Production method of high-adhesion matt aluminum-coated film

A production method and bonding technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems that the aluminized film is difficult to meet the requirements, and achieve smooth surface, good fracture resistance, and thick thickness Effect

Active Publication Date: 2017-10-24
嘉兴鹏翔包装材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As people have higher and higher requirements for the aesthetic effect and quality of the outer packaging of products, further requirements have been put forward for the matt effect of the aluminized film, but the existing aluminized film is difficult to meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The present invention will be further described in conjunction with specific embodiments.

[0016] The present invention provides a kind of production method of highly laminating matte aluminized film, comprising the following steps:

[0017] Step 1: Prepare high light-transmitting composite particles: the mass percentages of the various raw materials are 20-60% of silica particles, 39.5-79.5% of polyethylene terephthalate and 0.5% of simethicone emulsifier. Mixing, the sum of the mass percentages of each raw material is 100%; then after being centrifuged in a high-speed centrifuge, it is polymerized; then the polymerized material is extruded and granulated through a twin-screw extruder, and then Cool and dry to obtain high light-transmitting composite particles; preferably, the mass percentage of the above-mentioned raw materials is preferably 40-50% of silicon dioxide particles, 49.5-59.5% of polyethylene terephthalate, and dimethyl silicone oil emulsifier 0.5%.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
hazeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of a highly-laminated matte aluminized film. The method comprises the following steps: step 1, preparing high-transmittance composite particles: fully mixing (by mass percentage) 20-60% of silicon dioxide particles, 39.5-79.5% of polyethylene terephthalate and 0.5% of simethicone emulsifier; and performing centrifugalization in a high speed centrifuge so that polymerization reaction can be carried out; performing extrusion and granulation to the material after polymerization reaction through a double-screw extruder and then cooling and drying; step 2, fully mixing 18-35 parts by weight of high-transmittance composite particles with 54-80 parts by weight of PET (Polyethylene Terephthalate), and carrying out melt extrusion by the double-screw extruder and cooling to obtain a PET base film; step 3, performing corona on the surface of the PET base film obtained in the step 2; step 4, laying a glass fiber grid layer on the surface of the PET base film after corona; and step 5, performing vacuum aluminizing by a vacuum aluminizing machine to form an aluminized layer, so as to obtain the highly-laminated matte aluminized film.

Description

technical field [0001] The invention relates to the technical field of film production, in particular to a production method of a high-adherence matt aluminum-coated film. Background technique [0002] Traditional flexible plastic packaging generally uses aluminum foil with a thickness of 6-20 μm. The aluminum foil has a silvery white luster. Printing transparent ink directly on the aluminum foil can have a unique metallic luster. Aluminum foil has good shading properties, gas barrier properties, moisture barrier properties, good thermal conductivity, and electromagnetic shielding properties. Among them, the most prominent is the barrier performance of aluminum foil. Under the premise of sufficient thickness of aluminum foil, it can completely block gas and moisture. Therefore, aluminum foil is an indispensable material in flexible plastic packaging base film and is widely used in pharmaceutical packaging, food Packaging, especially the flexible packaging of high-end produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B17/02B32B17/10B32B27/36B32B27/18B32B27/12B32B33/00B32B38/00B32B38/08B32B43/00
CPCB32B17/02B32B17/10B32B27/12B32B27/18B32B27/36B32B33/00B32B38/0008B32B38/08B32B43/003B32B2262/101B32B2307/414B32B2307/582
Inventor 曹赤鹏
Owner 嘉兴鹏翔包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap