Epoxy group end-capped polysulfide polymer, preparation method and application thereof and room temperature fast-curing epoxy resin adhesive containing epoxy group end-capped polysulfide polymer

An epoxy resin and epoxy-based technology, applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems of reducing the cohesive strength of the resin, unfavorable industrialization, and slow curing reaction, so as to improve the impact resistance and fracture toughness, avoid irritating odor, and improve oil stain resistance

Active Publication Date: 2015-03-25
ZHENGZHOU ZHONGYUAN SILANDE HIGH TECH CO LTD
View PDF6 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, nitrile rubber is generally viscous and expensive, and is not suitable for low-viscosity epoxy resin adhesives and is not suitable for uniform mixing; for carboxyl-terminated nitrile rubber-modified epoxy resins, although it can method to improve toughness, but the process of rubber-resin prepolymerization is too complicated, which is not conducive to industrialization
The curing reaction of polysulfide rubber toughened epoxy resin is slow, and it will reduce the cohesive strength of the resin, which cannot meet the performance requirements of tensile shear strength and impact strength at the same time, and polysulfide rubber is terminated with mercapto groups, which is irritating The smell is strong, and the production and construction use of the product have a great impact on personnel and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy group end-capped polysulfide polymer, preparation method and application thereof and room temperature fast-curing epoxy resin adhesive containing epoxy group end-capped polysulfide polymer
  • Epoxy group end-capped polysulfide polymer, preparation method and application thereof and room temperature fast-curing epoxy resin adhesive containing epoxy group end-capped polysulfide polymer
  • Epoxy group end-capped polysulfide polymer, preparation method and application thereof and room temperature fast-curing epoxy resin adhesive containing epoxy group end-capped polysulfide polymer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0064] The preparation process of epoxy adhesive is:

[0065] Component A: First, add epoxy resin and epoxy-terminated polysulfide polymer into a double planetary stirring tank, vacuumize and stir, add filler after the temperature rises to about 50°C, and stir at a high speed of 800-1000rpm for 10 ~20min to make component A.

[0066] Component B: First, add the curing agent, accelerator and filler into the dual planetary stirring tank in sequence, the vacuum degree is 0.1Mpa, the rotation speed is 500-1000rpm, the stirring time is 30-60min, and the temperature does not exceed 70°C throughout the process. Finally, add the coupling agent, vacuumize and stir for 5-10 minutes to make component B.

Embodiment 1

[0068] In a nitrogen atmosphere, add 1200g of dithiol-terminated liquid polysulfide rubber (polysulfide rubber LP-3 from Japan Toray Polysulfide Co., Ltd. The molecular weight is 1000, the number of moles is 1.2mol, and the content of mercapto groups is 6.6%), heating and stirring until the temperature is 50°C, adding a total amount of 106.7g (the number of moles is 0.75mol) 1,4-butanediol divinyl within 1 hour ether, and 0.05 g of catalyst 2,2'-azobisisobutyronitrile was added, and the reaction was maintained for 3 h under airtight conditions. Track and measure the vinyl content. When the vinyl content drops to 0, add 110g (1.12mol) of 1,2-epoxy-5-hexene within 1 hour at 70°C and keep the reaction for 3h , measure the content of thiol group, when the content of thiol group is 0, remove the unreacted 1,2-epoxy-5-hexene in the reaction mixture for 2 hours under the vacuum condition of 70 ℃ and 1kPa, and cool After reaching room temperature, a light yellow transparent epoxy-ter...

Embodiment 2

[0070] In a nitrogen atmosphere, add 1375g (0.55mol in moles, 3.9% in mercapto group) trimercapto-terminated liquid polysulfide rubber (Japan Toray Polysulfide Co., Ltd. polysulfide rubber LP-980, molecular weight 2500), heating and stirring until the temperature is 50 ° C, adding a total amount of 75.84g (molar number is 0.48mol) diethylene glycol divinyl ether within 50 minutes, And add 0.05 g of catalyst 2,2'-azobisisobutyronitrile, and maintain the reaction for 3 hours under airtight conditions. Follow up and measure the vinyl content. When the vinyl content drops to 0, add 86.64g (0.76mol moles) of allyl glycidyl ether within 50 minutes at 70°C, keep the reaction for 3h, and measure the thiol group content, when the thiol group content is 0, remove the unreacted allyl glycidyl ether in the reaction mixture for 2 hours at 70°C and 1kPa vacuum conditions, and cool to room temperature to obtain a light yellow transparent liquid ring Oxygen-terminated polysulfide polymers of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
epoxy valueaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides an epoxy group end-capped polysulfide polymer as shown in a general formula (I), a preparation method thereof and application of the epoxy group end-capped polysulfide polymer as an epoxy resin adhesive toughening agent. The invention also provides an epoxy resin adhesive which contains the epoxy group end-capped polysulfide polymer. The epoxy group end-capped polysulfide polymer provided by the invention contains an epoxy group end group and a polysulfide bond, is capable of increasing the curing speed of an adhesive and enhancing the properties, namely impact resistance, fracture toughness, oil resistance and the like, of a cured material obtained after curing when used for the epoxy resin adhesive, and prevents the pungent smell brought by sulfhydryl. The epoxy resin adhesive provided by the invention has the advantages of no special smell in preparation and usage processes after the adhesive is cured, good product properties, no pollution on the environment and suitability for large-scale industrialized production.

Description

technical field [0001] The present invention relates to the field of epoxy resin adhesives, in particular to an epoxy-terminated polysulfide polymer, its preparation method and application, and a room temperature fast-curing epoxy resin adhesive comprising the epoxy-terminated polysulfide polymer . Background technique [0002] Room temperature fast-curing epoxy resin adhesive can effectively reduce the use cost of the adhesive because of its fast curing speed, high bonding strength, stable storage, good durability, and wide range of bonding materials. It is especially suitable for aviation, aerospace, automotive, etc. Rapid positioning and bonding of materials such as ships, large equipment, building structures, electronics and sports equipment. However, after curing, the epoxy resin has high crosslinking density, high brittleness, and poor impact toughness. Therefore, the development of toughened and modified room temperature fast-curing epoxy resin adhesives is a hot spo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G75/14C09J163/00C09J181/04
Inventor 张燕红曹兴园胡生祥吴欢秦瑞瑞宫祥怡曲雪艳
Owner ZHENGZHOU ZHONGYUAN SILANDE HIGH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap