Tea plastic tableware and preparation method thereof

A technology for dining utensils and tea plastics, which is applied in the field of dining utensils and their preparation, can solve the problems of less research on the application of tea-plastic composite dining utensils and wood-plastic composite materials, and achieves enhanced mechanical properties, reduced white pollution, and reduced effect of dosage

Inactive Publication Date: 2015-07-08
FUJIAN AGRI & FORESTRY UNIV
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the raw materials used for wood-plastic composite material filling mainly come from bamboo, pine wood, camphor wood, straw and waste paper, etc. The wood-plastic composite materials prepared by the predecessors with these natural plant fiber materials are mainly used for pallets, packaging, furniture, In the fields of automobiles, gardens, and construction, there are few researches on the application of wood-plastic composite materials in catering utensils, and there are no related reports on the use of tea-plastic composite materials to prepare catering utensils

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1, a kind of preparation method of tea-plastic catering utensils, comprises the following steps:

[0018] 1. Preparation of materials:

[0019] (1) Preparation of tea by-product powder: take the tea by-product, dry to a moisture content of 3%, then pulverize and pass through a 100-mesh sieve to prepare the tea by-product powder for later use;

[0020] (2) Dry the high-density polyethylene resin: dry the high-density polyethylene resin at 105°C for 4.5 hours, and set aside;

[0021] (3) drying maleic anhydride grafted polyethylene: dry the maleic anhydride grafted polyethylene at 85°C for 3 hours, and set aside;

[0022] 2. Mixing: In parts by mass, take 35 parts of tea by-product powder in step 1, 65 parts of dry high-density polyethylene resin, and 10 parts of dry maleic anhydride grafted polyethylene, and put them in a mixer at 90°C. 300r·min -1 Mix for 15min to prepare the mixed material;

[0023] 3. Take the mixed material in step 2 at 175°C, 40r min ...

Embodiment 2

[0025] Embodiment 2: a kind of preparation method of tea plastic dining utensils, comprises the following steps:

[0026] 1. Prepare materials

[0027] (1) Preparation of tea by-product powder: take the tea by-product, dry to a moisture content of 8%, then pulverize and pass through a 100-mesh sieve to prepare the tea by-product powder for later use;

[0028] (2) Dry the high-density polyethylene resin: dry the high-density polyethylene resin at 110°C for 5 hours, and set aside;

[0029] (3) drying maleic anhydride grafted polyethylene: dry the maleic anhydride grafted polyethylene at 90°C for 3 hours, and set aside;

[0030] 2. Mixing: Take 40kg of tea by-product powder from step 1, 60kg of dry high-density polyethylene resin, and 8kg of dry maleic anhydride grafted polyethylene, and put them in a mixer at 90°C at 300r min -1 Mix for 20min to prepare the mixed material;

[0031] 3. Take the mixed material in step 2 at 175°C, 40r min -1 Mix in an internal mixer for 12 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to tea plastic tableware and a preparation method thereof. The preparation method of the tea plastic tableware comprises the following steps: preparing materials, mixing, preparing tea plastic powder and preparing tea plastic tableware. According to the preparation method of the tea plastic tableware, the use amount of high-density polyvinyl resin can be decreased by taking tea side products as stuffing, the white pollution can be effectively reduced, and the mechanical performance of the tea plastic tableware can be enhanced. The tea plastic tableware produced by adopting the method is made of tea plastic composite materials, and internally has a complicated network structure, and the stability of the tea plastic tableware product can be guaranteed. Furthermore, the tea side product contains cellulose, crude protein, tea polyphenol, amino acid, saponin, aromatic substances and the like, the tea plastic tableware prepared by taking tea side products as stuffing has antibacterial action to certain extent, and can emit pleasant tea aroma.

Description

technical field [0001] The invention relates to a catering utensil and a preparation method thereof, in particular to a tea-plastic catering utensil using tea by-products as natural fiber fillers and a preparation method thereof. Background technique [0002] China is the hometown of tea, and it is also a big tea production and consumption country. Tea by-products such as tea stems, tea dust, tea dregs and tea prunings will be produced during the tea production process. Most of these tea by-products are discarded. These by-products are rich in natural plant fibers and are good filling materials for wood-plastic composite materials. [0003] At present, the raw materials used for wood-plastic composite material filling mainly come from bamboo, pine wood, camphor wood, straw and waste paper, etc. The wood-plastic composite materials prepared by the predecessors with these natural plant fiber materials are mainly used for pallets, packaging, furniture, In the fields of automob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L97/02C08L51/06C08L89/00
CPCC08L23/06C08L2205/03C08L2207/062
Inventor 杨江帆于学领叶乃兴杨文斌高水练郑德勇
Owner FUJIAN AGRI & FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com