Ecological resin board and preparation method thereof

A technology of ecological resin board and ecological plant, applied in the field of ecological resin board and its preparation, can solve the problems of poor stability of physical properties, narrow molding temperature range, deterioration of product adhesion, etc., and achieve safe and convenient installation, stable physical properties, The effect of high mechanical strength

Inactive Publication Date: 2015-08-19
常州伊柯瑞斯装饰材料有限公司 +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing ecological resin boards still have the following technical deficiencies: (1) The molding temperature range is narrow, and at low molding temperatures, the edges of the product may crack, or the adhesion of the product may deteriorate
(2) Low surface hardness: not scratch-resistant, prone to scratches; (3) Poor stability of physical properties: low transparency, low heat distortion temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An ecological resin board, characterized in that, the ecological resin board is made of PEGT board, the embedded material is 100% natural ecological plants, and the surface of the ecological resin board is frosted.

[0031] The 100% natural ecological plants use leaf veins and bamboo rings, and the mass ratio of the leaf veins to bamboo rings is 1:1.

[0032] A method for preparing an ecological resin board, said method comprising the following steps:

[0033] (1) Put the raw materials to be processed into the automatic pressure equipment, automatically heat at a constant temperature, set the heating temperature to 100°C, the pressure to 20MPa, and control the constant temperature time to 120min to obtain the required plate;

[0034] (2) Mold cooling: Cool the mold with frozen water, and control the temperature range of the mold: 15°C; the mold is made of wood.

[0035] (3) Special-shaped processing: put the plate prepared in step (1) into a mold, heat to 105°C, and ex...

Embodiment 2

[0037] An ecological resin board, characterized in that, the ecological resin board is made of PEGT board, the embedded material is 100% natural ecological plants, and the surface of the ecological resin board is frosted.

[0038] The 100% natural ecological plants use leaf veins and bamboo rings, and the mass ratio of the leaf veins to bamboo rings is 1:3.

[0039] A method for preparing an ecological resin board, said method comprising the following steps:

[0040] (1) Put the raw materials to be processed into the automatic pressure equipment, automatically heat at a constant temperature, set the heating temperature to 115°C, the pressure to 20MPa, and control the constant temperature time to 100min to obtain the required plate;

[0041] (2) Mold cooling: Cool the mold with frozen water, and control the temperature range of the mold: 35°C; the mold is made of glass fiber reinforced plastic;

[0042] (3) Special-shaped processing: put the plate prepared in step (1) into a m...

Embodiment 3

[0044] An ecological resin board, characterized in that, the ecological resin board is made of PEGT board, the embedded material is 100% natural ecological plants, and the surface of the ecological resin board is frosted.

[0045] The 100% natural ecological plant selects leaf veins and bamboo rings, and the mass ratio of the leaf veins and bamboo rings is 1:5.

[0046] A method for preparing an ecological resin board, said method comprising the following steps:

[0047] (1) Put the raw materials to be processed into the automatic pressure equipment, automatically heat at a constant temperature, set the heating temperature to 130°C, the pressure to 20MPa, and control the constant temperature time to 90min to obtain the required plate;

[0048] (2) Mold cooling: Cool the mold with frozen water, and control the temperature range of the mold: 40°C; the mold is made of glass fiber reinforced plastic;

[0049] (3) Special-shaped processing: put the plate prepared in step (1) into ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of artificial boards and in particular relates to an ecological resin board and a preparation method thereof. The raw material of the ecological resin board is a PEGT board, and the embedded material of the ecological resin board is 100% natural ecological plant; the surface of the ecological resin board is frosted. The 100% natural ecological plant is one or several of such materials as leaf veins, bamboo circles, sea grass, tree branches and silk fabrics. The ecological resin board has outstanding tenacity and high shock strength; the shock strength is 3-10 times that of modified polyacrylates; the ecological resin board also has a quite wide processing range, extremely high mechanical strength and excellent flexibility; compared with PVC, the ecological resin board is high in transparency, good in gloss, prone to printing and environmental friendly.

Description

technical field [0001] The invention relates to the technical field of wood-based panels, in particular to an ecological resin panel and a preparation method thereof. Background technique [0002] Decorative sheets based on polyethylene terephthalate (PETG) for molding purposes show excellent surface properties compared with polyvinyl chloride (PVC), PETG products are highly transparent and have excellent impact resistance, which can maintain the toughness of the product , to prevent yellowing. PETG sheets are easy to produce products with complex shapes and large draw ratios. Also, unlike PC board and impact-modified acrylic, the board does not require pre-drying prior to thermoforming. Compared with PC board and acrylic board, its molding cycle is shorter, the temperature is lower, and the yield is higher. [0003] The existing ecological resin boards still have the following technical deficiencies: (1) The molding temperature range is narrow, and at low molding tempera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L97/02
Inventor 尚国萍殷东波
Owner 常州伊柯瑞斯装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com