Aluminum wiredrawing fluid with nanometer titanium dioxide, and preparation method for aluminum wiredrawing fluid

A technology of nano-titanium dioxide and aluminum wire drawing fluid, which is applied in the direction of additives, petroleum industry, lubricating composition, etc., can solve the problem of high cost, and achieve the effect of bright surface, good dispersibility, and good lubricating effect

Inactive Publication Date: 2015-05-13
ANHUI WANGDA COPPER DEV
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the aluminum wire drawing liquid commonly used in the market is an emulsion, and most of the products are imported from abroad, and the cost is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The present invention will be described in detail below through specific examples.

[0013] An aluminum wire drawing liquid added with nano-titanium dioxide, which is made of the following parts by weight (kg) of raw materials: nano-titanium dioxide 8, triethanolamine borate 2, aluminum alloy corrosion inhibitor 2, vulcanized whale oil 5, morpholine 2.5, three Ethanolamine oleic acid soap 3, 2,6-di-tert-butyl-p-cresol 0.8, castor oil 5.5, cocamidopropyl amine oxide 4, additives 5, deionized water 900;

[0014] The additives are made of the following parts by weight (kg) of raw materials: graphite particles 2, nano diatomaceous earth 2.5, bisphenol A dimethacrylate 1, vulcanized cottonseed oil 2, dodecyl alcohol ester 2, aniline Base triethoxysilane 1, Bupleurum oil 1, open powder 3, water 90; the preparation method is to first add graphite particles, nano diatomaceous earth, Bupleurum oil, and open powder into half of the water, grind 1- 2 hours, then slowly add the remaini...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum wiredrawing fluid with nanometer titanium dioxide. The aluminum wiredrawing fluid is characterized by being prepared from the following raw materials in parts by weight: 8-11 parts of nanometer titanium dioxide, 2-4 parts of triethanolamine borate, 2-3 parts of an aluminum alloy inhibiter, 5-6 parts of a vulcanized haco oil, 2.5-3.5 parts of morpholine, 3-4 parts of triethanolamine oleic soap, 0.8-1.5 parts of 2,6-butylated hydroxytoluene, 5.5-7 parts of a castor oil, 4-5 parts of cocamidopropyl dimethylamine oxide, 5-7 parts of an addition agent, and 900-950 parts of deionized water. According to the invention, the nanometer titanium dioxide and a surfactant are mixed through grinding, and the aluminum wiredrawing fluid has favorable dispersibility and wear resistance, does not damage wiredrawing molds, and has a good cleaning ability; the addition agent is added, so that the wear resistance, the dispersibility, the lubrication and the filming performance are enhanced. The aluminum wiredrawing fluid disclosed by the invention has good flowability, good lubrication effects and corrosion inhibition effects; drawn aluminum wires are uniform in shape, light in surface, and unlikely to corrode; the aluminum wiredrawing fluid is suitable for wiredrawing machines.

Description

Technical field [0001] The invention relates to the technical field of wire drawing, in particular to an aluminum wire drawing liquid added with nanometer titanium dioxide and a preparation method thereof. Background technique [0002] Determined by the processing characteristics of aluminum metal itself, aluminum wire drawing has high requirements for wire drawing fluid. First of all, the lubricity of the drawing fluid is required to be very high. Only when the lubricity meets the processing requirements, the drawn aluminum wire can be smooth and scratch-free, and then the aluminum wire can be processed in a later order; second, after the aluminum wire is uniformly stretched, After washing with high-speed water flow, the wire drawing liquid on the surface of the aluminum wire is rinsed to prepare for the next process. Therefore, the wire drawing liquid is required to have excellent cleaning properties; of course, for aluminum metal, the corrosion problem is equally important. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10M125/10C10M141/08C10N30/04C10N30/06C10N40/24
Inventor 周小刚储刘生
Owner ANHUI WANGDA COPPER DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap