3D Curved ultrathin glass bending and forming device and manufacturing method

A technology of ultra-thin glass and bending forming, which is applied in glass forming, glass reshaping, glass manufacturing equipment, etc., can solve the problems of lower pass rate in the production process, poor bending accuracy, cracking of ultra-thin glass, etc., and achieve saving Effect of working time, reducing stress, ensuring light transmission and cleanliness

Active Publication Date: 2015-08-19
海程光电科技有限公司
View PDF6 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current invention patents are mainly aimed at automobile windshields or condenser mirrors, such as patents CN101720308A, CN1856451A, CN103402934A, etc., all of which are aimed at bending glass with a thickness greater than 1 mm, while the thickness of ultra-thin glass used for screen protection is generally 0.1- 0.4 mm, parameters such as forming device, mold shape, stress control, and temperature field control are very critical in the hot bending process of ultra-thi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 3D Curved ultrathin glass bending and forming device and manufacturing method
  • 3D Curved ultrathin glass bending and forming device and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] The present invention provides such as figure 1 A 3D curved ultra-thin glass bending forming device shown includes a turntable 1 , a die 2 , a punch 3 , a cylinder 4 , a glass transfer mechanism 5 , a tunnel furnace 7 , a vacuum system 8 and an electrical control operating system 9 .

[0032] Described die 2 is arranged evenly around the turntable 1; Described punch 3 is arranged on the corresponding top of the die 2 of turntable 1 station, and cylinder 4 is set above punch 3; Described turntable 1, The glass transfer mechanism 5 and the tunnel furnace 7 are sequentially connected; the electrical control operating system 9 is arranged on the side of the device; the vacuum system 8 is arranged in the casing of the molding device.

[0033] The turntable 1 is made of quartz glass, and a rotating mechanism is arranged in the housing of the molding device corresponding to the turntable 1; the turntable 1 is evenly provided with 6 concave molds 2 made of...

Example Embodiment

[0038] Example 2

[0039] Based on the device of embodiment 1, a manufacturing method of a 3D curved ultra-thin glass is as follows:

[0040] (1) Automatically controlled by the temperature controller, die 2 is raised to 450°C at a rate of 30°C / min, and then raised to 650°C at a rate of 50°C / min, and the temperature of punch 3 is raised to 50°C / min Speed ​​up to 650°C.

[0041] (2) The ultra-thin glass 6 with a thickness of 0.3 mm is cut to a size of 154.6×74.8 mm in length and width, and is ground and chamfered by a CNC machine tool. ° on the die 2, and turn on the turntable 1 to rotate clockwise.

[0042] (3) When the die 2 on the turntable 1 rotates to the position corresponding to the punch 3, press the punch 3 down, and when the temperature reaches the softening temperature of ultra-thin glass 650 °C, vacuumize to -0.15 Pa, and use a negative Press to preform the ultra-thin glass 6 for 10 seconds, then apply a pressure of 0.2 Pa on the punch 3 and keep the pressure f...

Example Embodiment

[0044] Example 3

[0045] Based on the device of embodiment 1, a manufacturing method of a 3D curved ultra-thin glass is as follows:

[0046] (1) Automatically controlled by the temperature controller, die 2 is raised to 500°C at a rate of 10°C / min, and then raised to 680°C at a rate of 100°C / min, and the temperature of punch 3 is raised to 100°C / min Speed ​​up to 680°C.

[0047] (2) The ultra-thin glass 6 with a thickness of 0.2 mm is cut to a size of 154.6×74.8 mm in length and width, and is ground and chamfered by a CNC machine tool, and then the ultra-thin glass 6 is placed 2.6 mm inwards from the two long sides in turn. On the concave mold 2 bent at 5°, and turn on the turntable 1 to rotate clockwise.

[0048] (3) When the die 2 on the turntable 1 rotates to the position corresponding to the punch 3, press the punch 3 down, and when the temperature reaches the softening temperature of ultra-thin glass at 680 °C, vacuumize to -0.1 Pa, and use a negative Press to prefo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a 3D curved ultrathin glass bending and forming device and a manufacturing method. The device comprises a rotor disc, concave dies, a convex die, a cylinder, a glass transfer mechanism, a tunnel furnace, a vacuum system and an electric control operating system, and a plurality of concave dies are arranged on the rotor disc. By adopting the device, the concave dies and the convex die are quickly heated in different stages; the ultrathin glass is sequentially placed on the concave dies of the rotor disc and is subjected to preheating; when the ultrathin glass rotates and reaches the corresponding work station on the convex die, the convex die is pressed, and a far infrared lamp tube is utilized to quickly heat to the glass softening point; in addition, the ultrathin glass on the concave dies is sucked and the convex die is pressurized by virtue of the vacuum system, so that the ultrathin glass is bended; the ultrathin glass is transferred to the tunnel furnace to be cooled by virtue of the glass transfer mechanism, so that the 3D curved ultrathin glass can be manufactured.

Description

technical field [0001] The invention relates to a bending forming device and a manufacturing method of 3D curved ultra-thin glass, in particular to a bending forming device and a batch manufacturing method of 3D curved ultra-thin glass used for a curved display screen protective film. Background technique [0002] Recently, curved display technology has become increasingly mature and has begun to be applied in the display field. For example, Apple, Samsung and LG mobile phone displays have begun to use curved display technology. The application of curved display technology can greatly improve the display design. The degree of freedom is also the trend of personalized development of display screens such as mobile phones in the future. For example, the Apple Iphone6 ​​mobile phone recently launched by Apple adopts the arc edge technology with four edges bent downward. Therefore, there is an urgent need for a technology to realize the bending of ultra-thin glass for the protect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03B23/03
CPCY02P40/57
Inventor 朱归胜徐华蕊
Owner 海程光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap