A technology of corrosion-resistant concrete and mass fraction, applied in the field of concrete, can solve the problems of weak corrosion resistance, inevitable corrosion, and shortened service life of concrete, and achieve the effect of resisting external corrosive substances, strong corrosion resistance, and antifreeze Good results
Inactive Publication Date: 2016-04-06
QINGDAO HONGYU ENVIRONMENTAL PROTECTION AIR CONDITIONING EQUIP
View PDF0 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Concrete is a durable material, but it is essentially a heterogeneous porous material. Under the erosion of carbon dioxide, water, chloride ions, sulfate and other media, it is inevitably corroded by external factors. Concrete It will accelerate the damage and greatly shorten the service life
The existing concrete has weak corrosion resistance and cannot effectively resist the erosion of external corrosive substances
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] A corrosion-resistant concrete made of the following raw materials in parts by mass:
[0012] 50 parts of cement, 5 parts of diisopropanolamine, 7 parts of calcium lignosulfonate, 6 parts of calcium nitrate, 15 parts of urea-formaldehyde resin, 4 parts of monoethanolamine, 8 parts of acrylic emulsion, 7 parts of calcium carbonate, and 8 parts of glass fiber , 6 parts of silica powder, 3 parts of sodium perborate, 14-17 parts of fly ash, 16-18 parts of ceramsite.
Embodiment 2
[0014] A corrosion-resistant concrete is characterized in that: it is made of the following raw materials in parts by mass:
[0015] 55 parts of cement, 7 parts of diisopropanolamine, 8 parts of calcium lignosulfonate, 7 parts of calcium nitrate, 18 parts of urea-formaldehyde resin, 6 parts of monoethanolamine, 9 parts of acrylic emulsion, 10 parts of calcium carbonate, and 9 parts of glass fiber , 7 parts of silica powder, 5 parts of sodium perborate, 15 parts of fly ash, and 17 parts of ceramsite.
Embodiment 3
[0017] A corrosion-resistant concrete made of the following raw materials in parts by mass:
[0018] 50-60 parts of cement, 5-9 parts of diisopropanolamine, 7-9 parts of calcium lignosulfonate, 6-8 parts of calcium nitrate, 15-20 parts of urea-formaldehyde resin, 4-7 parts of monoethanolamine, acrylic emulsion 8-11 parts, 7-12 parts of calcium carbonate, 8-10 parts of glass fiber, 6-8 parts of silica powder, 3-6 parts of sodium perborate, 14-17 parts of fly ash, 16-18 parts of ceramsite .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses anti-corrosion concrete. The anti-corrosion concrete is prepared from the following raw materials in parts by mass: 50 to 60 parts of cement, 5 to 9 parts of diisopropanolamine, 7 to 9 parts of calcium lignosulphonate, 6 to 8 parts of calcium nitrate, 15 to 20 parts of urea formaldehyde resin, 4 to 7 parts of monoethanolamine, 8 to 11 parts of acrylic emulsion, 7 to 12 parts of calcium carbonate, 8 to 10 parts of fiberglass, 6 to 8 parts of silicon dioxide powder, 3 to 6 parts of sodium perborate, 14 to 17 parts of pulverized fuel ash and 16 to 18 parts of haycite. The anti-corrosion concrete disclosed by the invention is strong in corrosion resistance, is capable of resisting corrosion of external corrosive articles, and is good in anti-freezing effect and small in cracking.
Description
technical field [0001] The invention relates to the technical field of concrete, in particular to a corrosion-resistant concrete. Background technique [0002] Concrete is a durable material, but it is essentially a heterogeneous porous material. Under the erosion of carbon dioxide, water, chloride ions, sulfate and other media, it is inevitably corroded by external factors. Concrete It will accelerate the damage and greatly shorten the service life. The existing concrete has weak corrosion resistance and cannot effectively resist the erosion of external corrosive substances. Contents of the invention [0003] In order to solve the above problems, the present invention provides a corrosion-resistant concrete with strong corrosion resistance, effective resistance to external corrosive substances, good antifreeze effect and small cracking. [0004] The technical solution adopted by the present invention to solve the above technical problems is: a corrosion-resistant concre...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/20
CPCC04B28/00C04B2111/20
Inventor 李盛明
Owner QINGDAO HONGYU ENVIRONMENTAL PROTECTION AIR CONDITIONING EQUIP
Login to view more 
Login to view more