LOCA (Liquid Optical Clear Adhesive) and preparation method thereof

An optically transparent and adhesive technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of insufficient elasticity and hardness, poor yellowing resistance, and high optical radiation energy, to prevent Free radical polymerization, effect of good photocuring properties

Active Publication Date: 2016-04-27
矽时代材料科技股份有限公司
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing UV-moisture dual-curable liquid optically transparent adhesive LOCA has defects such as low ph

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • LOCA (Liquid Optical Clear Adhesive) and preparation method thereof
  • LOCA (Liquid Optical Clear Adhesive) and preparation method thereof
  • LOCA (Liquid Optical Clear Adhesive) and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0075] Example 1

[0076] S1. Add 0.4 parts of 2,6-di-tert-butyl-4-methylphenol (BHT) to 40 parts of AS-1 with a viscosity of 20000 cps and 60 parts of AS-2 with a viscosity of 3000 cps, and heat at 600Pa, 120°C and Dehydrate under vacuum for 2h;

[0077] S2. After cooling to room temperature, add 4 parts of methyltrimethoxysilane to the above-mentioned base polymer, and continue stirring for 30 minutes under vacuum;

[0078] S3. Add 0.4 parts of 2-hydroxy-2-methyl-1-phenyl-1-propanone and 0.15 parts of dibutyltin dilaurate to the above base polymer together, and continue to stir for 0.5h under vacuum Make it mix well;

[0079] S4. The product is a liquid optically transparent adhesive after being sealed and stored under vacuum.

Example Embodiment

[0080] Example 2

[0081] S1. Add 0.5 parts of p-methoxyphenol to 100 parts of AS-2 with a viscosity of 3000cps and 60 parts of methyldimethoxy-terminated polydimethylsiloxane with a viscosity of 30000cps, and heat at 600pa, 120℃ and Dehydrate under vacuum for 2h;

[0082] S2. After cooling to room temperature, add 8 parts of methyltrimethoxysilane to the above-mentioned base polymer, and continue to stir for 50 minutes under vacuum;

[0083] S3. Add 0.5 parts of 2-hydroxy-2-methyl-1-phenyl-1-acetone and 0.2 parts of diisopropoxy bis(ethyl acetoacetate) titanium to the above base polymer, and add Continue to stir for 0.5h under vacuum to fully mix;

[0084] S4. The product is a liquid optically transparent adhesive after being sealed and stored under vacuum.

Example Embodiment

[0085] Example 3

[0086] S1. Add 0.5 parts of 2,6-di-tert-butyl-4-methylphenol (BHT) to 100 parts of AS-2 synthesized in Example 1, 40 parts of hydroxy-terminated polydimethylsiloxane with a viscosity of 30000cps And 10 parts of methyl MQ resin ({(CH 3 ) 3 SiO 1 / 2 } 0.44 (SiO 4 / 2 ) 0.56 ), and dehydrated for 2h under 600Pa, 120℃ and vacuum conditions;

[0087] S2. After cooling to room temperature, add 9 parts of methyltrimethoxysilane to the base gum, and continue to stir for 60 minutes under vacuum;

[0088] S3. Add 0.5 parts of 1-hydroxycyclohexyl benzophenone and 0.2 parts of stannous octoate to the above-mentioned base polymer together, and continue to stir for 0.5 hours to fully mix under vacuum;

[0089] S4. The product is a liquid optically transparent adhesive after being sealed and stored under vacuum.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an LOCA (Liquid Optical Clear Adhesive), and a preparation method and application of the LOCA. The LOCA is prepared from (A) 100 parts of (methyl) acryloyloxy alkylate polysiloxane, (B) 0 to 200 parts of hydroxyl or alkoxyl end-capping poly dialkyl siloxane, (C) 0 to 100 parts of organic silicon resin, (D) cross-linking agent which occupies 0 to 10 percent of the total amount of (A), (B) and (C) and connected with silicon and can be used for hydrolyzing groups, (E) 0.01 to 5 parts of photoinitiator, (F) 0.01 to 5 parts of polymerization inhibitor and (G) 0.0001 to 2 parts of condensation catalyst. The LOCA disclosed by the invention not only can be cured through an ultraviolet irradiation mode, but also can be cured through a moisturizing mode, and the LOCA can be widely applied to the adhesion of display screens, touch screens and optical devices.

Description

technical field [0001] The invention relates to the field of organosilicon polymer materials, more specifically, to a liquid optically transparent adhesive LOCA capable of dual curing by ultraviolet light and moisture and a preparation method thereof. Background technique [0002] With the advent of the smart era, tablet computers and touch-screen mobile phones have become increasingly popular, and the excellent visual effects of display panels will be favored by more people. Using liquid optically clear adhesive (LOCA) to fill the air layer between the touch screen and the display panel can reduce glare and light loss, increase the contrast, especially under strong light, and significantly improve the visual effect of the display panel . [0003] LOCA, a liquid optically transparent adhesive based on acryloyloxyalkyl modified polyorganosiloxane modified materials, has the characteristics of non-toxic, odorless, high light transmittance and good adhesion. The dual characte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J183/06C09J11/08C09J11/06
CPCC08L2201/08C08L2201/10C08L2205/025C08L2205/03C09J11/06C09J11/08C09J183/06C08L83/06C08L83/04C08K5/5419
Inventor 康润华许静文
Owner 矽时代材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap