Plugging agent for oilfield development
A technology of oil field development and plugging agent, which is applied in the direction of drilling composition, chemical instruments and methods, etc., can solve the problems of different water discharge patterns, etc., and achieve the effects of long validity period, wide application range and obvious plugging advantages
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] Preparation method of plugging agent: Add 10g of unsaturated resin 196# and 1.5g of emulsifier Tween 80 into a three-neck flask, stir at 600r / min at 25°C, add 20ml of deionized water at a constant speed of 1mL / min, and heat at 25°C Under the conditions of 600r / min stirring for 0.5h, the unsaturated resin emulsion is formed; then 9g of curing agent hydrogen peroxide and 4.5g of coupling agent organosilicon compound KH-550 are added to the above unsaturated resin emulsion. Stir at 30°C for 0.5h to obtain the plugging agent for profile control and water plugging.
[0024] In the blocking agent, the mass ratio of 196 unsaturated polyester resin in the unsaturated resin emulsion to the emulsifier is 6.67:1, and the amount of 196 unsaturated polyester resin is 31.75wt% of the unsaturated resin emulsion; And in the blocking agent, the unsaturated resin emulsion is 70wt%, the curing agent is 20wt%, and the coupling agent is 10wt%.
[0025] The test conditions for the plugging ...
Embodiment 2
[0027] The preparation method of the plugging agent is the same as in Example 1, but the amount of each raw material is changed so that the mass ratio of the 196 unsaturated polyester resin to the emulsifier in the unsaturated resin emulsion is 3:1, and the amount of 196 unsaturated polyester resin It is 20wt% of the unsaturated resin emulsion; and the unsaturated resin emulsion in the blocking agent is 72wt%, the curing agent is 21wt%, and the coupling agent is 7wt%.
[0028] The test conditions of the plugging agent in this example are: at 60°C, the permeability of the core is 0.46 μm 2 And when the plugging agent injection volume is 0.4 times PV (core pore volume); the breakthrough pressure gradient of the system is >60MPa / m, and the core plugging rate is 100%.
Embodiment 3
[0030] The preparation method of the blocking agent is the same as in Example 1, but the amount of each raw material is changed so that the mass ratio of the 196 unsaturated polyester resin in the unsaturated resin emulsion to the emulsifier is 10:1, and the amount of the 196 unsaturated polyester resin It is 25wt% of the unsaturated resin emulsion; and the unsaturated resin emulsion in the blocking agent is 65wt%, the curing agent is 25wt%, and the coupling agent is 10wt%.
[0031] The test conditions for the plugging agent in this example are: at 50°C, the permeability of the core is 1.98 μm 2 And when the plugging agent injection volume is 0.4 times PV (core pore volume); the breakthrough pressure gradient of the system is >60MPa / m, and the core plugging rate is 100%.
PUM
Property | Measurement | Unit |
---|---|---|
compressive strength | aaaaa | aaaaa |
core plugging rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com