Spiral carbon fiber composite ceramics for activating water and its production method and application
A technology of spiral carbon fiber and composite ceramics, applied in the field of water treatment, can solve the problems of low raw water quality and difficulty in completely removing trace harmful drugs and chemical substances, and achieve the effects of convenient use, inhibition of bacterial reproduction, and improvement of human brain blood flow
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] Example 1. Preparation of spiral carbon fiber composite ceramic beads: take 0.5wt% spiral carbon fiber and 99.5% by weight ceramic floor tile powder, first spray dry the ceramic floor tile powder at 40, and then mix the spiral carbon fiber and ceramic floor tile powder by a gravity-free method Evenly, the composite body is made by rolling and rolling with water. Balls with a diameter of 3-5 mm are separated by a sieve and dried, and then placed in an oxygen-free atmosphere furnace and sintered at a high temperature of 1180°C to make spiral carbon fiber composite ceramic beads.
[0032] In the experiment, by adding spiral carbon fiber composite ceramic beads to 10 liters of tap water with a cerebral blood flow rate of 1.8L / min, the cerebral blood flow rate of the outlet water was rapidly increased to 7L / min.
Embodiment 2
[0033] Example 2: Preparation of spiral carbon fiber composite ceramic particles: firstly select 37wt% red loam and 63wt% granite powder, then add 100wt% water, pass through ball milling to a 10,000-hole sieve with 0.5wt% mud, and then add 0.2wt% spiral The carbon fiber is stirred and mixed uniformly, and the mixed mud is dehydrated into a mud cake with a filter press. The mud cake is dried and crushed by a granulator into particles of 2-4 mm, and then sintered in an oxygen-free atmosphere furnace at 1050°C.
[0034] In the experiment, several spiral carbon fiber composite ceramic particles were taken and put into a tube with an inner diameter of 17mm and a length of 450mm. Tap water with a cerebral blood flow rate of 1.8L / min was flowed at a flow rate of 50L / min, and the cerebral blood flow rate of the outlet water was increased to 6L. / min.
Embodiment 3
[0035] Example 3: Preparation of spiral carbon fiber composite ceramic cylinder: take 23wt% red loam, 17wt% black clay, 60wt% granite powder, add 100wt% water, ball mill to a 10,000-hole sieve with 2wt% slurry, and add 1wt% CMC Stir and mix uniformly. Dehydrate the mixed mud with a filter press to form mud cakes. Use a mud mixer to extrude mud sticks with a diameter of 5 mm and cut them into 5 mm long mud sections. The mud sections are dried in an oxygen-free atmosphere furnace at 1000°C Sintered.
[0036] In the experiment, water with a cerebral blood flow rate of 0.6L / min was added to a 200-liter container, and a ceramic cylinder containing spiral carbon fiber was added to it. After stirring, the cerebral blood flow rate was measured at 6L / min.
[0037] The application of the above-mentioned spiral carbon fiber composite ceramics is specifically: in the application of drinking water treatment, spiral carbon fiber composite ceramics can be added to the water container, or spiral c...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com