Automatic leakage stoppage adhesive for rubber tires

A technology for rubber tires and plugging rubber, which is applied to other rubber adhesives, adhesives, adhesive types, etc., can solve the problems of increased tire wear, high labor intensity, and soft tires, to prevent tire blowouts, The effect of pollution-free environment and low product price

Inactive Publication Date: 2015-06-03
招远市东晟橡胶制品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As we all know, tires rotate at high speed on the ground, and they are easy to rub against the ground to generate a lot of heat, which makes the tires soft, which not only increases tire wear, but also is easy to punctur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] An automatic plugging glue for rubber tires, comprising 5 parts of polyvinyl alcohol, 12 parts of ethylene glycol, 7 parts of methyl cellulose, 1 part of sodium nitrite, 1 part of gypsum powder, 10 parts of rubber powder, 4 parts of anti-aging agent, 2 parts of antifreeze, 3 parts of lime, 3 parts of white cement, 2 parts of preservative, 60 parts of water.

[0013] Preparation method: Take 5 parts of polyvinyl alcohol, 12 parts of ethylene glycol, 7 parts of methyl cellulose, 1 part of sodium nitrite, 1 part of gypsum powder, 10 parts of rubber powder, 4 parts of anti-aging agent, 2 parts of anti-aging agent, 3 parts of lime, 3 parts of white cement, 2 parts of preservative, and 60 parts of water are placed in a reaction kettle, heated and stirred to mix evenly, and cooled to obtain the finished product.

Embodiment 2

[0015] An automatic plugging glue for rubber tires, comprising 6 parts of polyvinyl alcohol, 13 parts of ethylene glycol, 8 parts of methyl cellulose, 2 parts of sodium nitrite, 2 parts of gypsum powder, 11 parts of rubber powder, 4.5 parts of anti-aging agent, 2.5 parts of antifreeze, 4 parts of lime, 4 parts of white cement, 2.5 parts of preservative, 70 parts of water.

[0016] Preparation method: Take 6 parts of polyvinyl alcohol, 13 parts of ethylene glycol, 8 parts of methyl cellulose, 2 parts of sodium nitrite, 2 parts of gypsum powder, 11 parts of rubber powder, 4.5 parts of anti-aging agent, 2.5 parts of old refrigerant, 4 parts of lime, 4 parts of white cement, 2.5 parts of preservative, and 70 parts of water are placed in a reaction kettle, heated and stirred to mix evenly, and cooled to obtain the finished product.

Embodiment 3

[0018] An automatic plugging glue for rubber tires, 7 parts of polyvinyl alcohol, 14 parts of ethylene glycol, 9 parts of methyl cellulose, 3 parts of sodium nitrite, 3 parts of gypsum powder, 12 parts of rubber powder, 5 parts of anti-aging agent, 3 parts of antifreeze, 5 parts of lime, 5 parts of white cement, 3 parts of preservative, 80 parts of water.

[0019] Preparation method: Take 7 parts of polyvinyl alcohol, 14 parts of ethylene glycol, 9 parts of methyl cellulose, 3 parts of sodium nitrite, 3 parts of gypsum powder, 12 parts of rubber powder, 5 parts of anti-aging agent, 3 parts of anti-aging agent, 5 parts of lime, 5 parts of white cement, 3 parts of preservative, and 80 parts of water are placed in a reaction kettle, heated and stirred to mix evenly, and cooled to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an adhesive, particularly an automatic leakage stoppage adhesive for rubber tires. The invention is characterized in that the automatic leakage stoppage adhesive for rubber tires is prepared from the following raw materials in parts by weight: 5-7 parts of polyvinyl alcohol, 12-14 parts of ethylene glycol, 7-9 parts of methyl cellulose, 1-3 parts of sodium nitrate, 1-3 parts of gypsum powder, 10-12 parts of rubber powder, 4-5 parts of anti-aging agent, 2-3 parts of antifreezing agent, 3-5 parts of lime, 3-5 parts of white cement, 2-3 parts of preservative and 60-80 parts of water. The automatic leakage stoppage adhesive for rubber tires can quickly fill and repair the rupture without influencing normal running, can absorb heat under the high-temperature high-speed conditions, prevents tire burst, and is capable of preventing volatilization and freezing and resisting tire aging. The automatic leakage stoppage adhesive for rubber tires has the advantages of simple manufacturing technique, no environment pollution, low flammability, no toxicity, low price and quick effect taking, and can be easily received by people.

Description

[0001] technical field [0002] The invention relates to an adhesive, in particular to an automatic plugging adhesive for rubber tires. Background technique [0003] As we all know, tires rotate at high speed on the ground, and they are easy to rub against the ground to generate a lot of heat, which makes the tires soft, which not only increases tire wear, but also is easy to puncture and explode. Tire repair is an indispensable technology. The traditional tire repairing technology is by manual tire, labor-intensive, not suitable for the needs of modern social and economic development. [0004] As an important part of the car, the car tire is an important part of the car to bear gravity, transmit traction force, braking force, steering force and bear the reaction force of the road surface. Its quality is directly related to personal and property safety. Contents of the invention [0005] In order to overcome the shortcomings of the prior art, the present invention provide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J121/00C09J101/28C09J129/04C09J11/04
Inventor 石德龙
Owner 招远市东晟橡胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap