Bamboo fiber and fibrilia fiber blending cloth

A bamboo fiber and hemp fiber technology, applied in the field of bamboo fiber and hemp fiber blended fabrics, can solve the problems of low added value, single function and low grade, and achieve the effects of novel functional design, uniform dyeing and high added value.

Inactive Publication Date: 2015-12-09
JIESHOU SHUANGXIN TEXTILE
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional fabrics have single functions, low grades, poor comfort, and low added value, which cannot meet people's needs for clothing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo fiber and fibrilia fiber blending cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of bamboo fiber and hemp fiber blended fabric is obtained by blending raw materials in the following weight ratios:

[0031] Bamboo fiber 90%

[0032] Hemp fiber 3%

[0033] Flax fiber 2%

[0034] Ramie fiber 2%

[0035] Jute fiber 1%

[0036] Apocynum fiber 2%.

[0037] A preparation method of bamboo fiber and hemp fiber blended cloth, comprising the steps of:

[0038] (1) blending bamboo fiber, hemp fiber, flax fiber, ramie fiber, jute fiber and apocynum fiber according to the ratio in the formula to obtain a blended product;

[0039] (2) Dissolve chitosan in 0.8% acetic acid solution at a concentration of 0.5%, sonicate until completely dissolved without air bubbles, soak the blended product in the chitosan solution for 15 minutes, take it out and dry it;

[0040] (3) Immerse the blended fabric in the compound enzyme preparation, the dosage is 0.8% owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep ...

Embodiment 2

[0049] A kind of bamboo fiber and hemp fiber blended fabric is obtained by blending raw materials in the following weight ratios:

[0050] Bamboo fiber 90%

[0051] Hemp fiber 3%

[0052] Flax fiber 2%

[0053] Ramie fiber 2%

[0054] Jute fiber 1%

[0055] Apocynum fiber 2%.

[0056] A preparation method of bamboo fiber and hemp fiber blended cloth, comprising the steps of:

[0057] (1) blending bamboo fiber, hemp fiber, flax fiber, ramie fiber, jute fiber and apocynum fiber according to the ratio in the formula to obtain a blended product;

[0058] (2) Dissolve chitosan in 0.8% acetic acid solution at a concentration of 0.5%, sonicate until completely dissolved without air bubbles, soak the blended product in the chitosan solution for 17 minutes, take it out and dry it;

[0059] (3) Immerse the blended fabric in the compound enzyme preparation, the dosage is 1% owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep wa...

Embodiment 3

[0068] A kind of bamboo fiber and hemp fiber blended fabric is obtained by blending raw materials in the following weight ratios:

[0069] Bamboo fiber 90%

[0070] Hemp fiber 3%

[0071] Flax fiber 2%

[0072] Ramie fiber 2%

[0073] Jute fiber 1%

[0074] Apocynum fiber 2%.

[0075] A preparation method of bamboo fiber and hemp fiber blended cloth, comprising the steps of:

[0076] (1) blending bamboo fiber, hemp fiber, flax fiber, ramie fiber, jute fiber and apocynum fiber according to the ratio in the formula to obtain a blended product;

[0077] (2) Dissolve chitosan in 0.8% acetic acid solution at a concentration of 0.5%, sonicate until completely dissolved without air bubbles, soak the blended product in the chitosan solution for 20 minutes, take it out and dry it;

[0078] (3) Immerse the blended fabric in the compound enzyme preparation, the dosage is 1.2%owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bamboo fiber and fibrilia fiber blending cloth formed by raw material according to a weight ratio of bamboo fibers taking up of 90%, hemp fibers of 3%, flax fibers of 25%, ramie fibers of 2%, jute fibers of 1% and apocynum venetum fibers of 2%. The bamboo fiber and fibrilia fiber blending cloth has great product bacteria-resisting performance, protects skin and is characterized by uvioresistant performance, wear resistance, smoothness, a moisture permeability and shrink resistance; natural finishing agent chitosan is employed in the post-processing phase for a product to further enhance cloth bacteria resisting effect; all natural plant dye-fixing agents and coloring agents are employed during the dying process; even dying, simple technology and unfading color can be achieved; no harm is caused to skin; the whole manufacturing process employs natural material during the whole manufacturing process of the blending bamboo fiber cloth, so the cloth is environment-friendly and safe and requires low cost; the cloth functions and design are novel, high-end, possesses great product comfortableness and high additional value.

Description

technical field [0001] The invention relates to a cloth, in particular to a bamboo fiber and hemp fiber blended cloth. Background technique [0002] In recent years, with the continuous development of textile technology, people's requirements for fabrics such as clothing and bedding have changed from durable and strong to beautiful, comfortable and diversified, while pursuing personalized and high-grade products. However, traditional fabrics have single functions, low grades, poor comfort, and low added value, which cannot meet people's needs for clothing. [0003] As a kind of cellulose fiber, bamboo fiber is a natural high polymer processed from the well-known bamboo. Because of its special macromolecular structure, bamboo fiber has good health functions such as inhibiting bacterial growth and absorbing odors. It is also moisture-absorbing, breathable, and biodegradable. It is known as the green fiber of the new century. [0004] Lyocell bamboo fiber, also known as solve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/00D02G3/04
Inventor 杨文超
Owner JIESHOU SHUANGXIN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com