Outdoor power distribution box with transparent outer box body and manufacturing method of outdoor power distribution box

A manufacturing method and technology of distribution boxes, applied in electrical components, substation/switch layout details, optics, etc., can solve problems such as potential safety hazards

Inactive Publication Date: 2015-12-30
杨超坤
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing distribution boxes are generally made of opaque materials, and operators need to open them to check and check their internal conditions, so there are certain potential safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Outdoor power distribution box with transparent outer box body and manufacturing method of outdoor power distribution box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] The electrical box outer box part 10 , the electrochromic device 20 and the regulator 30 are assembled.

[0068] Making the electrochromic device 20 includes:

[0069] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0070] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 320nm;

[0071] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 220nm; W film is used as WO 3 a growth source for the nanowires;

[0072] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtai...

Embodiment 2

[0087] The electrical box outer box part 10 , the electrochromic device 20 and the regulator 30 are assembled.

[0088] Making the electrochromic device 20 includes:

[0089] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0090] a. Magnetron sputtering fluorine-doped tin oxide (FTO) film 2 on the surface of tempered glass 1 with a specific size, with a thickness of about 360nm;

[0091] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 200nm; W film is used as WO 3 a growth source for the nanowires;

[0092] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtained ...

Embodiment 3

[0107] The electrical box outer box part 10 , the electrochromic device 20 and the regulator 30 are assembled.

[0108] Making the electrochromic device 20 includes:

[0109] (1) WO 3 Nano film 5 material electrochromic electrode preparation:

[0110] a. Magnetron sputtering a fluorine-doped tin oxide (FTO) film on the surface of tempered glass 1 with a specific size, with a thickness of about 340nm;

[0111] b. Perform high-temperature annealing treatment on it to obtain FTO conductive glass with higher strength, then ultrasonically clean the FTO conductive glass for 15 minutes in the order of ultrapure water, acetone, and ethanol, and dry it for later use; then, use magnetron sputtering method Coating W film on FTO glass with a thickness of 210nm; W film is used as WO 3 a growth source for the nanowires;

[0112] c. Prepare a 0.2mol / L sodium tungstate aqueous solution, then add 3mol / L hydrochloric acid dropwise until no precipitation occurs, and then dissolve the obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an outdoor power distribution box with a transparent outer box body and a manufacturing method of the outdoor power distribution box. The structure and manufacturing process of an electrochromic device are both improved so that the electrochromic device can have the self-power-supply characteristic; the electrochromic device can be controlled through solar power generation, and then transparency of the outer box body of the power distribution box is controlled; the manufactured electrochromic device has the advantages of being short in response time, extremely high in solar energy and electric energy conversion efficiency, prolonged in service life and good in cold resistance, and the method is simple, easy to operate and beneficial to industrialized production.

Description

technical field [0001] The invention belongs to the field of electric engineering, and more specifically relates to an outdoor distribution box with a transparent outer box and a manufacturing method thereof. Background technique [0002] Power distribution box is assembled in closed or semiclosed metal cabinet by switch, measuring instrument, protective device and auxiliary equipment according to electrical wiring requirement. Its purpose is to distribute electric energy reasonably, facilitate the opening and closing operation of the circuit, and have a high safety level. [0003] However, the existing distribution boxes are generally made of opaque materials, and operators need to open them to check and view their internal conditions, so there are certain potential safety hazards. Contents of the invention [0004] In view of the problems existing in the background technology, the present invention provides an outdoor distribution box with a transparent outer box and a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H02B1/46G02F1/155G02F1/15
Inventor 杨超坤
Owner 杨超坤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products