Desulfurization recovery method of slag iron of blowing-process desulfurizing slag

A recovery method and desulfurization slag technology are applied in the direction of recycling technology, process efficiency improvement, etc., which can solve the increase of sulfur content in molten steel, effectively solve the process method of spraying desulfurization slag iron, and the desulfurization slag iron is not effective. Recycling and other issues, to achieve remarkable results

Active Publication Date: 2015-04-29
北京璞域环保科技有限公司
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high viscosity of sprayed desulfurization slag, the separation of metallic iron and desulfurization slag is difficult, and the slag iron inevitably contains desulfurization slag, which is directly used for steelmaking. In the oxidizing atmosphere of steelmaking, MgS in the slag will produce MgS The reaction of +O→MgO+S increases the sulfur content of molten steel, which limits the recycling space of desulfurized slag and iron in steelmaking plants
[0004] Literature Search (1) Niu Xiyun, Liu Shuhai Practice of Injection Granular Magnesium Desulfurization Technology Continuous Casting 2007 (5) Zhang Wanqing Research and Application of Hot Metal Composite Injection Desulfurization Technology 2009 (6) (3) Zhuo Jun Li Pingfan Ge Wensun Pan Steel-magnesium composite injection desulfurization and slag adjustment process practice Sichuan Metallurgy - 2009 (3) It can be seen that there is no systematic and effective solution to the process of injection desulfurization slag iron, resulting in many domestic steel mills desulfurization slag iron has not been Effective recycling becomes a tasteless idle resource

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0017] Take a desulfurization station with double-station injection of passivated magnesium and passivated lime, and a steel plant equipped with 3×120 tons of converters as an example. The amount of slag in the converter is 95kg / ton of steel, and the amount of slag in each furnace is 11-12 tons. .

[0018] 1. Turn over the desulfurization slag by the injection method in the slag field, magnetically separate the desulfurization slag iron, and crush it to a size below 0.5m×0.5m×0.2m;

[0019] 2. Add the crushed desulfurization slag iron into the 11m 3 slag tank, add 100-300kg desulfurization slag iron to each tank;

[0020] 3. Add the desulfurization slag iron into the converter slag tank to the converter slag pit to receive the converter slag;

[0021] 4. The converter discharges the slag according to the conventional process. When the reaction in the slag tank is intense, the slag dumping speed can be appropriately slowed down, and the slag dumping is normal when the reactio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a desulfurization recovery method of slag iron of blowing-process desulfurizing slag, which comprises the following steps: 1) transporting slag iron obtained from blowing-process desulfurizing slag by magnetic separation to a converter slag field; 2) adding the slag iron to the middle of a slag ladle of the converter for use, wherein 20kg of slag iron is added to every ton of liquid converter steel slag, the size is less than 0.5*0.5m (length*width), the thickness is less than 0.2m, the slag iron is kept dry, and the maximal amount is not greater than 500kg for each ladle; 3) suspending the converter slag ladle with the blowing-process desulfurizing slag slag iron to a converter slag vehicle, and receiving the converter turndown slag by a converter slag pit; 4) pouring the turndown slag into the slag ladle by the converter according to the conventional slag discharge technique; 5) transporting the slag ladle filled with the converter turndown slag to the converter slag field, and standing for 20-40 minutes; 6) treating according to a hot application or hot braising conventional treatment technique for converter carbon steel slag; and 7) after the hot application or hot braising technique is finished, carrying out magnetic separation to recover the slag iron in the steel slag, which is directly used for steel making.

Description

technical field [0001] The invention relates to a desulfurization recovery method of jet desulfurization slag iron. Background technique [0002] Hot metal desulfurization process is the operation process with the highest efficiency and the lowest desulfurization cost in the metallurgical process, which has brought huge benefits to the iron and steel industry. The core of the problem is the recovery of metallic iron in the desulfurization slag. [0003] At present, hot metal injection desulfurization is the preferred desulfurization process for smelting ultra-low sulfur steel. This process is mainly desulfurization by spraying passivated magnesium powder and passivated lime powder. This desulfurization mode causes high magnesium oxide content in the slag, high viscosity of the slag, and a large amount of iron in the slag removal process, resulting in injection desulfurization. The slag contains high iron content, and the CO, H released during the disposal process 2 S, SO ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C1/02C21B3/06
CPCY02P10/20Y02W30/50
Inventor 俞海明
Owner 北京璞域环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products