High-structural-strength three-dimensional solid wood composite board and forming method thereof

A high-structure, composite panel technology, which is applied in the jointing of wooden veneers, chemical instruments and methods, and wood layered products, can solve problems such as difficulty in maintaining consistency, inability of panels to bear loads, and inconvenience in practical application, and achieve reduction Thickness, improved load-bearing capacity, and structural stability

Active Publication Date: 2015-09-23
SHENZHEN SONGBOYU TIMBERING
View PDF12 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the key load-bearing capacity of the plate during the rolling process, the thickness of the plate of this technology is relatively high, which is inconvenient for practical application
However, when the thickness of the plate in this technology is low, the increased rolling strength will inevitably cause the plate to be unable to bear the load and crack
At the same time, due to the different degrees of contact between each layer and the external environment during use of multi-layer materials, it is difficult to maintain a consistent state between layers, and the final product is prone to deformation due to uneven force between layers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-structural-strength three-dimensional solid wood composite board and forming method thereof
  • High-structural-strength three-dimensional solid wood composite board and forming method thereof
  • High-structural-strength three-dimensional solid wood composite board and forming method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] The present embodiment provides a kind of three-dimensional solid wood composite panel with high structural strength, such as figure 1 , including a hard base layer 1, and a first capacity layer group 2 and a second capacity layer group 3 arranged on both sides of the base layer; a flexible capacity layer is respectively arranged in the first capacity layer group and the second capacity layer group; It includes a surface layer 4 arranged on the surface of the first capacity layer.

[0044] In this embodiment, the above-mentioned hard base layer is a commercially available Ozon board. The flexible capacity layer is pine wood. Natural wood veneer for the finish.

[0045] Further, the thickness of the surface layer 4 is 1 mm, the thickness of the first capacity layer is 1 mm, the thickness of the second capacity layer group is 1.2 mm, and the thickness of the base layer is 25 mm.

[0046] Further, the surface layer is provided with a decorative groove 41, and the bottom...

Embodiment 2

[0051] Such as figure 2 , the present embodiment provides the preparation method of embodiment 1 high structural strength three-dimensional solid wood composite board, specifically as follows:

[0052] a. Polish the Ozon board, 1, and apply glue on both sides of the Ozon board;

[0053] b. Paste a layer of pine board 2 and pine board 3 on both sides of the European pine board;

[0054] c. coating glue on the surface of one of the pine boards 2;

[0055] d. Paste one deck of natural veneer 4 on the surface of above-mentioned pine board 2;

[0056] e. Heat the above plate to 101°C under 6MP high pressure and keep it for 9 minutes;

[0057] f. Cold pressing the above plate at 5°C for 16 minutes to obtain a semi-finished plate;

[0058] g. Using a mold with embossed lines, press the semi-finished board under a pressure of 13 MP for 5 minutes to obtain the high structural strength three-dimensional solid wood composite board of this embodiment.

Embodiment 3

[0060] The present embodiment provides a kind of three-dimensional solid wood composite panel with high structural strength, such as image 3 , including a hard base 1, and a first capacity layer group 2 and a second capacity layer group 3 arranged on both sides of the base layer; a flexible capacity layer is respectively arranged in the first capacity layer group and the second capacity layer group; It includes a surface layer 4 arranged on the surface of the first capacity layer.

[0061] In this embodiment, the hard base layer is a reconstituted board. The capacity layer is poplar board.

[0062] Further, the thickness of the surface layer is 2 mm, the thickness of the first capacity layer is 5 mm, the thickness of the second capacity layer group is 5 mm, and the thickness of the base layer is 31 mm.

[0063] The surface layer is provided with a decorative groove 41, and the bottom of the decorative groove is embedded in the first capacity layer group.

[0064] The ratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
angleaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-structural-strength three-dimensional solid wood composite board which comprises a hard base layer and further comprises a first capacity layer group, a second capacity layer group and a surface layer, wherein the first capacity layer group and the second capacity layer group are arranged on the two sides of the base layer, wherein each of the first capacity layer group and the second capacity layer group is provided with at least one flexible capacity layer; the surface layer is arranged on the surface of the first capacity layer; a decoration groove is formed in the surface layer; and the bottom of the decoration groove is embedded into the first capacity layer group. The hard base layer can provide enough mechanical strength for the whole board and support the capacity layers and the surface layer in the board, so as to prevent the board from deforming in the process of making the decoration groove under high pressure. The solid wood composite board provided by the invention has a brand-new structure different from that of a conventional board, has the characteristics of stereoscopic vision, high mechanical strength and long service life, further has the advantages of low formaldehyde release amount and environment friendliness in use and can be widely applied to the fields of home decoration, artwork processing, commercial place decoration and municipal construction.

Description

technical field [0001] The invention relates to the technical field of decorative boards, in particular to a three-dimensional solid wood composite board with high structural strength and a forming method thereof. Background technique [0002] There are two types of furniture decoration panels currently on the market, one is a traditional flat panel and the other is a three-dimensional panel. The traditional flat decoration has poor visual effect and no three-dimensional effect, which cannot meet the needs of the market. The new generation of decorative panels with 3D effect has a strong three-dimensional effect and is more and more popular among consumers. In the prior art, it is common to use special equipment to mill or plan out a three-dimensional shape on the surface of the substrate, and then spray glue and then absorb plastic or stick a film to finally obtain a decorative plate with a three-dimensional texture on the surface. Although this manufacturing process can f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/04B32B21/13B32B7/12B32B3/30B32B37/10B32B37/12
CPCB27D1/04B27D1/08B32B3/28B32B7/12B32B21/042B32B37/06B32B37/10B32B37/12B32B2250/04B32B2307/50B32B2307/734B32B2451/00
Inventor 詹雄光颜宝娟罗俊光黄远林
Owner SHENZHEN SONGBOYU TIMBERING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap