3D printing floor

A 3D printing and floor technology, applied in the direction of additive processing, can solve the problems of cumbersome floor construction, labor and material resources, etc., and achieve the effects of long service life, fast drying and good chemical resistance.

Active Publication Date: 2016-03-23
浙江西塘实业有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a 3D printing floor, which solves the cu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] 3D printing floor, the floor is composed of the following components by weight: 30 parts of polyurethane resin, 10 parts of epoxy acrylate, 15 parts of 1,6-hexanediol diacrylate, and 15 parts of dipropylene glycol diacrylate: 10 parts, photoinitiator 127: 2.5 parts, talc powder: 10 parts, bentonite: 0.5 parts, defoamer: 0.4 parts, dispersant: 0.3 parts, color paste: 1 part.

[0013] The preparation method is:

[0014] a. Mix the above-mentioned 3D printing floor materials, and spray the adhesive micro-droplets layer by layer to form and superimpose the 3D printing materials layer by layer through the method of droplet jet bonding, thereby forming a 3D printing floor body;

[0015] b. The 3D printed floor body is shaped at room temperature to obtain a 3D printed floor.

Embodiment 2

[0017] 3D printing floor, the floor is composed of the following components by weight: 35 parts of polyurethane resin, 20 parts of epoxy acrylate, 20 parts of 1,6-hexanediol diacrylate, and 20 parts of dipropylene glycol diacrylate: 15 parts, photoinitiator 127: 3.0 parts, talc powder: 15 parts, bentonite: 1.0 parts, defoamer: 0.6 parts, dispersant: 0.5 parts, color paste: 8 parts.

[0018] The preparation method is:

[0019] a. Mix the above-mentioned 3D printing floor materials, and spray the adhesive micro-droplets layer by layer to form and superimpose the 3D printing materials layer by layer through the method of droplet jet bonding, thereby forming a 3D printing floor body;

[0020] b. The 3D printed floor body is shaped at room temperature to obtain a 3D printed floor.

Embodiment 3

[0022] 3D printing floor, the floor is composed of the following components by weight: 33 parts of polyurethane resin, 15 parts of epoxy acrylate, 17 parts of 1,6-hexanediol diacrylate, and 17 parts of dipropylene glycol diacrylate: 12 parts, photoinitiator 127: 2.7 parts, talc powder: 13 parts, bentonite: 0.8 parts, defoamer: 0.5 parts, dispersant: 0.4 parts, color paste: 4 parts.

[0023] The preparation method is:

[0024] a. Mix the above-mentioned 3D printing floor materials, and spray the adhesive micro-droplets layer by layer to form and superimpose the 3D printing materials layer by layer through the method of droplet jet bonding, thereby forming a 3D printing floor body;

[0025] b. The 3D printed floor body is shaped at room temperature to obtain a 3D printed floor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a 3D printing floor. The 3D printing floor comprises the following components, by weight, 30-35 parts of polyurethane resin, 10-20 parts of epoxy acrylate, 15-20 parts of 1,6-hexanediol diacrylate, 10-15 parts of dipropylene glycol diacrylate, 2.5-3.0 parts of photoinitiator 127, 10-15 parts of talcum powder, 0.5-1.0 part of bentonite, 0.4-0.6 part of defoaming agent, 0.3-0.5 part of dispersant and 1-8 parts of color paste. The construction technology time is shortened greatly, and problems of materials and technology processes are solved through a new technology. The3D printing floor is presented on the ground through a 3D printer, which is simple and rapid, and the performances of the original materials are not changed.

Description

technical field [0001] The invention belongs to the field of construction engineering, and in particular relates to a 3D printing floor. Background technique [0002] With the advancement of science and technology, the optimization of various materials, ecology, and exquisite craftsmanship, the final result is that the technologies in various fields are also changing with each passing day, and 3D printing technology is also advancing in various fields with the pace of the times. 3D printing floors also occupy a place in this field. It greatly shortens the construction process time, and also solves the problems in materials and process with new technology. Here is a study of a 3D printed floor material, which is presented on the ground through a 3D printer, which is simple and fast, and the performance of the original material will not change. Contents of the invention [0003] The purpose of the present invention is to provide a 3D printing floor, which solves the cumber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/04C08K13/02C08K3/34B33Y70/00B29C67/00
CPCB29C67/00C08K3/34C08K3/346C08K13/02C08L2201/08C08L75/04
Inventor 郑鸿芳苗建成陈宙飞谢桂秀
Owner 浙江西塘实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap