Infrared nonlinear optical single crystal sulfur tellurium indium barium
A technology of sulfur, tellurium, indium barium, and single crystal, which is applied in the field of infrared nonlinear optical materials, and can solve the problems that the comprehensive performance cannot reach people's ideal level.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] Embodiment 1: Preparation of sulfur tellurium indium barium single crystal
[0021] According to the molar ratio of BaS:In:Te:S as 5:4:4:2, weigh BaS, In, Te and S and mix them evenly, put them into a graphite crucible, then put them into a quartz tube, seal it after vacuuming, and place In a high-temperature furnace, it takes 50 hours to bring the temperature up to 850°C, and keep the temperature at 850°C for 30 hours, and then slowly lowers to room temperature at a certain rate to obtain red blocky crystals. Through single crystal X-ray diffraction analysis, it is shown that the compound is barium sulfur telluride indium, and the crystal parameters are as follows:
[0022] The unit cell parameters are α=β=γ=90, Z=2. Space group Imm2. The molecular weight is 1880.75.
[0023] The crystal structure is attached as figure 1 shown.
[0024] Powder infrared frequency doubling experiments show that under the irradiation of 2.05 μm laser light, the single crystal of ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap