Antistatic knitted fabric and preparation method thereof

An antistatic and knitted fabric technology, which is applied in knitting, weft knitting, textiles and papermaking, etc., can solve the problems of easy generation of static electricity, high cost, anti-ultraviolet radiation, and weak fire prevention ability, so as to simplify the production process and improve production Good efficiency and thermal stability

Inactive Publication Date: 2016-01-20
SUZHOU SHUNTANG CHEM FIBER
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional knitted fabrics are usually composed of natural fibers, synthetic fibers or their blends. The antistatic effect is not good, it is easy to generate static electricity, and the anti-ultraviolet and fireproof capabilities are not strong. The multi-functional finishing process is complicated and the cost is high; while polyester fiber has a It is crisp and has good thermal stability, so it has good application prospects in clothing, bedding, interior decoration, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Preparation of polyester fiber Yilun yarn: the equivalent of terephthalic acid and ethylene glycol are subjected to polycondensation reaction at a temperature of 60 ℃, and the reaction time is 15 hours to generate polyester stock solution, and then spin it to obtain The polyester fiber is then sorted into threads by a shuttle to obtain polyester fiber Yilun yarn. The length of the polyester fiber Yilun yarn is greater than 60mm and the fineness is 20-25den;

[0025] (2) Fading: the raw material polyester fiber Yilun silk is fading treated with sodium hypochlorite fading agent, and the fading temperature is kept above 120℃;

[0026] (3) Twisting: twisting polyester fiber Yilun silk: 50 parts; wool: 10 parts; flax: 5 parts; ramie: 5 parts; viscose: 3 parts twisting, and adding twisting auxiliary, water and ammonium Mix 1.5 parts of salt and ensure that the single-strand twist is higher than 160 turns / 10cm to form yarn;

[0027] (4) Coloring: use a color steaming machine to ...

Embodiment 2

[0030] (1) Preparation of polyester fiber Yilun yarn: the equivalent of terephthalic acid and ethylene glycol are subjected to polycondensation reaction at a temperature of 60 ℃, and the reaction time is 15 hours to generate polyester stock solution, and then spin it to obtain The polyester fiber is then sorted into threads by a shuttle to obtain polyester fiber Yilun yarn. The length of the polyester fiber Yilun yarn is greater than 60mm and the fineness is 20-25den;

[0031] (2) Fading: the raw material polyester fiber Yilun silk is fading treated with sodium hypochlorite fading agent, and the fading temperature is kept above 120℃;

[0032] (3) Twisting: Polyester fiber Yilun silk: 60 parts; wool: 15 parts; flax: 10 parts; ramie: 8 parts; viscose: 5 parts twisting, and adding twisting aids, water and alkane 0.5 part of base amino acid is mixed, and the twist of single strand is higher than 160 twists / 10cm to form yarn;

[0033] (4) Coloring: use a color steaming machine to color t...

Embodiment 3

[0036] (1) Preparation of polyester fiber Yilun yarn: the equivalent of terephthalic acid and ethylene glycol are subjected to polycondensation reaction at a temperature of 55°C, and the reaction time is 18 hours to generate polyester stock solution, and then spin it to obtain The polyester fiber is then sorted into threads by a shuttle to obtain polyester fiber Yilun yarn. The length of the polyester fiber Yilun yarn is greater than 60mm and the fineness is 20-25den;

[0037] (2) Fading: the raw material polyester fiber Yilun silk is fading treated with sodium hypochlorite fading agent, and the fading temperature is kept above 120℃;

[0038] (3) Twisting: the polyester fiber Yilun yarn: 55 parts; wool: 12 parts; flax: 8 parts; ramie: 6 parts; viscose: 4 parts twisting, and adding twisting aids, water and seasoning Mix 1.0 part of ammonium salt, and ensure that the single-strand twist is higher than 160 turns / 10cm to form yarn;

[0039] (4) Coloring: use a color steaming machine to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic knitted fabric and a preparation method thereof; the antistatic knitted fabric comprises the following components by mass percentage: 50-60 parts of polyester fiber proliferation nylon filament; 10-15 parts of wool; 5-10 parts of flax; 5-8 parts of ramie; 3-5 parts of viscose glue; 0.5-1.5 parts of antistatic agent. The preparation method comprises fading, twisting, coloring, compositing and making sheet so as to obtain the knitted fabric. The knitted fabric made by the raw materials and preparation method is stiff in appearance, good in heat stability, soft, no pilling, is antistatic, and production technology is simplified, thus improving production efficiency.

Description

technical field [0001] The invention relates to a knitted fabric and a preparation method thereof, belonging to the technical field of textiles. Background technique [0002] Traditional knitted fabrics are usually composed of natural fibers, synthetic fibers or their blends. The antistatic effect is not good, it is easy to generate static electricity, and the anti-ultraviolet and fireproof capabilities are not strong. The multi-functional finishing process is complicated and the cost is high; while polyester fiber has a It has the advantages of crispness and good thermal stability, so it has good application prospects in clothing, bedding, interior decoration, etc. Contents of the invention [0003] In order to solve the above-mentioned problems in the prior art, the present invention provides an antistatic knitted fabric with a simple preparation method and high product quality and a preparation method thereof. [0004] In order to achieve the above-mentioned purpose of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D06M11/30D02G3/04D06M101/32
Inventor 刘惠峰
Owner SUZHOU SHUNTANG CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap