Fabric with flame-retardant function and anti-bacterial function and manufacturing method of fabric

A fabric and functional technology, applied in the field of fabrics with flame retardant and antibacterial functions and its preparation, can solve the problems of difficulty in obtaining flame retardant effect, only flame retardant effect, limited flame retardant effect, etc., and achieve significant flame retardant effect, The effect of excellent antibacterial performance, good durability and service life

Active Publication Date: 2015-08-19
HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this kind of non-woven fabric has flame retardant properties, it also has shortcomings. First, the flame retardants that make up the flame retardant layer are all single components, and the flame retardant effect that can be played is limited, and it is difficult to Obtain significant flame retardant effect; secondly, only flame retardant effect, but no antibacterial function; thirdly, the preparation method cannot obtain a product with both significant flame retardant effect and antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabric with flame-retardant function and anti-bacterial function and manufacturing method of fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The concrete steps of preparation are:

[0034] Step 1, adding polyhexamethylene guanidine salt and polyphosphate salt into deionized water respectively and stirring for 1 hour to obtain 0.05g / 100g polyhexamethylene guanidine salt aqueous solution and 5g / 100g polyphosphate aqueous solution; wherein, poly The hexamethylene guanidine salt is polyhexamethylene guanidine phosphate, and the polyphosphate is ammonium polyphosphate.

[0035] Step 2, first immerse the fabric in the polyhexamethyleneguanidine saline solution for 10 seconds, then take it out, rinse it with distilled water for 120 seconds, and then place it at 50°C for 60 minutes to obtain a fabric stained with polyhexamethyleneguanidine salt; , the fabric is cotton fabric. Then soak the fabric stained with polyhexamethylene guanidine salt in the polyphosphate aqueous solution for 10 seconds, take it out, rinse it with distilled water for 120 seconds, and then place it at 50°C for 60 minutes to obtain polyhexamet...

Embodiment 2

[0038] The concrete steps of preparation are:

[0039] Step 1, adding polyhexamethylene guanidine salt and polyphosphate salt into deionized water respectively and stirring for 1.5h to obtain 1.25g / 100g polyhexamethylene guanidine salt aqueous solution and 3.75g / 100g polyphosphate aqueous solution; wherein , polyhexamethylene guanidine salt is polyhexamethylene guanidine phosphate, and polyphosphate is ammonium polyphosphate.

[0040] Step 2, first immerse the fabric in the polyhexamethyleneguanidine saline solution for 35 seconds, then take it out, rinse it with distilled water for 95 seconds, and then place it at 58°C for 50 minutes to obtain a fabric stained with polyhexamethyleneguanidine salt; , the fabric is cotton fabric. Then soak the fabric stained with polyhexamethylene guanidine salt in the polyphosphate aqueous solution for 35s, take it out, rinse it with distilled water for 95s, and then bake it at 58°C for 50min to obtain polyhexamethylene Guanidine-salted and ...

Embodiment 3

[0043] The concrete steps of preparation are:

[0044] Step 1, adding polyhexamethylene guanidine salt and polyphosphate salt into deionized water respectively and stirring for 2h to obtain 2.5g / 100g polyhexamethylene guanidine salt aqueous solution and 2.5g / 100g polyphosphate aqueous solution; wherein, The polyhexamethylene guanidine salt is polyhexamethylene guanidine phosphate, and the polyphosphate is ammonium polyphosphate.

[0045]Step 2, first immerse the fabric in the polyhexamethyleneguanidine saline solution for 65 seconds, then take it out, rinse it with distilled water for 70 seconds, and then dry it at 65°C for 40 minutes to obtain a fabric stained with polyhexamethyleneguanidine salt; , the fabric is cotton fabric. Then soak the fabric stained with polyhexamethylene guanidine salt in the polyphosphate aqueous solution for 65 seconds, take it out, rinse it with distilled water for 70 seconds, and then bake it at 65°C for 40 minutes to obtain polyhexamethylene gua...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fabric with a flame-retardant function and an anti-bacterial function and a manufacturing method of the fabric. The functional fabric is formed by covering a fabric with more than one layer of polyhexamethylene guanidine salting layer and a polyphosphate salting layer on the polyhexamethylene guanidine salting layers. The manufacturing method includes the steps of dipping the fabric in a 0.05-5g / 100g polyhexamethylene guanidine saline solution for 10-120 seconds prior to taking out, washing with distilled water for 20-120 seconds, and drying at the temperature of 50-80 DEG C for 20-60 minutes to obtain the fabric with polyhexamethylene guanidine salting; dipping the fabric with the polyhexamethylene guanidine salting in a 0.05-5g / 100g polyphosphate saline solution for 10-120 seconds prior to taking out, washing with the distilled water for 20-120 seconds, and drying at the temperature of 50-80 DEG C for 20-60 minutes to obtain the fabric with the polyhexamethylene guanidine salting and polyphosphate salting; repeating the two steps for at least more than 0 time to obtain the fabric with the flame-retardant function and the anti-bacterial function. The fabric with the flame-retardant function and the anti-bacterial function is excellent in the flame-retardant function and the anti-bacterial function, is durable in quality and can be widely used in daily life of people.

Description

technical field [0001] The invention relates to a fabric and a preparation method, in particular to a fabric with flame-retardant and antibacterial functions and a preparation method thereof. Background technique [0002] Textile fabrics have been widely used in people's daily life, such as various cotton fabrics, hemp fabrics, chemical fiber fabrics, and their blended fabrics. These fabric materials are extremely flammable, and the flame spreads fast and is not easy to extinguish. At the same time, the dense smoke generated during the burning process also poses a huge threat to the natural environment and human life safety; in addition, the cellulose molecular chains in the fabric contain a large amount of Hydroxyl, therefore highly hygroscopic, provides a good living environment for the growth of bacteria. The bacteria they breed will not only pose a threat to human health, but also destroy the structure of cellulose by releasing acidic substances, causing the degradation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/37D06M11/72
Inventor 方飞张献丁欣陈小璇陈召包超田兴友
Owner HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap