Electric conduction compound ABS/PLA material for 3D printing wires as well as preparation method and application of electric conduction compound ABS/PLA material

A composite material and 3D printing technology, applied in the direction of additive processing, etc., can solve the problems of layering, high content of conductive filler, low precision, etc., and achieve the effect of low volume resistivity, good interlayer bonding, and enhanced toughness

Active Publication Date: 2015-10-28
广州润锋科技股份有限公司
View PDF8 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Therefore, in view of the above technical problems, the present invention seeks to provide a highly conductive material strip suitable for double-head 3D printing technology, which can be combined with non-conductive ABS materials and applied to printing electrical componen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric conduction compound ABS/PLA material for 3D printing wires as well as preparation method and application of electric conduction compound ABS/PLA material
  • Electric conduction compound ABS/PLA material for 3D printing wires as well as preparation method and application of electric conduction compound ABS/PLA material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] 1. According to the ratio of raw materials in Example 1 in Table 1, weigh CNT and GNP and place them in a beaker, add chloroform, stir at high speed, and ultrasonic (power 120W) for 8 hours, then add PLA, continue ultrasonic and stir for 4 hour, after the mixture was air-dried, it was placed in an oven at 120 degrees centigrade for 4 hours to obtain a PLA / carbon material masterbatch.

[0061] 2. Add pure PLA, PLA / carbon material masterbatch and metal nickel powder into an internal mixer and melt blend at 185 degrees Celsius to prepare PLA / Ni / carbon material conductive masterbatch.

[0062] The mass of CNT and GNP in step 1 accounts for 15-25% of the PLA / carbon material masterbatch.

[0063] The mass of metallic nickel powder in step 2 accounts for 15-25% of the PLA / Ni / carbon material conductive masterbatch.

[0064] 3. PLA / Ni / carbon material conductive masterbatch and bulk method ABS (Dow MAGNUM 213), emulsion method ABS (Taiwan Chimei 747), styrene-acrylonitrile-glyci...

Embodiment 2

[0067] The preparation method is the same as in Example 1, and the raw material of the emulsion method ABS is Taiwan Chimei 757, and the composition ratio of the raw materials is shown in Table 1.

Embodiment 3

[0069] The preparation method is the same as that in Example 1, and the raw material of the emulsion method ABS is Taiwan Chimei 756, and the composition ratio of the raw materials is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an electric conduction compound ABS/PLA material for 3D printing wires. The electric conduction compound ABS/PLA material is prepared from the following raw materials in percentage by weight: 15-30% of a synthetized material ABS by using a bulk method, 15-30% of a synthetized material ABS by an emulsion method, 1-10% of copolymers of styrene -acrylonitrile -2-methylpropenoic acid glycidyl ester, 0.01-0.05% of triphenylphosphonium bromide, 5-15% of metallic nickel powder , 30-50% of polylactic acid , 1-5% of walled carbon nanotubes and 1-5% of graphene microchips. According to the electric conduction compound ABS/PLA material disclosed by the invention, the nickel powder, the graphene microchips and the carbon nano tubes are optimized and collocated, so that the requirements for electrical conductivity by using lower volume resistivity under the low content of an electric conduction additive are met, the ABS material mixed in different particle diameters enables the particle diameters in the compound material to present bimodal distribution, and the toughness is enhanced; the consistency and the cocontinuity of ABS and PLA are good, so that the electric conduction compound ABS/PLA material is particularly suitable for strip-shaped high electric conduction materials required by 3D printing.

Description

technical field [0001] The invention belongs to the technical field of conductive materials for 3D printing wires, and more specifically relates to a conductive ABS / PLA composite material for 3D printing wires and its preparation method and application. Background technique [0002] At present, the ABS strips for 3D printing sold in China include imported STRATASYS P400 ABS, domestic montmorillonite modified ABS (CN104672755A), glass fiber reinforced ABS (CN104559034A), polycarbonate modified ABS (CN104559023A), rubber particle double ABS with peak distribution (CN104072935A, CN103980429A), carbon black conductive modified ABS (CN103788565A), among them, the conductive ABS strip for 3D printing has the carbon black conductive modified ABS disclosed in CN103788565A, but the carbon black conductive content reaches 35 parts by mass Above, the high filler content seriously affects the printing effect of ABS strips (low precision and delamination). And the volume resistivity of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L55/02C08L67/04C08L25/14C08K13/04C08K7/24C08K3/04C08K3/08C08K5/50B29C47/92B33Y70/00B29C48/92
Inventor 林志丹贺子芹曹琳邓淑玲张光正
Owner 广州润锋科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap