Liquid ethylene propylene diene monomer rubber asphalt waterproofing paint and preparation method thereof

A technology for EPDM rubber and asphalt waterproof coatings, which is applied in the direction of asphalt coatings, recycled rubber coatings, coatings, etc., and can solve the problem of inability to maintain the original performance of waterproof materials, poor self-healing performance and creep performance, and limited service life and other problems, to achieve the effect of solving the cracking problem of the waterproof layer, good self-healing performance and creep performance

Inactive Publication Date: 2015-10-14
阿尔法新材料江苏有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The waterproof materials in the prior art include modified asphalt waterproof coatings. The use of various polymer modified asphalt can greatly improve the performance of asphalt substrates, but its shortcomings are also obvious: poor self-healing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A liquid EPDM bituminous waterproof coating, the formula includes:

[0013] 42 parts of asphalt, 13 parts of liquid EPDM rubber, 9.4 parts of SBS, 8.6 parts of reclaimed rubber powder, 9.4 parts of polybutene, 20.9 parts of naphthenic oil, and 11.7 parts of petroleum resin.

[0014] The preparation method of the liquid EPDM bituminous waterproof coating comprises: first, heating the asphalt of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at -180°C for 1-2 hours; finally, cool down to 160°C, and add reclaimed rubber powder according to the weight of the formula, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

Embodiment 2

[0016] A liquid EPDM bituminous waterproof coating, the formula includes:

[0017] 32 parts of asphalt, 14 parts of liquid EPDM rubber, 9 parts of SBS, 10 parts of reclaimed rubber powder, 9 parts of polybutene, 22 parts of naphthenic oil, and 12 parts of petroleum resin.

[0018] The preparation method of the liquid EPDM bituminous waterproof coating comprises: first, heating the asphalt of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at -180°C for 1-2 hours; finally, cool down to 160°C, and add reclaimed rubber powder according to the weight of the formula, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

Embodiment 3

[0020] A liquid EPDM bituminous waterproof coating, the formula includes:

[0021] 48 parts of asphalt, 11 parts of liquid EPDM rubber, 8.1 parts of SBS, 9 parts of reclaimed rubber powder, 9.8 parts of polybutene, 25 parts of naphthenic oil, and 10.9 parts of petroleum resin.

[0022] The preparation method of the liquid EPDM bituminous waterproof coating comprises: first, heating the asphalt of formula weight to 130-180 DEG C; then, adding modifier, polybutene and tackifier of formula weight, and heating Stir at -180°C for 1-2 hours; finally, cool down to 160°C, and add reclaimed rubber powder according to the weight of the formula, stir for 1-1.5 hours until it is uniform and free of particles, and then discharged until it is in a molten state.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a liquid ethylene propylene diene monomer rubber asphalt waterproofing paint and a preparation method thereof. The used additives are long-chain low-molecular-weight additives, can enable the asphalt to be mixed and dissolved with various high-polymer materials to form a stable combination in the production process, and display the respective characteristics in the most stable state in the application process, thereby achieving the goal of never curing. The preparation method comprises the following steps: heating asphalt according to the formula weight to 130-180 DEG C, adding liquid ethylene propylene diene monomer rubber, SBS (styrene-butadiene-styrene), naphthenic oil and a petroleum resin into the asphalt according to the formula weight, stirring at 175-180 DEG C for 1-2 hours, cooling to 160 DEG C, adding regenerated rubber powder according to the formula weight, uniformly stirring for 1-1.5 hours to the granule-free molten state, and discharging. The liquid ethylene propylene diene monomer rubber asphalt waterproofing paint has favorable self-recovery property and creep property, and can effectively solve the problem of waterproofing layer cracking caused by deformation of the building basal plane.

Description

technical field [0001] The invention relates to a liquid EPDM asphalt waterproof coating and a preparation method thereof. Background technique [0002] The waterproof materials in the prior art include modified asphalt waterproof coatings. The use of various polymer modified asphalt can greatly improve the performance of asphalt substrates, but its shortcomings are also obvious: poor self-healing performance and creep performance. The deformation of the base surface of the building is likely to cause cracking of the waterproof layer, so the original performance of the waterproof material cannot be maintained, which greatly limits the service life. Contents of the invention [0003] In view of this, the main purpose of the present invention is to provide a kind of liquid ternary vinyl rubber asphalt waterproof coating and preparation method thereof, the additive used in it is long chain, low molecular weight, can make asphalt and various macromolecule The materials are in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D195/00C09D153/02C09D123/16C09D157/02C09D117/00C09D123/20C09D7/12
Inventor 潘冰关兴霞
Owner 阿尔法新材料江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap