Cu-containing high-entropy alloy coating with liquid phase separation tissue and preparation method thereof

A high-entropy alloy and liquid phase separation technology, applied in the coating process of metal materials, coatings, etc., can solve the problems of rare high-entropy alloy components, achieve low cost, optimize the preparation process, and achieve significant economic benefits.

Active Publication Date: 2015-09-16
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the reported high-entropy alloy components contain Fe, Co, Ni, Cr, Cu and other main alloying elements. Although most of Cu and other alloying There are many elements in the alloy and the copper content generally does not exceed 35%. The high atomic disorder of the high-entropy alloy limits the separation of the copper-rich liquid phase from

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cu-containing high-entropy alloy coating with liquid phase separation tissue and preparation method thereof
  • Cu-containing high-entropy alloy coating with liquid phase separation tissue and preparation method thereof
  • Cu-containing high-entropy alloy coating with liquid phase separation tissue and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030] Example 1

[0031] A Cu-containing high-entropy alloy coating with a liquid phase separation structure, which is obtained by alloying 5 or more metal or non-metal elements in an equal atomic ratio or close to an equal atomic ratio. In addition, different amounts of Nano Y 2 O 3 , Nano Y 2 O 3 The particle size distribution is between 20-100nm. In this example, 4 kinds of high-entropy alloy powders are prefabricated, which are respectively recorded as 0.5% Y 2 O 3 -AlCoCrCuFeNiSi 0.5 , 1% Y 2 O 3 -CoCrCu 2 FeNi, 2% Y 2 O 3 -AlCoCrCuFeNi and 3% Y 2 O 3 -CoCrCuFeNi, of which 0.5% Y 2 O 3 -AlCoCrCuFeNiSi 0.5 Y in high entropy alloy 2 O 3 The mass fraction of is 0.5%, and the molar ratio of other metal elements is: Al:Co:Cr:Cu:Fe:Ni:Si=1:1:1:1:1:1:0.5; 1%Y 2 O 3 -CoCrCu 2 FeNi high entropy alloy in Y 2 O 3 The mass fraction of 1%, the molar ratio of other metal elements is: Co:Cr:Cu:Fe:Ni=1:1:2:1:1; 2%Y 2 O 3 -AlCoCrCuFeNi high-entropy alloy Y 2 O 3 The mass fraction is 2%, the ...

Example Embodiment

[0035] Example 2

[0036] A Cu-containing high-entropy alloy coating with a liquid phase separation structure, which is obtained by alloying 5 or more metal or non-metal elements in an equal atomic ratio or close to an equal atomic ratio. In addition, different amounts of Nano Y 2 O 3 , Nano Y 2 O 3 The particle size distribution is between 20-100nm. In this example, two kinds of high-entropy alloy powders are prefabricated, which are respectively recorded as 0.5% Y 2 O 3 -CuCo 0.5 Ni 1.2 CrAl 1.5 Fe 1.5 And 2.5% Y 2 O 3 -CuCrCoMoAl 1.5 Ti, where 0.5% Y 2 O 3 -CuCo 0.5 Ni 1.2 CrAl 1.5 Fe 1.5 Y in high entropy alloy 2 O 3 The mass fraction of is 0.5%, and the mole ratio of other metal elements is: Cu:Co:Ni:Cr:Al:Fe=1:0.5:1.2:1:1.5:1.5; 2.5%Y 2 O 3 -CuCrCoMoAl 1.5 Ti high entropy alloy in Y 2 O 3 The mass fraction of is 2.5%, and the molar ratio of other metal elements is: Cu:Cr:Co:Mo:Al:Ti=1:1:1:1:1.5:1; the purity of various metal powders in this embodiment is ≥ 99.5%, the partic...

Example Embodiment

[0040] Example 3

[0041] A Cu-containing high-entropy alloy coating with a liquid phase separation structure, which is obtained by alloying 5 or more metal or non-metal elements in an equal atomic ratio or close to an equal atomic ratio. In addition, different amounts of Nano Y 2 O 3 , Nano Y 2 O 3 The particle size distribution is between 20-100nm. In this example, two kinds of high-entropy alloy powders are prefabricated, which are respectively recorded as 0.8% Y 2 O 3 -CoCrCuFeNiAl 1.2 Ti 0.5 And 1.5% Y 2 O 3 -Al 1.2 CuNi 0.8 CrFe, of which 0.8% Y 2 O 3 -CoCrCuFeNiAl 1.2 Ti 0.5 Y in high entropy alloy 2 O 3 The mass fraction of is 0.8%, and the molar ratio of other metal elements is: Co:Cr:Cu:Fe:Ni:Al:Ti=1:1:1:1:1:1.2:0.5; 1.5%Y 2 O 3 -Al 1.2 CuNi 0.8 CrFe high entropy alloy in Y 2 O 3 The mass fraction is 1.5%, and the molar ratio of other metal elements is: Al:Cu:Ni:Cr:Fe=1.2:1:0.8:1:1; the purity of various metal powders in this embodiment is ≥99.5%, The diameter is 10-100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Crack lengthaaaaaaaaaa
Granularityaaaaaaaaaa
Crack lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Cu-containing high-entropy alloy coating with liquid phase separation tissue and a preparation method thereof, and belongs to the field of alloy material design. According to the invention, a small amount of nano Y2O3 (mass fraction of 0.5-3%) is added to the Cu-containing high-entropy alloy composition, and can promote laser cladding of the Cu-containing high-entropy alloy coating and formation of liquid phase separation tissue. The Cu-containing high-entropy alloy is composed of five or more metallic or non-metallic elements, and the compulsory Cu element accounts for 15-35% of the total moles of the high-entropy alloy composition. The nano Y2O3 has a large surface effect and small size effect, can promote separation of liquid copper from the alloy melt in the laser cladding of Cu-containing high-entropy alloy coating; and a large number of copper-rich particles in dispersed distribution grow in situ on the coating solidified matrix tissue, thus changing the single-phase structure of the coating, and providing a novel method for designing complex phase tissue and expanding capability of the high-entropy alloy by liquid phase separation.

Description

technical field [0001] The invention belongs to the field of alloy material design, and more specifically relates to a Cu-containing high-entropy alloy coating with a liquid phase separation structure and a preparation method thereof. Background technique [0002] Due to its unique high entropy effect, slow diffusion effect, nanophase strengthening and ultra-high lattice distortion, multi-principal high-entropy alloys have many excellent properties such as high hardness, high temperature resistance, and corrosion resistance, and are gradually being favored by alloy materials. designer's attention. The design range of its alloy composition is from 5 to 11 main alloy elements in equimolar ratio or nearly equimolar ratio. Due to its high mixing entropy effect, it can generally avoid a large number of nucleation of complex intermetallic compounds after solidification, and mostly form face-centered cubic (fcc) and body-centered cubic (bcc) single-phase structures dominated by si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C24/10B22F1/00C22C30/02
Inventor 张晖
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap