An alloy steel, combined technology, applied in the field of combined alloy steel, achieves the effect of excellent comprehensive performance, maintaining thermal conductivity and welding performance, and improving toughness
Active Publication Date: 2017-09-22
张家港市新凯带钢制造有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] Hardware equipment mainly includes most of the metal parts or combined parts on the market. Most of the hardware equipment is composed of alloy steel; abrasiveness, high strength and other properties, but most of the alloy steels on the market are difficult to guarantee good wear resistance when their strength or hardness is improved. On this premise, the alloy steel is limited Application range
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Embodiment 1: A combined alloy steel, the weight percentage of each component in the alloy steel is as follows: V0.08%, Ca 0.15%, Cu 0.18%, P 0.002%, Al 0.28%, Ti 0.02%, Mo 0.1%, Zn 0.35%: Sn 0.08%, Cr 0.32%, Si 0.28%, Ni 0.8%, Mn 0.25%, S 0.01%, C 0.51%, and the rest is Fe.
Embodiment 2
[0016] Embodiment 2: A combined alloy steel, the weight percentage of each component in the alloy steel is as follows: V0.085%, Ca 0.165%, Cu 0.23%, P 0.0035%, Al 0.295%, Ti 0.035%, Mo 0.012%, Zn 0.55%: Sn0.09%, Cr 0.62%, Si 0.31%, Ni 1.2%, Mn 0.33%, S 0.015%, C 0.62%, and the rest is Fe.
Embodiment 3
[0017] Embodiment 3: A combined alloy steel, the weight percentage of each component in the alloy steel is as follows: V0.082%, Ca 0.155%, Cu 0.19%, P 0.0028%, Al 0.29%, Ti 0.027%, Mo 0.11%, Zn 0.42%: Sn 0.085%, Cr 0.45%, Si 0.27%, Ni 0.9%, Mn 0.29%, S 0.012%, C 0.56%, and the rest is Fe.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses combined alloy steel which comprises the following components by weight percent: 0.08-0.085% of V, 0.15-0.165% of Ca, 0.18-0.23% of Cu, 0.002-0.0035% of P, 0.28-0.295% of Al, 0.02-0.035% of Ti, 0.1-0.12% of Mo, 0.35-0.55% of Zn, 0.08-0.09% of Sn, 0.32-0.62% of Cr, 0.28-0.31% of Si, 0.8-1.2% of Ni, 0.25-0.33% of Mn, 0.01-0.015% of S, 0.51-0.62% of C and the balance of Fe. The components are combined to obtain the alloy steel through the combination function of a plurality of elements, and the comprehensive performance of the alloy steel is excellent; the produced alloy steel is applied to production of hardware, so that the processing property of hardware is greatly improved, and the application range of hardware is broadened.
Description
Technical field [0001] The invention relates to the production field of hardware equipment, in particular to a combined alloy steel suitable for manufacturing hardware parts. Background technique [0002] An iron-carbon alloy formed by adding an appropriate amount of one or more alloying elements on the basis of ordinary carbon steel. According to the different added elements, and adopting appropriate processing technology, special properties such as high strength, high toughness, wear resistance, corrosion resistance, low temperature resistance, high temperature resistance, and non-magnetic properties can be obtained. The main alloying elements of alloy steel are silicon, manganese, chromium, nickel, molybdenum, tungsten, vanadium, titanium, niobium, zirconium, cobalt, aluminum, copper, boron, rare earth and so on. Among them, vanadium, titanium, niobium, zirconium, etc. are strong carbide-forming elements in steel. As long as there is enough carbon, under appropriate condition...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more