Anti-skid cement mortar and preparation method thereof

A technology of cement mortar and cement, which is applied in the field of cement mortar, can solve the problems of poor friction performance, high energy consumption, and long construction period, and achieve the effects of excellent performance, reducing road surface water, and improving driving safety

Inactive Publication Date: 2015-04-29
李林声
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] In order to solve the existing technical problems, the present invention provides an anti-skid cement mortar and its preparation method, which solves the defects of the current cement mortar materials such as poor friction performance, easy slipping, poor ductility, easy fracture and easy corrosion; solves the defects of the current cement mortar materials The preparation method has the problems of high energy consumption, heavy environmental pollution, and long construction period

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-skid cement mortar and preparation method thereof
  • Anti-skid cement mortar and preparation method thereof
  • Anti-skid cement mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of antiskid cement mortar and preparation method thereof,

[0052] Its components include: high molecular polymer, cement, water, engineering fine sand;

[0053] Its weight percent of each component is:

[0054] High molecular polymer 10%;

[0055] Cement 20%;

[0056] water 40%;

[0057] Engineering fine sand 30%;

[0058] The sum of the percentages of the above components is 100%;

[0059] The above water is clean natural water;

[0060] The above-mentioned cement is not less than 42.5R cement, which is composed of clinker mineral components, magnesium oxide, sulfur trioxide, free calcium oxide, alkali, etc.; the setting time of cement is ≥1 hour for initial setting and ≤10 hours for final setting ; Dry shrinkage rate of cement ≤ 0.10%; Abrasion resistance of cement is 3.60 kg / ㎡;

[0061] The above engineering fine sand is 20-40 mesh;

[0062] The above-mentioned high molecular polymer is prepared from high molecular polymer monomer, initiator, emulsifi...

Embodiment 2

[0073] A kind of antiskid cement mortar and preparation method thereof,

[0074] Its components include: high molecular polymer, cement, water, engineering fine sand;

[0075] Its weight percent of each component is:

[0076] High molecular polymer 20%;

[0077] Cement 10%;

[0078] water 30%;

[0079] Engineering fine sand 40%;

[0080] The sum of the percentages of the above components is 100%;

[0081] The above water is clean natural water;

[0082] The above-mentioned cement is not less than 42.5R cement, which is composed of clinker mineral components, magnesium oxide, sulfur trioxide, free calcium oxide, alkali, etc.; the setting time of cement is ≥1 hour for initial setting and ≤10 hours for final setting ; Dry shrinkage rate of cement ≤ 0.10%; Abrasion resistance of cement is 3.60 kg / m2;

[0083] The above-mentioned engineering fine sand is 40-90 mesh;

[0084] The above-mentioned high molecular polymer is prepared from high molecular polymer monomer, initiato...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Wear resistanceaaaaaaaaaa
Login to view more

Abstract

The invention relates to anti-skid cement mortar and a preparation method thereof. The anti-skid cement mortar comprises the following components in percentage by weight: 10-40 percent of high-molecular polymer, 10-40 percent of cement, 20-50 percent of water and 30-60 percent of engineering fine sand. The sum of the percentages of the components is 100%. The preparation method of the anti-skid cement mortar comprises the following steps: (1) pouring water, cement, high-molecular polymer and engineering fine sand into a clean agitation vat in proportion in sequence; (2) uniformly agitating the cement mortar raw materials for 30min in a normal-temperature environment with an agitator fixed above the agitation vat; and (3) pouring fully and uniformly agitated cement mortar into a charging bucket for use. The anti-skid cement mortar and the preparation method thereof overcome the defects of poor friction performance, high possibilities of skidding, cracking and corrosion and poor ductility of conventional cement mortar material, and solve the problems of high energy consumption, severe environmental pollution and long construction period during preparation of the conventional cement mortar material.

Description

technical field [0001] The invention belongs to the field of cement mortar, and in particular relates to an anti-skid cement mortar and a preparation method thereof. The invention provides an anti-skid cement mortar maintenance material for concrete cement pavement, and a preparation method of the anti-skid cement mortar. Background technique [0002] During the service period, the concrete pavement not only bears tens of thousands of wheel loads, but also withstands the influence of periodic changes in temperature and humidity in the environment, which eventually leads to various damages. Concrete pavement diseases are mainly manifested as cracks, subsidence, severely broken slabs, cracked slab corners, mud pumping, misalignment, damage to joint materials, etc. If these diseases are not maintained and repaired in time, the performance of the pavement will decline rapidly. [0003] The deep-rooted reason for the above-mentioned lesions on the concrete pavement is that althou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B28/04
Inventor 李林声
Owner 李林声
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka