Ceramic anodizing process for frosted glaze of aluminum alloy

A kind of anodizing and aluminum alloy technology, applied in anodizing and other directions, can solve the problem of high hardness, high glaze anti-scratch, acid and alkali resistance, vibration grinding UV/salt spray resistance, high-gloss glaze effect , multiple processes, etc., to achieve the effect of expanding the range of surface decoration color, satisfying the appearance of color and luster, and good wear resistance

Inactive Publication Date: 2016-02-03
HUIZHOU ZEHONG TECH CO LTD
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the more mature one is ordinary sulfuric acid decorative anodizing. The film pores formed by ordinary sulfuric acid decorative anodizing are honeycomb, and the hardness is far inferior to that of ceramic anodizing. The existing aluminum alloy anodizing process is as follows: Machining materials (Aluminum alloy materials include 1000 series, 5000 series, 6000 series, 7000 series) - cleaning - drying - sandblasting - hanging - degreasing - chemical polishing - neutralization - ordinary anodizing - dyeing - sealing - drying, the most common The dyeing of aluminum alloy anodic oxi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic anodizing process for frosted glaze of aluminum alloy
  • Ceramic anodizing process for frosted glaze of aluminum alloy
  • Ceramic anodizing process for frosted glaze of aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The anodic oxidation process of aluminum alloy frosted glazed ceramics comprises the following steps:

[0022] 1) Machined aluminum alloy; 2) Three-stage polishing; 3) Finishing; 4) Hanging; 5) Cleaning; 6) Drying; 7) Sandblasting; 8) Hanging; 9) Degreasing; 10) Chemical Polishing; 11) neutralization; 12) dull white; 13) neutralization; 14) ceramic anode; 15) dyeing and sealing; 16) drying; and; 21) ceramic anode; 22) dyeing and sealing; 24) drying.

[0023] For the machined aluminum alloy in step 1, the aluminum alloy materials that can be selected include 1000 series, 5000 series, 6000 series, 7000 series, etc., which are machined and cut into the required size and shape. The above-mentioned types of aluminum alloys can be obtained from purchased in the market;

[0024] The three-stage polishing process of step 2 is as follows, first rough polishing, then intermediate polishing, and finally fine polishing, using physical three-stage fine polishing to polish the mach...

Embodiment 2

[0040] The anodic oxidation process of aluminum alloy frosted glazed ceramics comprises the following steps:

[0041] 1) Machined aluminum alloy; 2) Three-stage polishing; 3) Finishing; 4) Hanging; 5) Cleaning; 6) Drying; 7) Sandblasting; 8) Hanging; 9) Degreasing; 10) Chemical Polishing; 11) neutralization; 12) dull white; 13) neutralization; 14) ceramic anode; 15) dyeing and sealing; 16) drying; and; 21) ceramic anode; 22) dyeing and sealing; 24) drying.

[0042] Compared with Example 1, it has the following differences. Specifically, the blunt whitening in step 12 is carried out in an aqueous solution of phosphate, which contains dibutoxyethanol, and the phosphate can be sodium phosphate , sodium dihydrogen phosphate, sodium hydrogen phosphate, potassium phosphate, potassium dihydrogen phosphate, potassium hydrogen phosphate, etc.

[0043] Specifically, the mass concentration of the phosphate aqueous solution is 500 g / L, and the mass concentration of the dibutoxyethanol i...

Embodiment 3

[0047] The anodic oxidation process of aluminum alloy frosted glazed ceramics comprises the following steps:

[0048] 1) Machined aluminum alloy; 2) Three-stage polishing; 3) Finishing; 4) Hanging; 5) Cleaning; 6) Drying; 7) Sandblasting; 8) Hanging; 9) Degreasing; 10) Chemical Polishing; 11) neutralization; 12) dull white; 13) neutralization; 14) ceramic anode; 15) dyeing and sealing; 16) drying; and; 21) ceramic anode; 22) dyeing and sealing; 24) drying.

[0049] Compared with Example 1, it has the following differences. Specifically, the blunt whitening in step 12 is carried out in an aqueous solution of phosphoric acid.

[0050] Specifically, the mass concentration of the phosphate aqueous solution is 300 g / L, and the mass concentration of the dibutoxyethanol is 15 g / L. Through the formula of phosphoric acid and dibutoxyethanol, the surface of the degreased aluminum alloy is blunted. White, the method of covering the polishing material grain by the principle of chemical ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of anodizing processes, in particular to a ceramic anodizing process for a frosted glaze of aluminum alloy. The process includes the following steps of (1) machining of the aluminum alloy, (2) three-stage polishing, (3) sleeking, (4) racking, (5) cleaning, (6) drying, (7) sand blasting, (8) racking, (9) degreasing, (10) chemical polishing, (11) neutralization, (12) whitening, (13) neutralization, (14) ceramic anodizing, (15) dyeing and hole sealing, (16) drying, (17) C-angle highlighting, (18) racking, (19) degreasing, (20) neutralization, (21) ceramic anodizing, (22) dyeing and hole sealing, and (23) drying. The machined product is polished into a smooth surface similar to a mirror surface, so that basic requirements of the smooth glaze surface are met; then the matted or frosted effect is achieved through the sand blasting process, so that viewing angle requirements of customers are met; by means of the method that the basic brightness of the sand surface is improved through the chemical polishing principle, preparations are made for the frosted ceramic anodizing process; products with frosted and matted glazes are produced through the ceramic anodizing process, the color fastness of an oxidation film is improved, and the good functions of abrasion resistance, corrosion resistance and weather resistance are achieved.

Description

technical field [0001] The invention relates to the technical field of anodic oxidation technology, in particular to the anodic oxidation technology of aluminum alloy frosted glazed ceramics. Background technique [0002] With the widespread use of aluminum alloy in the current 3C industry, as well as the advancement of science and technology and the improvement of people's living standards, the aesthetics have undergone significant changes, and its surface treatment technology has also developed rapidly. Among aluminum alloy surface treatment technologies, anodic oxidation technology is currently the most widely used and most successful. Anodizing is an electrolytic oxidation process in which the surface of aluminum alloys is usually converted into an oxide film. This oxide film has protective, decorative, and some other functional properties. Anodizing technology is a reliable metal surface treatment process. It guarantees consistent gloss and color of the material in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D11/08C25D11/10C25D11/22C25D11/24C25D11/16
Inventor 江登山陈俊王亮
Owner HUIZHOU ZEHONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products