A post-finishing and fabric technology, applied in fiber processing, textiles and papermaking, etc., can solve the problems of flame retardant, antibacterial, anti-wrinkle, anti-static performance and washability, and achieve strong washability and excellent flame retardant. Effect

Inactive Publication Date: 2016-02-03
常熟市华谊织造有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The flame retardant, antibacterial, anti-wrinkle, antistatic properties and washable properties of existing fabrics need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A post-finishing process for polyester fabrics, comprising the steps of:

[0021] 1) Add 1 to 2 parts by mass of resorcinol, 3.3 parts by mass of aniline-3,5-disulfonic acid, 2.9 parts by mass of potassium sorbate, and 0.7 parts by mass of zinc stearate in 37 parts by mass of deionized water, mix and stir Uniform;

[0022] 2) At the same time, slowly add 1.9 parts by mass of nonylphenol ethoxylate carboxylate, 2.8 parts by mass of ethyl acetate, 1.1 parts by mass of sodium benzoate, and 2.4 parts by mass of dimethylolurea, and continue to stir until fully mixed and uniform. Finishing agent;

[0023] 3) Pad the fabric in the dipping solution containing the finishing agent, and dry it at a constant temperature.

Embodiment 2

[0025] The post-finishing process of polyester fabrics includes the following steps:

[0026] 1) 1 mass part of resorcinol, 3.3 mass parts of aniline-3,5-disulfonic acid, 2.9 mass parts of potassium sorbate, and 0.7 mass part of zinc stearate were mixed in 37 mass parts of deionized water, and stirred evenly;

[0027] 2) At the same time, slowly add 1.9 parts by mass of nonylphenol ethoxylate carboxylate, 2.8 parts by mass of ethyl acetate, 1.1 parts by mass of sodium benzoate, and 2.4 parts by mass of dimethylolurea, and continue to stir until fully mixed and uniform. Finishing agent;

[0028] 3) Pad the fabric in the dipping solution containing the finishing agent, and dry it at a constant temperature.

Embodiment 3

[0030] The post-finishing process of polyester fabrics includes the following steps:

[0031] 1) Add 2 parts by mass of resorcinol, 3.3 parts by mass of aniline-3,5-disulfonic acid, 2.9 parts by mass of potassium sorbate, and 0.7 parts by mass of zinc stearate into 37 parts by mass of deionized water and mix them evenly;

[0032] 2) At the same time, slowly add 1.9 parts by mass of nonylphenol ethoxylate carboxylate, 2.8 parts by mass of ethyl acetate, 1.1 parts by mass of sodium benzoate, and 2.4 parts by mass of dimethylolurea, and continue to stir until fully mixed and uniform. Finishing agent;

[0033] 3) Pad the fabric in the dipping solution containing the finishing agent, and dry it at a constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an after-finishing process of a dacron fabric. The after-finishing process comprises the following steps: (1) adding the following components into 37 parts of de-ionized water in parts by mass: 1-2 parts of resorcinol, 3.3 parts of aniline-3,5-disulfonic acid, 2.9 parts of potassium sorbate and 0.7 part of zinc stearate, and mixing and uniformly stirring; (2) slowly adding the following components in parts by mass: 1.9 parts of nonylphenol ethoxylate carboxylate, 2.8 parts of ethyl acetate, 1.1 parts of sodium benzoate and 2.4 parts of dimethylol urea, and further stirring until the components are sufficiently and uniformly mixed to prepare a finishing agent; and (3) padding a fabric into an impregnation solution containing the finishing agent to be subjected to padding treatment, and drying at a constant temperature. According to the after-finishing process of the dacron fabric, provided by the invention, the finished fabric has excellent inflaming retarding, antibacterial, anti-wrinkle and anti-static performances, and strong washing fastness.

Description

technical field [0001] The invention relates to a post-finishing process for polyester fabrics. Background technique [0002] The flame retardancy, antibacterial, anti-wrinkle, antistatic performance and washability of existing fabrics all need to be improved. Contents of the invention [0003] The object of the present invention is to provide a post-finishing process for polyester fabrics. The finished fabrics have excellent flame-retardant, anti-bacterial, anti-wrinkle, anti-static properties, and strong washability. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of post-finishing process of polyester fabric, comprising the steps: [0005] 1) Add 1 to 2 parts by mass of resorcinol, 3.3 parts by mass of aniline-3,5-disulfonic acid, 2.9 parts by mass of potassium sorbate, and 0.7 parts by mass of zinc stearate in 37 parts by mass of deionized water, mix and stir Uniform; [0006] 2) At the same time, sl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/342D06M13/152D06M13/203D06M13/188D06M13/207D06M13/224D06M13/432
Inventor 孙国祥
Owner 常熟市华谊织造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap