Reinforced toughened plant fiber composite film and preparation method thereof

A composite film and plant fiber technology, applied in the direction of coating, etc., can solve the problems of poor strength and tensile properties of plant fiber films, and achieve the effects of low cost, simple preparation method, and universal raw materials

Inactive Publication Date: 2015-11-25
SUZHOU FAST INFORMATION TECH CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved is: in order to solve the problem of poor strength and tensile properties of traditional plant fiber films, to provide a reinforced and toughened plant fiber composite film and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A reinforced and toughened plant fiber composite film, which is made of the following raw materials in parts by weight: 20 parts of straw extract fiber, 15 parts of loofah fiber, 20 parts of ramie fiber, 10 parts of corn starch, shell 12 parts polysaccharide, 6 parts molecular sieve, 5 parts polyvinyl alcohol, 5 parts polycaprolactone, 2 parts potassium tripolyphosphate, 2 parts diethyl phthalate, 1 part triethanolamine stearate quaternary ammonium salt , 2 parts of reinforcing agent, 5 parts of transparent agent and 6 parts of binder.

[0019] The enhancer is ethylene glycol sebacate. The transparent agent is chlorinated paraffin. The binder is acrylate.

[0020] The preparation method of described reinforced and toughened type plant fiber composite film, comprises the following steps:

[0021] Step 1: Extract straw fiber, loofah fiber, ramie fiber, corn starch, chitosan, molecular sieve, polyvinyl alcohol, polycaprolactone, potassium tripolyphosphate, diethyl phtha...

Embodiment 2

[0025] A reinforced and toughened plant fiber composite film, which is made of the following raw materials in parts by weight: 45 parts of straw extract fiber, 35 parts of luffa fiber, 40 parts of ramie fiber, 30 parts of cornstarch, shell 25 parts polysaccharide, 17 parts molecular sieve, 20 parts polyvinyl alcohol, 15 parts polycaprolactone, 6 parts potassium tripolyphosphate, 7 parts diethyl phthalate, 5 parts triethanolamine stearate quaternary ammonium salt , 8 parts of reinforcing agent, 25 parts of transparent agent and 20 parts of binder.

[0026] The enhancer is dodecyl alcohol ester. The transparent agent is liquid paraffin. The binder is phenolic resin.

[0027] The preparation method of described reinforced and toughened type plant fiber composite film, comprises the following steps:

[0028] Step 1: Extract straw fiber, loofah fiber, ramie fiber, corn starch, chitosan, molecular sieve, polyvinyl alcohol, polycaprolactone, potassium tripolyphosphate, diethyl pht...

Embodiment 3

[0032] A reinforced and toughened plant fiber composite film, which is made of the following raw materials in parts by weight: 32 parts of straw extract fiber, 25 parts of luffa fiber, 30 parts of ramie fiber, 20 parts of cornstarch, shell 18 parts polysaccharide, 11 parts molecular sieve, 12 parts polyvinyl alcohol, 10 parts polycaprolactone, 4 parts potassium tripolyphosphate, 4 parts diethyl phthalate, 3 parts triethanolamine stearate quaternary ammonium salt , 5 parts of reinforcing agent, 15 parts of transparent agent and 13 parts of adhesive.

[0033] The enhancer is dodecyl alcohol ester. The transparent agent is chlorinated paraffin. The binder is phenolic resin.

[0034] The preparation method of described reinforced and toughened type plant fiber composite film, comprises the following steps:

[0035] Step 1: Extract straw fiber, loofah fiber, ramie fiber, corn starch, chitosan, molecular sieve, polyvinyl alcohol, polycaprolactone, potassium tripolyphosphate, diet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a reinforced toughened plant fiber composite film and a preparation method thereof. The composite film is prepared from the following raw materials in parts by weight: 20-45 parts of straw extract fiber, 15-35 parts of towel gourd fiber, 20-40 parts of ramee, 10-30 parts of corn starch, 12-25 parts of chitosan, 6-17 parts of molecular sieve, 5-20 parts of polyvinyl alcohol, 5-15 parts of polycaprolactone, 2-6 parts of potassium tripolyphosphate, 2-7 parts of diethyl phthalate 1-5 parts of triethanolamine stearate quaternary ammonium salt, 2-8 parts of reinforcer, 5-25 parts of clearing agent and 6-20 parts of adhesive. The invention also discloses a preparation method of the composite film. The tensile strength of the plant fiber composite film is 16-25 MPa, the tearing strength is 75-105 MPa, and the plant fiber composite film has favorable stretching resistance and tear resistance. Besides, the preparation method is simple, has the advantages of accessible and common raw materials and lower cost, and is suitable for wide popularization and further expanded application.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a reinforced and toughened plant fiber composite film and a preparation method thereof. Background technique [0002] Plant fiber film is a kind of film with good biodegradability prepared by using plant fiber such as wood, cotton, hemp and other natural raw materials, and crop waste such as straw, straw, bagasse, etc. as raw materials. Due to the wide source and low price of plant fiber, and its excellent degradability, it can improve the problem of film pollution in today's environment. Therefore, fiber film has attracted much attention. However, just because the traditional plant fiber film is mainly made of some natural raw materials or crop waste, its strength and tensile properties are poor, and it is easy to be torn and deformed under the action of external force. Moreover, the traditional plant fiber film has poor water resistance, and its mechanical properties are gre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J7/04C08J7/16C08L97/02C08L3/02C08L5/08C08L29/04C08L67/04C08L61/06C08L89/00C08K13/02C08K3/32C08K5/12C08K5/19
Inventor 彭孝茹
Owner SUZHOU FAST INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap