Process of making a continuous dielectric film comprising dispersed nanoparticles

A nanoparticle and dielectric film technology, applied in the field of dielectrics, can solve the problems of no way to ensure the mixing of particles, and achieve the effects of reduced error introduction, large control, and short processing time

Active Publication Date: 2015-05-13
THE SEC OF STATE FOR DEFENCE IN HER BRITANNIC MAJESTYS GOVERNMENT OF THE UK OF GREAT BRITAIN & NORTHERN IRELAND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, such in-situ mixing is not possible in order to produce a continuous feed, and there is no way to ensure that the particles become properly mixed during the process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process of making a continuous dielectric film comprising dispersed nanoparticles
  • Process of making a continuous dielectric film comprising dispersed nanoparticles
  • Process of making a continuous dielectric film comprising dispersed nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] Figure 1 explains the terms "distribution" and "dispersion". Particles 1 are contained in a matrix 2 . exist Figure 1a In , particles 1 agglomerate in one region. The particles are neither dispersed nor distributed. exist Figure 1b In , there are several random clumps of particles 1 . These particles are distributed but not yet dispersed. exist Figure 1c In , the particles are both dispersed and distributed.

[0030] go to figure 2 , figure 2The method is shown. The general extrusion of polystyrene is known in the prior art. Polystyrene particles are added to the machine 20 through a hopper 21 and entrained by overlapping co-rotating screws 22 located in a cylinder 23 which melt the polystyrene by friction and shear. The temperature along the screw 22 is measured and controlled to ensure constant temperature and pressure. At the end of the machine 20, molten polystyrene is extruded through a die 24 to determine the shape of the emerging strip 25. The str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
relative permittivityaaaaaaaaaa
Login to View More

Abstract

A process of making a continuous freeform thermoplastic dielectric film that is evenly loaded with dispersed nanoparticles comprises the steps of; feeding thermoplastic granules into an extruder, injecting a secondary feed comprising a suspension of nanoparticles in a liquid carrier to create a nanocomposite, and extruding said composite onto cooled rollers at a preset rate thereby enabling the crystalline structure of the nanocomposite film to be controlled wherein the secondary feed is mixed continuously by an ultrasonicator whilst being injected into the extruder. By selecting the size of the nano particles based on their de Broglie wavelength in the crystalline polymer the dielectric can be produced in bulk to make high capacitance high energy density storage capacitors. The thermoplastic may be polystyrene, polypropylene or polyethylene terephthalate. The nanoparticles may be titanium dioxide. Additionally a second particle feed (for example silver) may be added.

Description

technical field [0001] This invention relates to dielectrics and their use in capacitors. A capacitor is a device that stores electrical charge and generally consists of two conducting plates separated by a dielectric. In an ideal system, the conductive plates hold their charge until discharge is required, and in doing so the conductive plates are able to supply power to the system in a controlled manner. Background technique [0002] Factors that affect capacitance are the area of ​​the plates, their spacing, and the ability of the dielectric between them to store charge and delay applied voltage. The dielectric can be made of any suitable insulating material. The greater the dielectric constant and dielectric breakdown strength, the more energy can be stored. Eventually any capacitor will fail when the potential difference rises above the dielectric strength and causes electrical breakdown of the dielectric. [0003] Dielectrics are often made from thermoplastics or th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C47/10B29C47/04B82Y30/00B29C47/88B29B7/90H01G4/14B29C48/08B29C48/10B29C48/16B29C48/305
CPCB29C48/16B29C48/914B29C48/08B29C48/287B29C48/288B29C48/142C08J5/18H01G4/18H01G4/206B29B7/90B29C43/222H01G4/14B29K2105/122B29K2105/124B29K2105/162B29K2995/0006B29C48/10B29C2948/92219C08J2325/06B29C48/022B29C2948/92714H01B3/442B29K2995/006B29K2025/06B29K2505/00B29K2505/14C08K3/08C08K3/22C08K2003/0806C08K2003/2241
Inventor M·A·布朗S·A·多诺万M·S·兰
Owner THE SEC OF STATE FOR DEFENCE IN HER BRITANNIC MAJESTYS GOVERNMENT OF THE UK OF GREAT BRITAIN & NORTHERN IRELAND