A kind of acid and alkali resistant insulating rubber material and preparation method thereof

An insulating rubber, acid and alkali resistance technology, applied in the field of rubber materials, can solve the problems of depolymerization, high price, rubber swelling, etc., and achieve the effect of simple preparation process and easy operation

Active Publication Date: 2016-12-07
三丰盈新材料(江苏)有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when ordinary rubber materials encounter working environments with acid-base or salt solutions, they are often corroded due to frequent contact with chemicals such as acid-base or salt, resulting in rubber swelling, rubber molecule breakage, and depolymerization, which in turn increases its mechanical strength. and physical properties are significantly reduced, or even completely lose their due effect, which will directly affect production safety and personal safety; in addition, in some specific occasions, the insulating properties of rubber are also a limiting factor for rubber applications
In the prior art, although the acid and alkali resistance of nitrile rubber and fluorine rubber are relatively strong, the price is relatively expensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Add 65 parts of reclaimed rubber and 20 parts of fluorine rubber to an internal mixer and masticate at a temperature of 60°C for 10 minutes to obtain mixture A, which is ready for use;

[0030] (2) Mix 4 parts of magnesium oxide, 2 parts of zinc oxide, 25 parts of nano calcium silicate, 0.2 parts of vanadium acetylacetonate, 8 parts of 2-dibenzofuranol, 4 parts of 4-bromo-2-furan valeraldehyde, and furfuryl alcohol Put 18 parts of resin and 8 parts of polyimide fiber into a reaction kettle at a temperature of 120°C and stir evenly to obtain mixture B; wherein, the rotation speed is 250r / min and the time is 30min;

[0031] (3) Mix the mixture A described in step (1) and the mixture B described in step (2) to obtain mixture C; the mixing speed is 35 rpm, the filling factor is 0.45, the feeding temperature is 55°C, and the discharge temperature It is 110℃, and the time is 5min;

[0032] (4) The mixture C described in step (3) is extruded using a twin-screw extruder at a spee...

Embodiment 2

[0034] (1) Put 80 parts of reclaimed rubber and 50 parts of fluorine rubber into an internal mixer and masticate at a temperature of 65°C for 15 minutes to obtain mixture A, which is ready for use;

[0035] (2) Combine 9 parts of magnesium oxide, 6 parts of zinc oxide, 40 parts of nano calcium silicate, 0.8 parts of acetylacetone, 15 parts of 2-dibenzofuranol, 12 parts of 4-bromo-2-furan valeraldehyde, and furfuryl alcohol resin 30 parts and 15 parts of polyimide fiber are put into a reaction kettle at 170°C and mechanically stirred to obtain mixture B; wherein, the speed is 400r / min and the time is 60min;

[0036] (3) Mix the mixture A described in step (1) and the mixture B described in step (2) to obtain mixture C; the mixing speed is 45 rpm, the filling factor is 0.6, the feeding temperature is 75 °C, and the discharge temperature It is 120℃, and the time is 12min;

[0037] (4) The mixture C described in step (3) is extruded using a twin-screw extruder at a speed of 80 rpm at a ...

Embodiment 3

[0039] (1) Add 70 parts of reclaimed rubber and 30 parts of fluorine rubber to an internal mixer and masticate for 15 minutes at a temperature of 65°C to obtain mixture A, which is ready for use

[0040] (2) Mix 5 parts of magnesium oxide, 3 parts of zinc oxide, 30 parts of nano calcium silicate, 0.4 parts of triphenylphosphine, 10 parts of 2-dibenzofuranol, 7 parts of 4-bromo-2-furan valeraldehyde, 20 parts of furfuryl alcohol resin and 10 parts of polyimide fiber are placed in a reaction kettle at a temperature of 150°C and mechanically stirred to obtain mixture B; wherein, the speed is 350r / min and the time is 40min;

[0041] (3) Mix the mixture A described in step (1) and the mixture B described in step (2) to obtain mixture C; the mixing speed is 40 rpm, the filling factor is 0.5, the feeding temperature is 60°C, and the discharge temperature It is 110℃, and the time is 8min;

[0042] (4) The mixture C described in step (3) is extruded with a twin-screw extruder at a speed of 7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an acid and alkali resistant insulating rubber material, which comprises 65-80 parts of reclaimed rubber, 20-50 parts of fluorine rubber, 4-9 parts of magnesium oxide, 2-6 parts of zinc oxide, and 25-40 parts of nano-calcium silicate , 0.2-0.8 parts of accelerator, 8-15 parts of 2-dibenzofuran alcohol, 4-12 parts of 4-bromo-2-furan valeraldehyde, 18-30 parts of furfuryl alcohol resin, 8-15 parts of polyimide fiber . The preparation process is: adding reclaimed rubber and fluorine rubber into the internal mixer for mastication; adding magnesium oxide, zinc oxide, nano-calcium silicate, accelerator, 2-dibenzofuran alcohol, 4-bromo-2-furalvaleraldehyde , furfuryl alcohol resin and polyimide fibers are placed in a reaction kettle with a temperature of 120-170°C and mechanically stirred; mixture A and mixture B are mixed to obtain mixture C; mixture C can be obtained after extrusion treatment and natural cooling The above-mentioned rubber material has strong acid and alkali resistance and good insulation performance.

Description

technical field [0001] The invention belongs to the field of rubber materials, and in particular relates to an acid and alkali resistant insulating rubber material and a preparation method thereof. Background technique [0002] At present, rubber products are used in all aspects of social life, such as various rubber production equipment or rubber parts in heavy industries such as mining, transportation, construction, machinery, electronics, and emerging industries. However, when ordinary rubber materials encounter working environments with acid-base or salt solutions, they are often corroded due to frequent contact with chemicals such as acid-base or salt, resulting in rubber swelling, rubber molecule breakage, and depolymerization, which in turn increases its mechanical strength. And physical properties are significantly reduced, or even completely lose their due effect, which will directly affect production safety and personal safety; in addition, in some specific occasio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L17/00C08L27/12C08L79/08C08L71/14C08K13/02C08K3/22C08K3/34C08K5/1535
Inventor 林文全
Owner 三丰盈新材料(江苏)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap