Manufacturing method for breathable and wearable composite insole material

A manufacturing method and technology for insoles, applied in wet spinning, non-woven fabrics, textiles and papermaking, etc., can solve the problems of insufficient environmental protection and poor air permeability, and achieve good air permeability and wear resistance, good degradation performance, Effect of improving degradability

Active Publication Date: 2016-05-04
湖州奇奇机电科技有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The insole material is a polyurethane high polymer material, its wear resistance is acceptable, but its air permeability is poor, and it is not environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for breathable and wearable composite insole material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Manufacture the breathable and wear-resistant composite insole material according to the following steps:

[0028] (1) Peanut seedlings are cut into peanut seedlings with a length of 2.5cm, and then peeled in a peeling machine to obtain peeled peanut seedlings, and the peeled peanut seedlings are added with a mass concentration of 10% sodium hydroxide In the solution, the mass ratio of peeled peanut seedlings to sodium hydroxide solution is 1:10, heated to 60°C in a water bath, stirred for 3 hours, taken out, filtered, washed repeatedly with distilled water, drained, and placed in a vacuum oven at 70°C drying for 3 hours, to obtain alkalized peanut seedling fiber;

[0029] (2) Add the alkalized peanut seedling fiber obtained in step (1) into the pectinase treatment solution, the mass ratio of the alkalized peanut seedling fiber to the pectinase treatment solution is 1:20, and the pectinase treatment solution includes a mass concentration of 3% pectinase and EDTA with a...

Embodiment 2

[0033] Manufacture the breathable and wear-resistant composite insole material according to the following steps:

[0034] (1) Peanut seedlings are cut into peanut seedlings with a length of 2.5cm, and then peeled in a peeling machine to obtain peeled peanut seedlings, and the peeled peanut seedlings are added with a mass concentration of 10% sodium hydroxide In the solution, the mass ratio of peeled peanut seedlings to sodium hydroxide solution is 1:10, heated to 60°C in a water bath, stirred for 3 hours, taken out, filtered, washed repeatedly with distilled water, drained, and placed in a vacuum oven at 70°C drying for 3 hours, to obtain alkalized peanut seedling fiber;

[0035] (2) Add the alkalized peanut seedling fiber obtained in step (1) into the pectinase treatment solution, the mass ratio of the alkalized peanut seedling fiber to the pectinase treatment solution is 1:20, and the pectinase treatment solution includes a mass concentration of 3% pectinase and EDTA with a...

Embodiment 3

[0039] Manufacture the breathable and wear-resistant composite insole material according to the following steps:

[0040] (1) Peanut seedlings are cut into peanut seedlings with a length of 2.5cm, and then peeled in a peeling machine to obtain peeled peanut seedlings, and the peeled peanut seedlings are added with a mass concentration of 10% sodium hydroxide In the solution, the mass ratio of peeled peanut seedlings to sodium hydroxide solution is 1:10, heated to 60°C in a water bath, stirred for 3 hours, taken out, filtered, washed repeatedly with distilled water, drained, and placed in a vacuum oven at 70°C drying for 3 hours, to obtain alkalized peanut seedling fiber;

[0041] (2) Add the alkalized peanut seedling fiber obtained in step (1) into the pectinase treatment solution, the mass ratio of the alkalized peanut seedling fiber to the pectinase treatment solution is 1:20, and the pectinase treatment solution includes a mass concentration of 3% pectinase and EDTA with a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing method for a breathable and wearable composite insole material. The manufacturing method roughly includes the steps that (1), peanut vines are shorn into peanut vine strips, and alkalified peanut vine fibers are prepared through peeling and soda boiling; (2), the alkalified peanut vine fibers are treated with pectinase treatment fluid to prepare peanut vine fibers; (3), the peanut vine fibers and a spandex spinning solution are mixed, spun and formed through a coagulating bath to obtain composite fibers; (4), opening, carding, lapping, setting, needling and pressing are sequentially conducted on the composite fibers to prepare formed cloth, and the formed cloth is smeared with adhesive and dried to obtain the breathable wearable composite insole material. The manufactured insole material is high in breathability and wear resistance.

Description

Technical field: [0001] The invention relates to an insole material, in particular to a method for manufacturing a breathable and wear-resistant composite insole material. Background technique: [0002] Insoles are widely used in the shoemaking industry, health care and special functions, and are generally divided into two models: shoemaking industry-applied insoles and market commodity types. The insoles used in the shoe industry are mainly used to match the outsole and midsole of the shoe to make a corresponding shape; make a size board according to the last board or panel, and make the corresponding shape. Market commodity insoles are mainly products that sell insoles directly as a commodity, designed by developers, and circulated in the market. [0003] Insoles can be subdivided according to their functions: 1. Health insoles, that is, insoles that are beneficial to human health. Such as: antibacterial insoles, deodorant insoles, traditional Chinese medicine insoles, e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline