Improved peelable soak-off gel and preparation method thereof

A nail polish and methyl phenyl technology, applied in medical preparations containing active ingredients, manicure, pedicure, etc., can solve the problems of inconvenient production and use of nail polish, and achieve good peelability and color Brightness changeable, reducing the effect of interaction

Inactive Publication Date: 2016-05-11
SHANGHAI INSTITUTE OF TECHNOLOGY
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned technical problems in the prior art, the invention provides a kind of improved peelable nail polish and preparation method thereof, described this improved peelable nail polish and preparation method thereof will solve existing The peelable nail polish in the technology generally adds a peelable component to the formula of the nail polish, which brings inconvenience to the production and use of the nail polish.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Improved peelable soak-off gel and preparation method thereof
  • Improved peelable soak-off gel and preparation method thereof
  • Improved peelable soak-off gel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] An improved peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0056]

[0057] Wherein said UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0058]

[0059] Described UV curing resin A is prepared as follows:

[0060] Add the above-mentioned 20 parts of methylphenyl hydrogen-containing silicone oil and 10 parts of dipentaerythritol hexaacrylate into a 500ml three-necked flask, then add 0.005 parts of polymerization inhibitor, pass in protective gas, stir and heat, and raise the temperature to 60°C. Add 0.03 part of catalyst, keep stirring for 3 hours, stop heating, wait until the temperature of the flask drops to room temperature, and obtain UV curable resin A.

[0061] The leveling agent is TegoGlide410;

[0062] Described wetting agent is NP-100 of U.S. Dow Company;

[0063] The defoamer is a mixture of German BYK-035 and BYK-037 in a mass ratio ...

Embodiment 2

[0073] An improved peelable nail polish, calculated in parts by weight, its raw material composition and content are as follows:

[0074]

[0075]

[0076] Wherein said UV curable resin A is calculated in parts by weight, and its composition and content are as follows:

[0077]

[0078] Described UV curing resin A is prepared as follows:

[0079] Add 60 parts of methylphenyl hydrogen-containing silicone oil and 20 parts of dipentaerythritol hexaacrylate into a 500ml three-necked flask, then add 0.01 part of polymerization inhibitor, pass in protective gas, stir and heat, raise the temperature to 80°C, add 0.05 part of catalyst, keep the temperature under stirring for 5 hours, stop heating, and wait for the temperature of the flask to drop to room temperature to obtain UV curable resin A.

[0080] The leveling agent is a mixture of German BYK-345 and BYK-346 in a mass ratio of 1:1;

[0081] The wetting agent is German BYK333;

[0082] The defoamer is a mixture of Ge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses improved peelable soak-off gel. The improved peelable soak-off gel is prepared from, by weight, 50-80 parts of UV curing resin A, 50-80 parts of UV curing resin B, 50-80 parts of reactive diluent, 0.05-0.1 part of flatting agent, 1-10 parts of wetting agent, 0.2-1 part of defoaming agent, 1-10 parts of color paste and 3-5 parts of photoinitiator. The invention further provides a preparation method of the improved peelable soak-off gel. Wetting agent, flatting agent, defoaming agent and color paste are added into a high-speed disperser, UV curing resin A, UV curing resin B, reactive diluent, thickening agent and photoinitiator are added after dispersion, dispersion continues to be conducted, and materials are evenly mixed to obtain the improved peelable soak-off gel. The improved peelable soak-off gel has rapid curing capacity after being used for coating and irradiated by a 395-nm UV-LED lamp and can be widely used for the technical field of nail beautifying of various people and the like.

Description

technical field [0001] The invention belongs to the field of polymer materials and relates to a nail polish, in particular to an improved peelable nail polish and a preparation method thereof. Background technique [0002] Women's love for nail art stems from a kind of love. Nail polish is applied to the nails with tools, and cross-linking polymerization occurs after being irradiated by ordinary UV light sources. The resulting cured nail polish is bright in color, crystal clear and full, and endlessly changing. It is the favorite of ladies. Compared with ordinary UV light source curing methods, UV-LED light source has many advantages such as high luminous efficiency, long life, fast response speed, less heat release, energy saving, environmental protection, etc., and has gradually replaced ordinary UV light source. With the enrichment of urban life and the acceleration of the pace of life, ladies already like to change their nails in a fast pace. The peelable nail polish g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61K8/89A61Q3/02C08G77/38
CPCA61K8/89A61K2800/43A61K2800/95A61Q3/02C08G77/38
Inventor 张英强常文秀李烨
Owner SHANGHAI INSTITUTE OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap