Green body of environment-friendly ceramic tile, environment-friendly ceramic tile and preparation method of ceramic tile

A ceramic brick and environmental protection technology, applied in the field of building materials, can solve the problems of poor bonding of raw materials, difficult production control, low firing temperature, etc., and achieve the effects of enhancing strength, improving adhesion, and overcoming low yield

Active Publication Date: 2016-01-27
SICHUAN JIANHUI CERAMIC CO LTD
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides green ceramic bricks, environmentally friendly ceramic bricks and a preparation method for the ceramic bricks, in order to overcome the disadvantages of low firing temperature of ceramic waste, poor bonding of raw materials and low strength, and difficult production control. It has the characteristics of high strength and high whiteness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] An environment-friendly ceramic tile green body, comprising the following components in parts by mass: 20 parts of dolomite clay, 35 parts of ceramic polishing waste, 10 parts of limestone, 5 parts of diaspore, and 8 parts of soft kaolin. Among them, the particle size of ceramic polishing waste is 100 mesh, the particle size of diaspore is 80 mesh, and the soft kaolin is 110 mesh.

Embodiment 2

[0041] A kind of environment-friendly ceramic brick green body comprises the following components in parts by mass: 21 parts of dolomite clay, 18 parts of ceramic scraps, 18 parts of ceramic scraps, 11 parts of limestone, 4 parts of boehmite, aluminum trihydrate 2 parts stone, 5 parts ball clay, 4 parts cream clay. Among them, the particle size of ceramic scrap is 105 mesh, the particle size of ceramic scrap is 110 mesh, the particle size of boehmite is 85 mesh, the particle size of gibbsite is 80 mesh, the particle size of ball clay is 105 mesh, and the particle size of cream clay is 120 mesh.

Embodiment 3

[0043] A kind of environment-friendly ceramic tile green body comprises the following components in parts by mass: 23 parts of dolomite clay, 15 parts of ceramic polishing waste, 20 parts of ceramic scrap, 17 parts of ceramic scrap, 12 parts of limestone, diaspore 2 parts, 3 parts boehmite, 4 parts gibbsite, 5 parts soft kaolin, 3 parts ball clay, 6 parts cream clay. Among them, the particle size of ceramic polishing waste is 120 mesh, the particle size of ceramic scrap is 110 mesh, the particle size of ceramic scrap is 105 mesh, the particle size of diaspore is 90 mesh, the particle size of boehmite is 80 mesh, the particle size of gibbsite is 85 mesh, and the particle size of soft kaolin is 130 mesh. Mesh, ball clay particle size 115 mesh, cream clay particle size 125 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of building materials and particularly relates to a green body of an environment-friendly ceramic tile, the environment-friendly ceramic tile and a preparation method of the ceramic tile. The green body of the environment-friendly ceramic tile comprises the following components in parts by mass: 20-25 parts of dolomite clay, 35-56 parts of ceramic wastes, 10-15 parts of limestone, 5-10 parts of aluminum ores and 8-15 parts of soft clay. The strength of the green body of the polished waste ceramic tile is larger than 0.25MPa, and the drying strength of the green body is larger than 1.8MPa; the whiteness of a finished product of the ceramic tile is high and higher than that of the like product; and environment pollution is greatly reduced, and the ceramic wastes are changed into things of value.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an environment-friendly ceramic brick green body, an environment-friendly ceramic brick and a preparation method of the ceramic brick. Background technique [0002] With the continuous progress of society, people's requirements for environmental protection are getting higher and higher. At present, in the ceramic industry, there are many waste slurry produced by cleaning polished tiles and other products, as well as various waste materials that need to be treated. Slurry and waste materials have a relatively low degree of treatment and utilization, and most of them are landfilled as waste, which has an impact on environmental pollution, and at the same time causes a lot of waste of manpower and financial resources for environmental governance. Therefore how to effectively utilize it has become a topic that ceramic manufacturers and ceramic workers pay close attention to. The ce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/24
CPCY02P40/60
Inventor 宋黎
Owner SICHUAN JIANHUI CERAMIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com