Emulsion-type antifoaming agent used for rubber and plastic

An emulsion-type defoamer, rubber and plastic technology, applied in the direction of foam dispersion/prevention, can solve problems affecting the performance of rubber and resin products, environmental hazards, adverse effects of rubber and plastic polymers, etc., to achieve strong antifoaming ability, eliminate The effect of fast brewing speed and easy operation

Inactive Publication Date: 2015-06-10
QINGDAO HAOTAI WATER
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of chemical additives is convenient for its manufacture, but if used improperly, it will have a negative impact on rubber and plastic polymers, and eventually affect the performance of rubber and resin products, or produce some by-products, causing a certain degree of harm to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An emulsion type defoamer for rubber and plastics, comprising the following substances:

[0019] C 5 Alcohol amine 13 parts, hydrocarbonated oil 40 parts, C 11 25 parts of fatty acid, 5 parts of antifoaming agent, 4 parts of modified sodium lignosulfonate, appropriate amount of water.

[0020] The emulsion type defoamer for rubber and plastic is made by the following steps:

[0021] (1) Hydrocarbonated oil, C 5 Alcoholamine, C 11 Fatty acids were esterified for 50 minutes at a temperature of 100°C.

[0022] (2) Mix the esterification product (1) with anti-foaming agent and dispersant, add water and emulsify for 2.5 hours at 30-40°C to obtain the anti-foaming agent.

[0023] The emulsion type defoamer for rubber and plastics has good defoaming ability and fast defoaming speed.

Embodiment 2

[0025] An emulsion type defoamer for rubber and plastics, comprising the following substances:

[0026] C 6 Alcohol amine 15 parts, hydrocarbonated oil 42 parts, C 15 27 parts of fatty acid, 6 parts of antifoaming agent, 5 parts of sodium lignosulfonate, appropriate amount of water.

[0027] The emulsion type defoamer for rubber and plastic is made by the following steps:

[0028] (1) Hydrocarbonated oil, C 6 Alcoholamine, C 15 Fatty acids were esterified for 120min at a temperature of 80°C.

[0029] (2) Mix the esterified product (1) with anti-foaming agent and dispersant, add water and emulsify for 2 hours at 40-45°C to obtain the anti-foaming agent.

[0030] The latex-type defoamer for rubber and plastics has good anti-foaming ability and has no adverse effect on rubber and plastic polymers.

Embodiment 3

[0032] An emulsion type defoamer for rubber and plastics, comprising the following substances:

[0033] C 8 Alcohol amine 18 parts, hydrocarbonated oil 48 parts, C 18 30 parts of fatty acid, 8 parts of antifoaming agent, 8 parts of sodium lignosulfonate, appropriate amount of water.

[0034] The emulsion type defoamer for rubber and plastic is made by the following steps:

[0035] (3) Hydrocarbonated oil, C 8 Alcoholamine, C 18 Fatty acids were esterified for 150 minutes at a temperature of 150°C.

[0036] (4) Mix the esterification product (1) with anti-foaming agent and dispersant, add water and emulsify for 4 hours at 65-70°C to obtain the anti-foaming agent.

[0037] The latex-type defoamer for rubber and plastics has good anti-foaming ability and has no adverse effect on rubber and plastic polymers.

[0038] The defoamer can eliminate foam, the preparation method is simple, easy to operate, the defoaming speed is fast, the foam suppression ability is strong, it has ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an emulsion-type antifoaming agent used for rubber and plastic, which belongs to the chemical preparation field. The emulsion-type antifoaming agent used for rubber and plastic comprises the following components by weight part: 13-20 parts of alkylol amine, 40-50 parts of alkymer, 25-30 parts of aliphatic acid, 5-10 parts of assisted antifoaming agent, 4-10 parts of dispersant and a proper amount of water. The emulsion-type antifoaming agent is capable of eliminating foams, and has the advantages of simple preparation, easy operation, fast defoaming speed and strong foam inhibition capability, the emulsion-type antifoaming agent has no adverse influence on rubber and plastic polymers, no by-product, waste water, exhaust gas and solid waste materials can be generated during a reaction process, and no pollution is generated on environment.

Description

technical field [0001] The invention belongs to a defoamer, in particular to an emulsion type defoamer for rubber and plastic. Background technique [0002] Rubber and plastic is the collective name of the rubber and plastic industries. They are all subsidiary products of petroleum. They are all the same in source. However, in the process of making products, their physical properties are different, and their uses are even more different. The most common is tires. Plastics are becoming more and more widely used with the needs and uses of technology and markets, and they are inseparable from daily life. [0003] Both plastic and rubber belong to polymer materials, mainly composed of carbon and hydrogen atoms, and some contain a small amount of oxygen, nitrogen, chlorine, silicon, fluorine, sulfur and other atoms, which have special properties and uses. At room temperature, Plastic is solid, very hard, and cannot be stretched and deformed. Rubber is not very hard, but elastic,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D19/04
Inventor 徐苹绍星红
Owner QINGDAO HAOTAI WATER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap