Interface metallurgical bonding aluminum foam slab and preparation method thereof
A foamed aluminum plate and interface metallurgy technology, applied in chemical instruments and methods, metal layered products, lamination, etc., can solve problems such as large influence, complex process equipment, adhesive deactivation and aging, and improve stability , The effect of simple process equipment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] The density prepared by the melt foaming method is 0.15g / cm 3 , 5mm thickness of the foam aluminum plate with uniform porosity, remove the burrs with steel brushes, brushes, etc., and blow the surface of the foam aluminum plate with compressed air with a pressure of not less than 0.5MPa. Place the surface-treated foam aluminum plate in the interface heating furnace, and the surface of the foam aluminum core sheet to be treated is heated on the interface heating platform of the interface heating furnace. The interface heating platform is a high temperature resistant steel plate, and the surface of the high temperature resistant steel plate is brushed. Apply zinc oxide paint, heat the temperature to 1150℃, place the limit block on the heated foam aluminum core sheet to control the thickness of the skin, and apply a static pressure of 1.0Mpa to the limit block uniformly through the pressure machine. The surface of the foamed aluminum core sheet forms a skin...
Example Embodiment
[0024] Example 2
[0025] The density prepared by the melt foaming method is 1.0g / cm 3 , The thickness of 380mm foam aluminum sheet with uniform porosity, use steel brush, brush, etc. to remove burrs, and use compressed air with a pressure of not less than 0.5MPa to blow the surface of the foam aluminum sheet. Place the surface-treated foam aluminum plate in the interface heating furnace, and the surface of the foam aluminum core sheet to be treated is heated on the interface heating platform of the interface heating furnace. The interface heating platform is a high temperature resistant steel plate, and the surface of the high temperature resistant steel plate is brushed. Apply zinc oxide paint, heat the temperature to 1250℃, place the limit block on the heated foam aluminum core plate to control the thickness of the skin, and apply a static pressure of 5.0Mpa to the limit block uniformly through the pressure machine. One surface of the foamed aluminum core sheet forms a skin la...
Example Embodiment
[0026] Example 3
[0027] The density prepared by the melt foaming method is 0.55g / cm 3 , 150mm thick foam aluminum sheet with uniform porosity, use steel brushes, brushes, etc. to remove burrs, and use compressed air with a pressure of not less than 0.5MPa to blow the surface of the foam aluminum sheet. Place the surface-treated foam aluminum plate in the interface heating furnace, and the surface of the foam aluminum core sheet to be treated is heated on the interface heating platform of the interface heating furnace. The interface heating platform is a high temperature resistant steel plate, and the surface of the high temperature resistant steel plate is brushed. Apply zinc oxide paint, heat the temperature to 1200℃, place the limit block on the heated foam aluminum core sheet to control the thickness of the skin, and apply a static pressure of 3.5Mpa to the limit block uniformly by a pressure machine. One surface of the foamed aluminum core sheet forms a skin layer integrate...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap