Macromolecular self-adhesive glue film coiled material adopting SEBS self-adhesive glue as self-adhesive layer and production method of macromolecular self-adhesive glue film coiled material

A technology of self-adhesive film and production method, which is applied in the field of building waterproof materials, can solve the problems of many processes required for the construction of ordinary coils, poor adhesion between the coil and the base layer, and increased construction costs, so as to improve the self-waterproof function. , Significant waterproof effect, cost saving effect

Inactive Publication Date: 2015-03-25
WEIFANG HONGYUAN WATERPROOF MATERIAL
View PDF7 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, during construction, the bonding strength between the asphalt-based waterproofing membrane and the concrete structure is affected by factors such as the quality of the base layer, the construction environment, and the skill of the construction technicians. It cannot be guaranteed that each construction will meet the requirements of the construction technical specifications. The construction site often has problems such as poor bonding between the coiled material and the base layer, drumming, water channeling, and leakage, and increases the construction cost; in addition, ordinary coiled material construction requires many procedures and takes a long time to construct

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecular self-adhesive glue film coiled material adopting SEBS self-adhesive glue as self-adhesive layer and production method of macromolecular self-adhesive glue film coiled material
  • Macromolecular self-adhesive glue film coiled material adopting SEBS self-adhesive glue as self-adhesive layer and production method of macromolecular self-adhesive glue film coiled material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 1. Preparation of SEBS self-adhesive

[0034] Stir 5kg of SEBS elastomer, 25kg of butyl (IIR) rubber, 35kg of terpene resin and 10kg of naphthenic oil for rubber at 190-200°C for 2 hours. After swelling and stirring evenly, add 0.3kg of Stir the mixture of antioxidant 1010 and 0.3kg of light stabilizer 770 evenly to obtain a uniform and stable viscous SEBS self-adhesive liquid, which is cooled to 165-170°C for use.

[0035] 2. Preparation of Polymer Layer

[0036] The polyolefin synthetic polymer waterproof membrane is processed by an extruder and a calender to produce a homogeneous polymer membrane.

[0037] 3. Preparation of SEBS self-adhesive layer

[0038] The SEBS self-adhesive adhesive is evenly coated on the surface of the polymer coil by an automatic adhesive coating machine, and the thickness of the self-adhesive adhesive layer is 0.25mm.

[0039] 4. Preparation of anti-sticking layer of quartz sand

[0040] Evenly coat the quartz sand on the surface of the...

Embodiment 2

[0044] 1. Preparation of SEBS self-adhesive

[0045] Stir 7kg of SEBS elastomer, 27kg of butyl (IIR) rubber, 35kg of terpene resin and 10kg of naphthenic oil for rubber at 190-200°C for 2 hours. After swelling and stirring evenly, add 0.4kg of Stir the mixture of antioxidant 1010 and 0.4kg of light stabilizer 770 evenly to obtain a uniform and stable viscous SEBS self-adhesive liquid, which is cooled to 165-170°C for use.

[0046] 2. Preparation of Polymer Layer

[0047] The polyolefin synthetic polymer waterproof membrane is processed by an extruder and a calender to produce a homogeneous polymer membrane.

[0048] 3. Preparation of SEBS self-adhesive layer

[0049] The SEBS self-adhesive adhesive is evenly coated on the surface of the polymer coil by an automatic adhesive coating machine, and the thickness of the self-adhesive adhesive layer is 0.27mm.

[0050] 4. Preparation of anti-sticking layer of quartz sand

[0051] Evenly coat the quartz sand on the surface of the...

Embodiment 3

[0055] 1. Preparation of SEBS self-adhesive

[0056] Stir 10kg of SEBS elastomer, 30kg of butyl (IIR) rubber, 35kg of terpene resin and 10kg of naphthenic oil for rubber at 190-200°C for 2 hours. After swelling and stirring evenly, add 0.3kg of The mixture of antioxidant 1010 and light stabilizer 770 with a weight ratio of 1:1.2 is stirred evenly to obtain a uniform and stable viscous SEBS self-adhesive liquid, which is cooled to 165-170°C for use.

[0057] 2. Preparation of Polymer Layer

[0058] The polyolefin synthetic polymer waterproof membrane is processed by an extruder and a calender to produce a homogeneous polymer membrane.

[0059] 3. Preparation of SEBS self-adhesive layer

[0060] The SEBS self-adhesive adhesive is evenly coated on the surface of the polymer coil by an automatic adhesive coating machine, and the thickness of the self-adhesive adhesive layer is 0.30mm.

[0061] 4. Preparation of anti-sticking layer of quartz sand

[0062]Evenly coat the quartz ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a macromolecular self-adhesive glue film coiled material adopting SEBS self-adhesive glue as a self-adhesive layer and a production method of the macromolecular self-adhesive glue film coiled material. The coiled material comprises a macromolecular layer, an SEBS self-adhesive glue layer, a quartz sand anti-sticking layer and a polyethylene film overlap edge isolation layer, wherein the tensile strength of the macromolecular self-adhesive glue film coiled material is more than 800N / 50mm, the right-angled tearing strength of the macromolecular self-adhesive glue film coiled material is more than 80N / mm, the shear strength between two coiled materials is more than 550N / 50mm, the macromolecular layer is made of a polyolefins synthesized macromolecular waterproof coiled material, and the SEBS self-adhesive glue layer is prepared by adopting the following raw materials in parts by weight: 5 to 10 parts of SEBS elastomer, 25 to 30 parts of rubber, 35 parts of tackifying resin, 10 parts of a softening agent, 0.3 to 0.5 part of an antioxidant 1010 and 0.3 to 0.5 part of a light stabilizer 770. The product of the macromolecular self-adhesive glue film coiled material has the advantages of simplicity in construction, low requirement for the construction environment, less construction time and low construction cost and also has the advantages of high shear strength, high tensile strength and good waterproof effect.

Description

technical field [0001] The invention relates to a polymer self-adhesive film coil material with SEBS self-adhesive as a self-adhesive layer and a production method thereof, belonging to the field of building waterproof materials. Background technique [0002] At present, for large-scale building waterproof construction, waterproof membrane has become the material of choice. Traditional asphalt-based waterproofing membranes or modified asphalt waterproofing membranes are usually constructed using the hot-melt method, but this construction method is easily affected by environmental factors and cannot be constructed in wet or rainy weather; at the same time, the hot-melt method uses open flame construction, which has Security risks. Nowadays, many big cities have banned the use of open flames in construction, which puts forward higher requirements for manufacturers of waterproof membranes. In addition, during construction, the bonding strength between the asphalt-based waterp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B9/04B32B7/12B32B27/32B32B33/00C08L53/02C08L23/22C08L45/00C08K5/01C08K5/134C09J153/02C09J123/22C09J145/00
CPCB32B9/04B32B7/12B32B27/32B32B33/00B32B2307/73C08K5/01C08K5/134C08L23/22C08L45/00C08L53/02C09J123/22C09J145/00C09J153/02
Inventor 孙剑郑家玉刘兴邦
Owner WEIFANG HONGYUAN WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com