Preparing method of beryllium oxide base metal ceramic
A beryllium oxide and base metal technology is applied in the field of preparation of beryllium oxide-based cermet materials, which can solve the problems of low heat exchange efficiency and short service period, and achieve the effects of improving thermal conductivity and elongation and improving the preparation process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Further, in the present invention, the preparation method of beryllium oxide-based ceramic powder includes the following steps:
[0026] Step 1. Prepare the blank by using the existing technology, then evenly coat the glaze on the surface of the blank, and then fire it into a fired body at 1250°C;
[0027] Step 2. Crush the fired preform together with zinc oxide into a powder with an average particle size of less than 50μm to obtain ceramic powder, where the mass of zinc oxide added is not higher than 2.5% of the fired body mass fraction .
[0028] The present invention also includes a preparation method of beryllium oxide-based cermet material, including the following steps:
[0029] Step 1. Take the designed amount of beryllium oxide-based metal powder and ceramic powder and place them in a high-speed ball mill for mixing and grinding for 2-4 hours. The speed of the high-speed ball mill is 400 rad / min, and then mix them evenly in a high-speed mixer to obtain a primary mixture...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap