Toughness-enhanced carbon fiber reinforced polyformaldehyde composite material and preparation method thereof

A composite material, polyoxymethylene technology, applied in the field of carbon fiber reinforced polyoxymethylene composite material and its preparation, can solve the problems of affecting product qualification rate, increasing cost, wasting resources, etc., and achieve the goal of improving competitiveness, increasing elasticity and improving fracture performance Effect

Inactive Publication Date: 2015-05-27
HEFEI KANGLING HEALTH TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

POM products are prone to cracking and deformation in the later stage of processing, which greatly affects the product qualification rate, wastes resources and increases costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] specific implementation plan

[0015] The present invention will be described in detail below through specific examples.

[0016] A carbon fiber reinforced polyoxymethylene composite material with enhanced toughness and a preparation method thereof, which is made of the following raw materials in parts by weight (kg): polyoxymethylene 100, carbon fiber 26, light calcium carbonate 6, copolyamide 3, fatty acid zinc 0.4, anti Oxygen agent 10100.5, thermoplastic elastomer G155D4, silane coupling agent KH-5500.5, graphene oxide 4, nano silicon dioxide 3;

[0017] A carbon fiber reinforced polyoxymethylene composite material with enhanced toughness and a preparation method thereof of the present invention are made by the following specific steps:

[0018] (1) Mix polyoxymethylene, thermoplastic elastomer G155D, fatty acid zinc and antioxidant 1010 into a high-speed mixer, stir evenly, and dry in a vacuum oven at 80°C for 3 hours for later use;

[0019] (2) Vacuum sinter th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
flexural modulusaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a toughness-enhanced carbon fiber reinforced polyformaldehyde composite material and a preparation method thereof. The composite material is characterized by being prepared from the following raw materials in parts by weight: 90-100 parts of polyformaldehyde, 10-30 parts of carbon fibers, 4-7 parts of light calcium carbonate, 2-4 parts of copolyamide, 0.4-0.5 part of fatty acid zinc, 0.3-0.5 part of an antioxidant 1010, 3-5 parts of thermoplastic elastomer G155D, 0.3-0.6 part of a silane coupling agent KH-550, 2-4 parts of oxidized graphene and 2-3 parts of nano silica. According to the invention, the added carbon fibers are dispersed evenly in polyformaldehyde after being preheated, so that the comprehensive properties of the material can be improved; the added thermoplastic elastomer is capable of increasing the elasticity of the polyformaldehyde and improving the fracture property; the added light calcium carbonate is capable of improving the toughness of the polyformaldehyde; as a result, the product competitiveness is greatly improved.

Description

technical field [0001] The invention relates to a toughness-enhanced carbon fiber-reinforced polyoxymethylene composite material and a preparation method thereof, belonging to the technical field of plastic production. Background technique [0002] As one of engineering plastics, polyoxymethylene is a high-density, highly crystalline linear polymer with high strength and modulus, good wear resistance, chemical corrosion resistance, creep resistance, fatigue resistance, and products Good dimensional stability and other characteristics, it is an ideal material to replace copper, zinc, aluminum and alloy products, and is widely used in automobile manufacturing, electrical and electronic, machinery, chemical and other fields. Most of the existing polyoxymethylene products in my country are general-purpose. In order to improve the use of products in the aerospace field, it must be transferred to high-end modified polyoxymethylene. Generally, it is modified in the form of composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L59/00C08L77/00C08L101/00C08K13/06C08K7/06C08K3/26C08K5/098C08K3/04C08K3/36
Inventor 朱正娟
Owner HEFEI KANGLING HEALTH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com