Conveyor roller high temperature resistant acid and alkali resistant rubber coated layer

A rubber coating, high temperature resistant technology, applied in the field of conveyors, can solve the problems of cracks, cracks, sticky rubber layer, etc.

Inactive Publication Date: 2015-09-09
ANHUI JIAMU RUBBLE & PLASTIC IND
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The rubber coating layer of the existing ordinary rollers cannot work in chemicals such as acid, alkali, and salt solution. When the rubber coating layer of ordinary rollers is in contact with acid, alkali, and salt solution, it will cause corrosion, cause rubber swelling, and produce rubber molecules. Fracture, depolymerization, and decomposition and dissolution of compounding agents lead to a significant decrease in its mechanical strength and physical properties, and the rubber layer gradually becomes sticky, oxidized, hardened, embrittled, cracked, etc., and cracks occur due to the attack of ozone. So that the corrosion completely loses the ability to work
[0004] The rubber gasket of the existing conventional technology uses nitrile rubber as the base, and other materials are added to achieve the purpose of oil resistance, but its high temperature resistance is not strong. In order to improve its high temperature resistance and make the oil resistance and high temperature resistance reach a balance point, now provide A new technical solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Get the following raw materials in parts by weight, 85 parts of methyl vinyl phenyl silicone rubber, 65 parts of nitrile rubber, 30 parts of rubber-plastic alloy, 10 parts of polypropylene resin, 10 parts of thermosetting epoxy resin, dithiotetramethyl autumn 2 parts of lamb, 1 part of dithiodibenzothiazole, 20 parts of high wear-resistant furnace black, 15 parts of dioctyl (butyl) phthalate, N-isopropyl-N?-phenyl terephthalate 3 parts of amine, 10 parts of barium sulfate.

[0016] According to the following steps: first step, rubber preparation: prepare materials according to the above components and parts by weight; then carry out natural rubber mastication; then put the above raw materials into the internal mixer for mixing in turn, mix evenly Glue, glue removal temperature 120°C; press on the open mill, park to cool, then add vulcanizing agent on the open mill and release the tablet, park and cool for more than 8 hours for use;

[0017] The second step, molding: he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a conveyor roller high temperature resistant acid and alkali resistant rubber coated layer which consists of the following components by weight: 70-90 parts of methyl vinyl phenyl silicone rubber, 60-80 parts of nitrile rubber, 25-35 parts of rubber and plastic alloy, 8-12 parts of polypropylene resin, 10-13 parts of thermosetting epoxy resin, 2-3.5 parts of tetramethylthiuramdisufide, 1-1.4 parts of disulfide dibenzothiazole, 20-25 parts of high abrasion furnace black, 8-20 parts of dioctyl phthalate or dibutyl phthalate, 3-4 parts of N-isopropyl-N'-phenyl para-phenylene diamine and 10-20 parts of barium sulfate. Compared with the prior art, the rubber coated layer can keep original physical and mechanical properties for a long time under the action of acid and alkali bath, and has high temperature resistant characteristics.

Description

[0001] technical field [0002] The invention relates to the technical field of conveyors, in particular to a high temperature, acid and alkali resistant rubber coating layer for a conveyor roller. Background technique [0003] The rubber coating layer of the existing ordinary rollers cannot work in chemicals such as acid, alkali, and salt solution. When the rubber coating layer of ordinary rollers is in contact with acid, alkali, and salt solution, it will cause corrosion, cause rubber swelling, and produce rubber molecules. Fracture, depolymerization, and decomposition and dissolution of compounding agents lead to a significant decrease in its mechanical strength and physical properties, and the rubber layer gradually becomes sticky, oxidized, hardened, embrittled, cracked, etc., and cracks occur due to the attack of ozone. So that the corrosion completely loses the ability to work. [0004] The rubber gasket of the existing conventional technology uses nitrile rubber as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/07C08L9/02C08L23/12C08L63/00C08L101/00C08K13/02C08K5/40C08K5/47C08K3/04C08K5/12C08K5/18C08K3/30B29C35/02
Inventor 叶春会王泽平
Owner ANHUI JIAMU RUBBLE & PLASTIC IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products