Preparation method of polyamide textile material with good electromagnetic wave absorption ability in ultra-wide frequency spectrum range

A textile material and polyamide-based technology, applied in the field of preparation of polyamide-based textile materials, can solve the problems of fabric textile performance degradation, affecting textile performance, unfavorable large-scale application of products, etc., to ensure normal operation, avoid leaks, and good Effect of electromagnetic wave protection function

Active Publication Date: 2016-05-11
ZHEJIANG BONI CHINLON TECH CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But obviously, it is extremely difficult to load a large amount of media into the fabric in both methods
[0005] 2. Excessive media loading on the fabric will inevitably lead to a decline in the textile performance of the fabric
And too much load medium will inevitably affect its textile performance, which is not conducive to the large-scale application of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyamide textile material with good electromagnetic wave absorption ability in ultra-wide frequency spectrum range
  • Preparation method of polyamide textile material with good electromagnetic wave absorption ability in ultra-wide frequency spectrum range
  • Preparation method of polyamide textile material with good electromagnetic wave absorption ability in ultra-wide frequency spectrum range

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: the preparation method of the polyamide-based textile material that has good electromagnetic wave absorption ability in ultra-wide spectrum range, comprises the following steps:

[0033] 1) Selection of absorbing medium: Ni-Zn ferrite is selected as the absorbing medium, and its composition is (Ni 0.888 Zn 0.1 co 0.012 )Fe2 o 4 , NiZn ferrite presents a combination of one-dimensional nanorods and three-dimensional nanoparticles, wherein the diameter of the nanorods presents a gradient change, the diameter of the thin end part is 30nm, and the diameter of the thick end part is 110nm; the diameter of the three-dimensional nanoparticle is About 20nm, and the mass ratio of nickel zinc ferrite of one-dimensional nanorods and three-dimensional nanoparticles is 1:2;

[0034] 2) Slurry preparation: Add nano-nickel zinc ferrite material into deionized water, and then add 8wt% ionic liquid [BMIN]BCl 4 As a dispersant, turn on the mechanical stirring, and stir at...

Embodiment 2

[0038] Embodiment 2: A kind of preparation method of the polyamide-based textile material with good electromagnetic wave absorption ability in ultra-wide spectrum range, comprises the following steps:

[0039] 1) Selection of absorbing medium: Ni-Zn ferrite is selected as the absorbing medium, and its composition is (Ni 0.84 Zn 0.15 co 0.01 )Fe 2 o 4 . Nickel zinc ferrite presents a combination of one-dimensional nanorods and three-dimensional nanoparticles, in which the diameter of the nanorods presents a gradient change, the diameter of the thin end part is 30nm, and the diameter of the thick end part is 110nm; the diameter of the three-dimensional nanoparticle is about 50nm . The mass ratio of nickel zinc ferrite of one-dimensional nanorods and three-dimensional nanoparticles is 1:3;

[0040] 2) Slurry preparation: Add the nano-ferrite material into deionized water, and then add the ionic liquid [BMIN]BCl with a content of 6wt% 4 As a dispersant, turn on the mechanic...

Embodiment 3

[0044] Embodiment 3: A kind of preparation method of the polyamide-based textile material with good electromagnetic wave absorption ability in ultra-wide spectrum range, comprises the steps:

[0045] 1) Selection of absorbing medium: Ni-Zn ferrite is selected as the absorbing medium, and its composition is (Ni 0.838 Zn 0.15 co 0.012 )Fe 2 o 4 . Nickel zinc ferrite presents a combination of one-dimensional nanorods and three-dimensional nanoparticles, in which the diameter of the nanorods presents a gradient change, the diameter of the thin end part is 30nm, and the diameter of the thick end part is 110nm; the diameter of the three-dimensional nanoparticle is about 40nm . The mass ratio of nickel zinc ferrite of one-dimensional nanorods and three-dimensional nanoparticles is 1:2.5;

[0046] 2) Slurry preparation: Add the nano-ferrite material into deionized water, and then add the ionic liquid [BMIN]BCl with a content of 5wt% 4 As a dispersant, turn on the mechanical sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a polyamide textile material with good electromagnetic wave absorption ability in an ultra-wide frequency spectrum range. The preparation method comprises the following steps: selecting a nickel zinc ferrite nano-rod and nano-particle mixture as a wave absorption medium, wherein the diameter of the nano-rod is distributed in a gradient manner; adding the nickel zinc ferrite mixture to deionized water, and uniformly stirring with an ionic liquid as a dispersant to prepare a ferrite wave absorption medium source dispersion; carrying out surface pretreatment on polyamide long lines by adopting an anhydrous ethanol and acetone mixed liquid; putting the treated polyamide fiber long lines in the ferrite wave absorption medium source dispersion, and fully stirring and mixing above solution; and cleaning the polyamide fiber long lines adsorbed with the nanometer nickel zinc ferrite, and drying the cleaned polyamide fiber long lines adsorbed with the nanometer nickel zinc ferrite to obtain the polyamide texture material. The electromagnetic wave absorption rate of the texture material in an ultra-wide frequency spectrum range of 100MHz-10GHz is not lower than 30dB, so the polyamide textile material is especially suitable for some weak physique people, such as pregnant women, to use.

Description

technical field [0001] The invention belongs to the technical field of preparation of nanometer materials and functional textiles, and in particular relates to a preparation method of a polyamide-based textile material with good electromagnetic wave absorption capacity in an ultra-wide spectrum range. Background technique [0002] Electromagnetic wave pollution will seriously endanger human health, especially for some weak people, such as pregnant women. In addition, electromagnetic waves will cause serious harm to the normal operation of communication equipment and electrical and electronic equipment. In the military and communication fields, the leakage of electromagnetic waves can also cause leaks. Therefore, the development of various electromagnetic wave protection materials has always been a research hotspot, and it is also a market hotspot. Especially textile fabrics with anti-electromagnetic radiation function are in great demand in the market. Because in daily li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/49D06M13/144D06M13/127D06L1/16D06M101/34
CPCD06L1/16D06M11/49D06M13/127D06M13/144D06M2101/34
Inventor 金国军
Owner ZHEJIANG BONI CHINLON TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com