Outdoor waterproof weather-proof wave-absorbing material and preparation method thereof

A wave-absorbing material and weather-resistant technology, applied in the field of materials, can solve the problems of difficult realization of waterproof cloth, influence of waterproof effect, and difficulty in sealing

Active Publication Date: 2015-05-13
DALIAN DONGSHIN MICROWAVE TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polyurethane sponge absorbing material has an open-pore structure, and its performance is realized by impregnating absorbing agents and flame retardants. Therefore, this type of absorbing material can only be used indoors, but it cannot be used for absorbing materials used in outdoor laboratories. fulfil requirements
[0003] At present, the wave-absorbing materials used in the field laboratory are generally covered with a layer of waterproof cloth on the surface of the open-cell polyurethane sponge wave-absorbing material. The wave-absorbing material is generally made into a pyramid shape. The material has dozens of cone points, so it is sometimes difficult to directly cover the waterproof cloth. In addition, it is difficult to completely seal the waterproof cloth at the seam, which also affects the waterproof effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Outdoor waterproof weather-proof wave-absorbing material and preparation method thereof
  • Outdoor waterproof weather-proof wave-absorbing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Embodiment 1, the components by weight of the flame retardant rainproof coating and the content of each component include:

[0058] Film-forming material: fluorocarbon emulsion, 30 parts; pure acrylic emulsion, 30 parts;

[0059] Pigment and filler: titanium dioxide, 5 parts;

[0060] Flame retardant: aluminum hydroxide, 10 parts; ammonium polyphosphate, 6 parts;

[0061] Dispersant: 0.4 parts;

[0062] Defoamer: 0.4 parts;

[0063] Deionized water: 18.2 parts.

Embodiment 2

[0064] Embodiment two, the composition components of flame retardant rainproof coating and the weight parts of each component content include:

[0065] Film-forming material: fluorocarbon emulsion, 30 parts; pure acrylic emulsion, 32 parts;

[0066] Pigment and filler: titanium dioxide, 6 parts;

[0067] Flame retardant: aluminum hydroxide, 9 parts; ammonium polyphosphate, 7 parts;

[0068] Dispersant: 0.5 parts;

[0069]Defoamer: 0.5 parts;

[0070] Deionized water: 15 parts.

Embodiment 3

[0071] Embodiment three, the components by weight of the flame retardant rainproof coating and the content of each component include:

[0072] Film-forming material: fluorocarbon emulsion, 28 parts; pure acrylic emulsion, 26 parts;

[0073] Pigment and filler: titanium dioxide, 4 parts;

[0074] Flame retardant: aluminum hydroxide, 9 parts; ammonium polyphosphate, 6 parts;

[0075] Dispersant: 0.4 parts;

[0076] Defoamer: 0.4 parts;

[0077] Deionized water: 26.2 parts.

[0078] At the same time, a preparation method for outdoor waterproof and weather-resistant wave-absorbing materials is also provided, including:

[0079] Add the dispersant, defoamer, pigment and filler, and flame retardant in specified proportions by weight to deionized water, and grind the mixture for 4 hours;

[0080] Add the film-forming substance to the above-mentioned ground mixture, stir in the disperser for 0.5 hours, and filter the material to obtain a flame-retardant and rainproof coating; the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an outdoor waterproof weather-proof wave-absorbing material and a preparation method thereof. The outdoor waterproof weather-proof wave-absorbing material is prepared by using a porous polyurethane sponge wave-absorbing material as a matrix, and coating a layer of completely closed flame-retardant rainproof coating on the outer surface of the matrix, wherein the flame-retardant rainproof coating is prepared from the following components in parts by weight: film forming matter: 28-30 parts of fluorocarbon emulsion and 26-32 parts of pure acrylic emulsion, pigment packing: 4-6 parts of titanium dioxide, fire retardants: 8-10 parts of aluminum hydroxide, and 5-8 parts of ammonium polyphosphate, 0.4-0.5 parts of a dispersing agent, 0.4-0.5 parts of a defoaming agent, and 15-27 parts of deionized water. The outdoor waterproof weather-proof wave-absorbing material has the characteristics of flame retardance, rainwater prevention and weather resistance.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to an outdoor waterproof and weather-resistant wave-absorbing material and a preparation method thereof. Background technique [0002] At present, the widely used absorbing material is polyurethane sponge absorbing material, which is mainly used in the construction of radio anechoic chambers (non-echo chambers, microwave anechoic chambers), radio anechoic chambers, absorbing screens and absorbing walls, etc., to cover reflectors in the test environment. , Reduce background noise, eliminate clutter interference, and improve test accuracy. The polyurethane sponge absorbing material has an open-pore structure, and its performance is realized by impregnating absorbing agents and flame retardants. Therefore, this type of absorbing material can only be used indoors, but it cannot be used for absorbing materials used in outdoor laboratories. fulfil requirements. [0003] At present, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D133/04C09D5/18C09D7/12C08J9/36C09K3/00
CPCC08J9/365C08J2205/05C08J2375/04C08J2427/12C08J2433/04C08L2201/02C09D5/18C09D7/61C09D127/12C09D133/04C08L33/04C08K2003/2241C08K2003/2227C08K2003/323C08L27/12
Inventor 董艳春周冬柏许洁宋宪超
Owner DALIAN DONGSHIN MICROWAVE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com