A technology of glass film and dodecyl glucoside, which is applied in anti-corrosion coatings, biocide-containing paints, anti-fouling/underwater coatings, etc. It can solve the problems that the glass film needs to be improved, achieve anti-static performance, and improve heat insulation Effect

Inactive Publication Date: 2016-02-17
CHANGSHU SEDY INLAY GLASS PROD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat insulation, heat preservation, cold resistance, explosion-proof, corrosion resistance, antibacterial and antistatic properties of the existing glass film need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A glass film consisting of the following components in parts by weight:

[0015] 14 parts of butyl acrylate, 1-2 parts of propylene glycol, 0.2 parts of calcium phosphate, 1.4 parts of aluminum nitride powder, 1.3 parts of acrylic acid, 3.4 parts of silicon dioxide, 2.3 parts of aluminum phosphate, 4.5 parts of dodecyl glucoside.

Embodiment 2

[0017] The glass film consists of the following components in parts by weight:

[0018] 14 parts of butyl acrylate, 1 part of propylene glycol, 0.2 parts of calcium phosphate, 1.4 parts of aluminum nitride powder, 1.3 parts of acrylic acid, 3.4 parts of silicon dioxide, 2.3 parts of aluminum phosphate, 4.5 parts of lauryl glucoside.

Embodiment 3

[0020] The glass film consists of the following components in parts by weight:

[0021] 14 parts of butyl acrylate, 2 parts of propylene glycol, 0.2 parts of calcium phosphate, 1.4 parts of aluminum nitride powder, 1.3 parts of acrylic acid, 3.4 parts of silicon dioxide, 2.3 parts of aluminum phosphate, 4.5 parts of lauryl glucoside.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass film which is prepared from, by weight, 14 parts of butyl acrylate, 1-2 parts of propylene glycol, 0.2 part of calcium phosphate, 1.4 parts of aluminum nitride powder, 1.3 parts of acrylic acid, 3.4 parts of silicon dioxide, 2.3 parts of aluminum phosphate and 4.5 parts of dodecyl polyglucoside. The glass film can improve the heat-isolation, heat-preservation, cold-resistant, anti-explosion, anti-corrosion, anti-bacterial and anti-static performance of glass.

Description

technical field [0001] The present invention relates to glass films. Background technique [0002] Glass film can change the monotonous and transparent image of ordinary glass and add beauty to indoor and outdoor. However, the heat insulation, heat preservation, cold resistance, explosion-proof, corrosion resistance, antibacterial, and antistatic properties of the existing glass film all need to be improved. Contents of the invention [0003] The object of the present invention is to provide a glass film, which can improve the performance of heat insulation, heat preservation, cold resistance, explosion protection, corrosion resistance, antibacterial and antistatic properties of glass. [0004] In order to achieve the above object, the technical solution of the present invention is to design a glass film, which consists of the following components in parts by weight: [0005] 14 parts of butyl acrylate, 1-2 parts of propylene glycol, 0.2 parts of calcium phosphate, 1.4 p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D5/24C09D5/08C09D7/12C09D5/14
Inventor 陶耀军
Owner CHANGSHU SEDY INLAY GLASS PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap