A waterproof membrane and PVC resin technology, applied in the field of building materials, can solve the problems of PVC membrane cracks, waterproof failure, plasticizer volatilization, migration, etc., and achieve low production costs, good aging resistance, and good heat resistance sexual effect

Inactive Publication Date: 2016-01-13
YUNNAN YUANAN WATERPROOF TECH CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the waterproof coiled material used for single-layer roofing is an exposed PVC waterproof coiled material. Since the PVC raw material in the PVC waterproof coiled material contains low molecular weight plasticizers, when exposed to sunlight, ozone, freeze-thaw When the natural conditions are destroyed, the plasticizer is easy to volatilize and migrate, which will cause cracks in the PVC coil and cause waterproof failure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A PVC waterproof membrane, prepared from the following raw materials in parts by weight: 75 parts of PVC resin particles, 15 parts of rubber particles, 50 parts of plasticizer, 0.5 parts of antioxidant, 0.5 parts of stabilizer, and 8 parts of flame retardant And 0.5 parts of light shielding agent.

[0013] Wherein, the PVC resin material is prepared from the following raw materials in parts by weight: 100 parts of PVC resin powder, CaCo 3 50 parts, 43 parts of DOP, 11 parts of DOA, 5 parts of triple salt, 3 parts of di-salt and 3 parts of chlorinated paraffin.

[0014] Preparation:

[0015] Step 1: 100 parts of PVC resin powder, CaCo 3 50 parts, 43 parts of DOP, 11 parts of DOA, 5 parts of tri-salt, 3 parts of di-salt and 3 parts of chlorinated paraffin; after mixing, put it into a high-speed mixer for mixing, the mixing time is 5 minutes, and the temperature is between 80 and 100 °C;

[0016] Step 2: Put the raw materials mixed in step 1 into a 75-type twin-screw ex...

Embodiment 2

[0024] A PVC waterproof membrane, prepared from the following raw materials in parts by weight: 95 parts of PVC resin particles, 10 parts of rubber particles, 70 parts of plasticizer, 0.3 parts of antioxidant, 1.0 part of stabilizer, and 3 parts of flame retardant And light shielding agent 0.8 parts.

[0025] Wherein, the PVC resin material is prepared from the following raw materials in parts by weight: 100 parts of PVC resin powder, CaCo 3 50 parts, 43 parts of DOP, 11 parts of DOA, 5 parts of triple salt, 3 parts of di-salt and 3 parts of chlorinated paraffin.

[0026] The preparation method is the same as in Example 1.

Embodiment 3

[0028] A PVC waterproof membrane, prepared from the following raw materials in parts by weight: 80 parts of PVC resin particles, 14 parts of rubber particles, 55 parts of plasticizer, 0.5 parts of antioxidant, 0.6 parts of stabilizer, and 7 parts of flame retardant And light shielding agent 0.6 parts.

[0029] Wherein, the PVC resin material is prepared from the following raw materials in parts by weight: 100 parts of PVC resin powder, CaCo 3 50 parts, 43 parts of DOP, 11 parts of DOA, 5 parts of triple salt, 3 parts of di-salt and 3 parts of chlorinated paraffin.

[0030] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of building materials, in particular to a PVC waterproof roll. The PVC waterproof roll is prepared from PVC resin particles, rubber particles, a plasticizer, an antioxidant, a stabilizer, a fire retardant and a light screening agent. In the technical scheme of the PVC waterproof roll disclosed by the invention, due to the fact that rubber has excellent ageing-resistant performance and higher heat resistance, the rubber is taken as a main material of modified PVC, and an ultraviolet light absorber, the light screening agent, the antioxidant and the like are added in the mixture of the rubber particles and the PVC particles, so that the outdoor ageing-resistant performance of the PVC waterproof roll is improved, and a double-protective effect is achieved with ethylene propylene rubber; and the PVC waterproof roll disclosed by the invention guarantees a physical performance index of the original PVC roll, the service life of the product is also prolonged, and the product life is more than 15 years. The PVC waterproof roll has the advantages of low production cost and good waterproof effect, the competitive advantages are obvious compared with similar products, and the PVC waterproof roll is suitable for being used in the field of architectural ornament.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a PVC waterproof coiled material. Background technique [0002] Roof leakage is a common problem in construction projects. To ensure the quality of waterproof projects, in addition to design and construction reasons, it is also necessary to select suitable waterproof materials. At present, there are many types of flexible waterproof materials on the market with different properties, such as petroleum, asphalt, and linoleum. However, when used as waterproof materials, they have problems of poor low-temperature flexibility, easy aging, and short service life. [0003] The polyester fiber internally reinforced polyvinyl chloride (PVC) waterproof membrane is a thermoplastic PVC membrane. The membrane uses polyester fabric as a reinforcing rib. Through a special extrusion coating process, the double-sided Polyvinyl chloride plastic layer and polyester reinforcing rib in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L21/00C08L91/06C08K13/02C08K3/26C08K5/12
Inventor 田几源
Owner YUNNAN YUANAN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap