A kind of preparation method of PET composite material used for packaging tape

A composite material and packaging tape technology, applied in the field of packaging materials, can solve problems such as poor corona resistance and water resistance, narrow application scope, etc., and achieve the effects of good water resistance, prolonged corona resistance life, and extended discharge path.

Active Publication Date: 2016-12-07
浙江恩特包装新材料股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the PET composite resin material has the defects of poor corona resistance and water resistance, which narrows its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of PET composite material used for packaging tape

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation method for a PET composite material of a packing tape, comprising the following steps:

[0024] (1) Grind the beidellite with a grinder and sieve it to obtain beidellite powder with a particle size of 300 mesh. Add the beidellite powder to distilled water and stir for 30 minutes to make a pulp. Adjust the ph value of the pulp to 7.5 and add CTAB The aqueous solution, the weight ratio of beidellite powder, distilled water, CTAB is 5: 55: 1, moves to the constant temperature water bath that temperature is 70 ℃ and stirs for 3 hours, obtains white precipitate after suction filtration, washes 5 times with deionized water, Place in an oven at a temperature of 90°C and dry for 12 hours to obtain modified beidellite powder for use;

[0025] (2) Dissolve 6 parts by weight of the modified beidellite powder obtained in step (1) in an organic solvent mixed with phenol and tetrachloromethane in a weight ratio of 1:1, and add 78 parts by weight after ultrasonic stirrin...

Embodiment 2

[0028] A preparation method for a PET composite material of a packing tape, comprising the following steps:

[0029] (1) Grind the beidellite with a grinder and sieve it to obtain beidellite powder with a particle size of 300 mesh. Add the beidellite powder to distilled water and stir for 30 minutes to make a pulp. Adjust the ph value of the pulp to 7.5 and add CTAB The aqueous solution, the weight ratio of beidellite powder, distilled water, CTAB is 5: 55: 1, moves to the constant temperature water bath that temperature is 70 ℃ and stirs for 3 hours, obtains white precipitate after suction filtration, washes 5 times with deionized water, Place in an oven at a temperature of 90°C and dry for 12 hours to obtain modified beidellite powder for use;

[0030] (2) 5 parts by weight of the modified beidellite powder obtained in step (1) are dissolved in an organic solvent mixed with phenol and tetrachloromethane in a weight ratio of 1:1, and 77 parts by weight of the powder are added...

Embodiment 3

[0033] A preparation method for a PET composite material of a packing tape, comprising the following steps:

[0034] (1) Grind the beidellite with a grinder and sieve it to obtain beidellite powder with a particle size of 300 mesh. Add the beidellite powder to distilled water and stir for 30 minutes to make a pulp. Adjust the ph value of the pulp to 7.5 and add CTAB The aqueous solution, the weight ratio of beidellite powder, distilled water, CTAB is 5: 55: 1, moves to the constant temperature water bath that temperature is 70 ℃ and stirs for 3 hours, obtains white precipitate after suction filtration, washes 5 times with deionized water, Place in an oven at a temperature of 90°C and dry for 12 hours to obtain modified beidellite powder for use;

[0035] (2) 4 parts by weight of the modified beidellite powder obtained in step (1) are dissolved in an organic solvent mixed with phenol and tetrachloromethane in a weight ratio of 1: 1, and 81 parts by weight are added after ultras...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a PET composite for a packaging tape. The preparation method comprises the following steps of (1) sieving after grinding beidellite by using a grinder to obtain beidellite powder, adding the beidellite powder into distilled water and stirring to obtain ore pulp, adding a CTAB water solution after regulating the ph value to 7.5, transferring the water solution to a thermostatic water bath to stir, carrying out suction filtration to obtain a white sediment, washing five times, and drying to obtain modified beidellite powder for later use; (2) dissolving the modified beidellite powder into an organic solvent, adding PET particles after ultrasonically stirring, stirring in a water bath, pouring the material into a vessel with a cover, placing the vessel with the cover into a fuming cupboard, and after the organic solvent is volatilized, transferring the vessel with the cover to a vacuum drying oven to dry for 15 hours to obtain a mixed material; and (3) after drying melamine-formaldehyde resin, placing the melamine-formaldehyde resin and the mixed material into a high-speed mixer to mix for 15 minutes, and transferring the mixture to a double-screw extruder to extrude to obtain the PET composite for the packaging tape. The composite prepared by using the preparation method has relatively good corona resistance and water resistance and can be applied to various occasions.

Description

Technical field: [0001] The invention relates to a packaging material, in particular to a preparation method of a PET composite material used for a packaging tape. Background technique: [0002] PET is the abbreviation of Polyethyleneterephthalate in English, and its Chinese meaning is polyethylene terephthalate. The molecular structure of PET is highly symmetrical, and it has certain crystal orientation ability. PET is a milky white or light yellow highly crystalline polymer with a smooth and shiny surface, good creep resistance, fatigue resistance, friction resistance, low wear and high hardness, and has the greatest toughness among thermoplastics; good electrical insulation performance , less affected by temperature, non-toxic, weather resistance, good stability against chemicals, weak acid and organic solvent resistance, so it can be widely used in fiber, film, packaging materials and other fields. [0003] For example, the Chinese patent with the publication number CN1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08L61/28C08K9/04C08K3/34B29C47/92B29C48/92
Inventor 矫磊
Owner 浙江恩特包装新材料股份有限公司