Crude-fine fiber blended yarn

A fiber blended and blended yarn technology, applied in fiber treatment, flame retardant fiber, biochemical fiber treatment, etc., can solve the problems of inability to meet customer requirements, single performance of thick and fine fiber blended yarn, and achieve excellent mildew resistance. Effect

Inactive Publication Date: 2016-04-20
常熟市明达腈纺有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The performance of the existing thick and thin fiber blended yarn is single, which cannot meet the requirements of customers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A blended yarn of thick and thin fibers, which is processed through padding, and the padding process comprises the steps of:

[0021] 1) Add 1 to 2 parts by weight of glycerol monostearate, 1.4 parts by weight of hydroxypropyl cellulose, 0.4 parts by weight of zinc sulfate, and 1.2 parts by weight of chloral in 12.7 parts by weight of deionized water, and stir evenly;

[0022] 2) Slowly add 0.7 parts by weight of vinyltriethoxysilane, 0.4 parts by weight of potassium persulfate, 0.8 parts by weight of di-n-octyl-4-isothiazolin-3-one, 0.9 parts by weight of octadecyl di Methyl hydroxyethyl quaternary ammonium nitrate, continue to stir, to fully mix, make finishing solution;

[0023] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 2

[0025] Coarse and thin fiber blended yarn, which is subjected to padding treatment, and the padding treatment comprises the following steps:

[0026] 1) Put 1 part by weight of glycerol monostearate, 1.4 parts by weight of hydroxypropyl cellulose, 0.4 parts by weight of zinc sulfate, and 1.2 parts by weight of chloral into 12.7 parts by weight of deionized water, and stir evenly;

[0027] 2) Slowly add 0.7 parts by weight of vinyltriethoxysilane, 0.4 parts by weight of potassium persulfate, 0.8 parts by weight of di-n-octyl-4-isothiazolin-3-one, 0.9 parts by weight of octadecyl di Methyl hydroxyethyl quaternary ammonium nitrate, continue to stir, to fully mix, make finishing solution;

[0028] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

Embodiment 3

[0030] Coarse and thin fiber blended yarn, which is subjected to padding treatment, and the padding treatment comprises the following steps:

[0031] 1) Put 2 parts by weight of glycerol monostearate, 1.4 parts by weight of hydroxypropyl cellulose, 0.4 parts by weight of zinc sulfate, and 1.2 parts by weight of chloral into 12.7 parts by weight of deionized water, and stir evenly;

[0032] 2) Slowly add 0.7 parts by weight of vinyltriethoxysilane, 0.4 parts by weight of potassium persulfate, 0.8 parts by weight of di-n-octyl-4-isothiazolin-3-one, 0.9 parts by weight of octadecyl di Methyl hydroxyethyl quaternary ammonium nitrate, continue to stir, to fully mix, make finishing solution;

[0033] 3) Pad the blended yarn in the finishing solution, take it out and dry it at a constant temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses crude-fine fiber blended yarn. The crude-fine fiber blended yarn is subjected to dipping treatment, and the dipping treatment comprises steps as follows: 1), 1-2 parts by weight of glycerol monostearate, 1.4 parts by weight of hydroxy propyl cellulose, 0.4 parts by weight of zinc sulfate and 1.2 parts by weight of trichloracetic aldehyde are added to 12.7 parts by weight of deionized water, and the materials are stirred uniformly; 2), 0.7 parts by weight of vinyltriethoxysilane, 0.4 parts by weight of potassium peroxodisulfate, 0.8 parts by weight of 2-n-octyl-4-isothiazolin-3-one and 0.9 parts by weight of dimethyl octadecyl hydroxyethyl ammonium nitrate are added simultaneously and slowly, the materials are stirred continuously until the materials are mixed sufficiently and uniformly, and a finishing liquid is prepared; 3), blended yarn is subjected to dipping treatment in the finishing liquid, and then is taken out for drying at the constant temperature. The crude-fine fiber blended yarn has excellent mould-proof, mothproof, anti-bacterial, anti-flaming and anti-static performance.

Description

technical field [0001] The present invention relates to thick and thin fiber blended yarns. Background technique [0002] The performance of the existing thick and thin fiber blended yarn is single, which cannot meet the requirements of customers. Contents of the invention [0003] The object of the present invention is to provide a thick and thin fiber blended yarn, which has excellent mildew-proof, moth-proof, antibacterial, flame-retardant and antistatic properties. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of thick and thin fiber blended yarn, which is processed through padding, and the padding process includes the following steps: [0005] 1) Add 1 to 2 parts by weight of glycerol monostearate, 1.4 parts by weight of hydroxypropyl cellulose, 0.4 parts by weight of zinc sulfate, and 1.2 parts by weight of chloral in 12.7 parts by weight of deionized water, and stir evenly; [0006] 2) Slowly add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M13/133D06M13/224D06M13/513D06M13/352D06M13/463D06M15/09D06M11/56D06M11/50
CPCD06M13/133D06M11/50D06M11/56D06M13/2243D06M13/352D06M13/463D06M13/513D06M15/09D06M16/00D06M2200/30
Inventor 缪栋华
Owner 常熟市明达腈纺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap