides and hydroxides. It has great harm to the performance and value of metals and their products. Serious Sometimes it will cause a major accident and cause the equipment to be scrapped. During the production, transportation and storage of metal and its products, especially in the process of sea transportation and high-heat and humid land transportation, it will inevitably encounter corrosion and rust. According to statistics, in 2005, the economic loss caused by corrosion in my country was more than...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08K13/02C08K5/098C08K3/24C08K5/56C08K3/36C08K5/20C08K5/134C08J3/22
CPCC08J3/226C08J5/18C08J2323/06C08J2323/08C08J2423/06C08J2423/08C08K3/24C08K3/36C08K5/092C08K5/1345C08K5/20C08K5/55C08K13/02C08K2201/003C08L23/06C08L23/0815C08L2203/16C08L2207/066
Inventor 李文强
Owner 青岛鑫盈鑫包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products