Novel fire resisting material

A refractory material, a new type of technology, applied in the field of high temperature resistance of pipelines, can solve the problems of short service life and so on

Inactive Publication Date: 2015-09-30
SINOMA CHENGDU ENERGY TECH
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In this field, there are still few refractory materials under alkaline environment, and the existing refractory materials under alkaline environment basically do not have long service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A new type of refractory material is characterized by comprising the following components: quartz sand, phenolic resin, magnesium silicate, sodium silicate, silicon carbide, magnesium oxide and calcium oxide.

[0033] Described a kind of novel refractory material is characterized in that: a kind of novel refractory material contains following components, and the parts by weight of each component are:

[0034] Quartz sand 55-150 parts

[0035] 30-50 parts of phenolic resin

[0036] Magnesium silicate 45-55 parts

[0037] Sodium silicate 60-80 parts

[0038] Silicon carbide 55-65 parts

[0039] Magnesium oxide 110-150 parts

[0040] Calcium oxide 110-150 parts.

Embodiment 2

[0042] Described a kind of novel refractory material is characterized in that: a kind of novel refractory material contains following components, and the parts by weight of each component are:

[0043] Quartz sand 55 parts

[0044] 30 parts of phenolic resin

[0045] Magnesium silicate 45 parts

[0046] Sodium silicate 60-parts

[0047] Silicon carbide 55 parts

[0048] Magnesium oxide 110 parts

[0049] Calcium oxide 110 parts.

Embodiment 3

[0051] Described a kind of novel refractory material, it is characterized in that: a kind of novel refractory material contains following components, and the parts by weight of each component are:

[0052] Quartz sand 150 parts

[0053] 50 parts of phenolic resin

[0054]Magnesium silicate 55 parts

[0055] Sodium silicate 80 parts

[0056] Silicon carbide 65 parts

[0057] Magnesium oxide 150 parts

[0058] 150 parts of calcium oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of pipeline high-temperature resistance and relates to the manufacturing of a novel fire resisting material, in particular to the novel fire resisting material. The novel fire resisting material is characterized by comprising the following components including quartz sand, phenolic resin, magnesium silicate, sodium silicate, silicon carbide, magnesium oxide and calcium oxide.

Description

technical field [0001] The invention belongs to the technical field of pipeline high temperature resistance, and relates to the manufacture of a novel refractory material, in particular to a novel refractory material. Background technique [0002] A class of inorganic non-metallic materials with a refractoriness not lower than 1599°C. Refractoriness refers to the Celsius temperature at which a refractory conical sample can resist high temperature without softening and melting without load. However, it is not possible to fully describe refractory materials only by the definition of refractoriness, and 1599°C is not absolute. It is now defined as a material whose physical and chemical properties allow it to be used in a high temperature environment is called a refractory material. Refractory materials are widely used in metallurgy, chemical industry, petroleum, machinery manufacturing, silicate, power and other industrial fields, and are used in the largest amount in the met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 付伟峰窦涛
Owner SINOMA CHENGDU ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap