Immersing material transferring roller

A roller and transfer technology, applied in the field of impregnated material transfer rollers, can solve problems such as difficult to achieve performance, and achieve the effects of easy control of reaction, good safety and simple operation

Active Publication Date: 2015-03-25
DONGGUAN INOAC METAL & ELASTOMER
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the increasing requirements of users for transfer rollers, the demand for high-speed printing is increasing. To achieve high-speed printing performance, a transfer roller with softer and lower resistance is required. However, the commonly used rubber materials and foam materials are currently It is difficult for the transfer roller to achieve this performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] An impregnated material transfer roller, the impregnated material transfer roller is prepared by soaking the transfer roller in an impregnating liquid, and the impregnating liquid includes the following raw materials in parts by weight:

[0055] Acrylate polymer emulsion 15 parts

[0056] Coloring agent 12 parts

[0057] Soaking agent 1 part

[0058] 0.1 part of defoamer

[0059] 40 parts of water.

[0060] Described acrylate polymer emulsion comprises the raw material of following percentage by weight:

[0061] Soft monomer 20 parts

[0062] Hard monomer 10 parts

[0063]Carboxyl-containing monomer 0.5 parts

[0064] 1 part of cross-linking monomer

[0065] 1 part emulsifier

[0066] Initiator 0.8 part

[0067] Deionized water balance.

[0068] The soft monomer is a mixture of ethyl acrylate and 2-ethylhexyl acrylate in a weight ratio of 1:1.4; the hard monomer is made of methyl methacrylate and styrene in a weight ratio of 1.5:1 The mixture of composition; ...

Embodiment 2

[0077] An impregnated material transfer roller, the impregnated material transfer roller is prepared by soaking the transfer roller in an impregnating liquid, and the impregnating liquid includes the following raw materials in parts by weight:

[0078] Acrylate polymer emulsion 17 parts

[0079] Coloring agent 14 parts

[0080] Soaking agent 1.2 parts

[0081] 0.15 parts of defoamer

[0082] 45 parts of water.

[0083] Described acrylate polymer emulsion comprises the raw material of following percentage by weight:

[0084] Soft monomer 22 parts

[0085] Hard monomer 12 parts

[0086] Carboxyl-containing monomer 0.7 parts

[0087] 1.5 parts of cross-linking monomer

[0088] Emulsifier 1.2 parts

[0089] Initiator 1.0 part

[0090] Deionized water balance.

[0091] The soft monomer is a mixture of ethyl acrylate and 2-ethylhexyl acrylate in a weight ratio of 1:1.6; the hard monomer is made of methyl methacrylate and styrene in a weight ratio of 1.7:1 The mixture of c...

Embodiment 3

[0100] An impregnated material transfer roller, the impregnated material transfer roller is prepared by soaking the transfer roller in an impregnating liquid, and the impregnating liquid includes the following raw materials in parts by weight:

[0101] Acrylate polymer emulsion 20 parts

[0102] Coloring agent 17 parts

[0103] Soaking agent 1.5 parts

[0104] 0.2 parts of defoamer

[0105] 50 parts of water.

[0106] Described acrylate polymer emulsion comprises the raw material of following percentage by weight:

[0107] Soft monomer 25 parts

[0108] Hard monomer 15 parts

[0109] Carboxyl-containing monomer 1.0 parts

[0110] 2 parts of cross-linking monomer

[0111] Emulsifier 1.5 parts

[0112] Initiator 1.2 parts

[0113] Deionized water balance.

[0114] The soft monomer is a mixture of ethyl acrylate and 2-ethylhexyl acrylate in a weight ratio of 1:1.8; the hard monomer is made of methyl methacrylate and styrene in a weight ratio of 2:1 The mixture of compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of electric imaging equipment, and particularly relates to an immersing material transferring roller. The immersing material transferring roller is prepared by soaking a transferring roller in an immersing solution, wherein the immersing solution comprises the following raw materials in parts by weight: 15-25 parts of an acrylate polymerized emulsion, 12-22 parts of a colorant, 1-2 parts of an impregnating agent, 0.1-0.3 part of a defoaming agent and 40-60 parts of water. The immersing solution adopts the raw materials with the weight ratio strictly controlled; when the transferring roller is soaked in the immersing solution, the prepared immersing material transferring roller is soft in sense of touch and excellent in conductivity; the immersing material transferring roller is prepared by soaking the transferring roller in the immersing solution, and is soft in sense of touch, excellent in conductivity, durable in washing and good in dry cleaning effect, the C hardness is 32.5+ / -17.5 degrees, and the resistance is less than 1*10<4> omegas.

Description

technical field [0001] The invention relates to the technical field of electro-imaging equipment, in particular to an impregnated material transfer roller. Background technique [0002] The transfer roller is the main component used in equipment such as printers or copiers. Its main function is to use its own material to have a certain degree of electrical conductivity. After external charging is applied to make itself have a certain amount of charge, it uses the principle of positive and negative charges. Adsorbs the toner attached to the surface of the photoreceptor to the surface of the paper. [0003] With the increasing requirements of users for transfer rollers, the demand for high-speed printing is increasing. To achieve high-speed printing performance, a transfer roller with softer and lower resistance is required. However, the commonly used rubber materials and foam materials are currently It is difficult for the transfer roller to achieve this performance. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G03G15/16
CPCG03G15/162
Inventor 曾志能
Owner DONGGUAN INOAC METAL & ELASTOMER
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com